Effect of a single application of TiF(4) and NaF varnishes and solutions on dentin erosion in vitro

Objectives: This in vitro study aimed to analyse the effect of a single application of TiF(4) and NaF varnishes and solutions to protect against dentin erosion. Methods: Bovine root dentin samples were pre-treated with NaF-Duraphat varnish (2.26%F, pH 4.5), NaF/CaF(2)-Duofluorid varnish (5.63%F, pH 8.0), NaF-experimental varnish (2.45%F, pH 4.5), TiF(4)-experimental varnish (2.45%F, pH 1.2), NaF solution (2.26%F, pH 4.5), TiF(4) solution (2.45%F, pH 1.2) and placebo varnish (pH 5.0, no-F varnish control). Controls remained untreated. Ten samples in each group were then subjected to an erosive demineralisation (Sprite Zero, 4x 90 s/day) and remineralisation (artificial saliva, between the erosive cycles) cycling for S days. Dentin loss was measured profilometrically after pretreatment and after 1, 3 and 5 days of de-remineralisation cycling. The data were statistically analysed by two-way ANOVA and Bonferroni`s post hoc test (p < 0.05). Results: After pre-treatment, TiF(4) solution significantly induced surface loss (1.08 +/- 0.53 mu m). Only Duraphat reduced the dentin loss overtime, but it did not significantly differ from placebo varnish (at 3rd and 5th days) and TiF(4) varnish (at 3rd day). Conclusions: Duraphat varnish seems to be the best option to partially reduce dentin erosion. However, the maintenance of the effects of this treatment after successive erosive challenges is limited. (C) 2009 Elsevier Ltd. All rights reserved.

Evaluation of several protocols for the application of ultrasound during the removal of cast intraradicular posts cemented with zinc phosphate cement

To evaluate several protocols for the application of ultrasound during removal of cast posts with varying core configurations cemented with zinc phosphate. Sixty maxillary canines were distributed into three groups (n = 20): group 1 - core with 5 mm diameter/height and post diameter of 1.3 mm; groups 2 and 3 - core with the same diameter as the post (1.3 mm) and heights of 5 mm and 3 mm, respectively. Posts/cores were cemented using a standard technique with zinc phosphate cement. Each group was divided into two subgroups according to the ultrasonic vibration mode: point vibration - ultrasonic vibration applied to the core surface for 5 s, on each face totalling 25 s; alternate vibration - intermittent application of ultrasonic vibration for 10 s to the labial and lingual surfaces, 10 s to the mesial and distal surfaces and 5 s to the incisal surface, totalling 25 s. The specimens were submitted to the tensile test using an Instron machine (1 mm min(-1)) and results were analysed by anova and t-test. The failure type was also analysed. Statistical analysis showed significant differences between groups relating to the core preparations (P < 0.05). The lowest mean values of traction force were obtained for group 3 (46.1 +/- 7.7 N), followed by group 2 (89.0 +/- 2.7 N) and group 1 (160.4 +/- 7.5 N). Regarding ultrasonic vibration, the lowest mean was observed with alternate vibration (81.1 +/- 10.1 N), which was significantly lower than the point vibration (115.9 +/- 9.5 N) (P < 0.05). Cohesive failure occurred in all cases. A reduction in core diameter/height and intermittent ultrasonic application improved the removal of cast posts cemented with zinc phosphate.