Flexural properties, microleakage, and degree of conversion of a resin polymerized with conventional light and argon laser

Objective: To evaluate the flexural strength, microleakage, and degree of conversion of a microhybrid resin polymerized with argon laser and halogen lamp. Method and Materials: For both flexural test and degree of conversion analysis, 5 bar samples of composite resin were prepared and polymerized according to ISO 4049. The halogen light-curing unit was used with 500 MW/cm(2) for 20 seconds and the argon laser with 250 mW for 10 and 20 seconds. Samples were stored in distilled water in a dark environment at 37 degrees C for 24 hours. The flexural property was quantified by a 3-point loading test. For the microleakage evaluation, 60 bovine incisors were used to prepare standardized Class 5 cavities, which were restored and polished. Specimens were stored in distilled water for 24 hours at 37 degrees C and thermocycled 500 times (6 degrees C to 60 degrees C). Specimens were then immersed in art aqueous solution of basic fuchsin for 24 hours. Longitudinal sections of each restoration were obtained and examined with a stereomicroscope for qualitative evaluation of microleakage. Fourier transform (FT)-Raman RFS 100/S spectrometer (Bruker) was used to analyze the degree of conversion. Results: ANOVA showed no statistically significant differences of flexural strength between the photoactivation types evaluated in the flexural study. Microleakage data were statistically analyzed by Mann-Whitney and Kruskal-Wallis tests. Enamel margins resulted in a statistically lower degree of leakage than dentin margins. No statistically significant difference was found among the 3 types of photocuring studied. ANOVA also showed no statistically significant difference in the degree of conversion among the studied groups. Conclusion: According to the methodology used in this research, the argon laser is a possible alternative for photocuring, providing the same quality of polymerization as the halogen lamp. None of the photocured units tested in this study completely eliminated microleakage.

Preparation and characterization of the novels terpolymers of poly-{trans-[RuCl(2)(vpy)(4)]-styrene-divinylbenzene} and styrene-divinylbenzene-vinylpiridine impregnated with silver nanoparticles

This paper reports the preparation and characterization of poly-{trans-[RuCl(2)(vpy)(4)]-styrene-divinylbenzene} and styrene-divinylbenzene-vinylpiridine filled with nanosilver. Theses materials were synthesized by non aqueous polymerization through a chemical reaction using benzoyl peroxide as the initiator. The nanosilver was obtained from chemical reduction using NaBH(4) as reducing agent and sodium citrate as stabilizer. The nanometric dimension of nanosilver was monitored by UV-visible and confirmed through TEM. The morphology was characterized by SEM and the thermal properties were done by TGA and DSC. The antimicrobial action of the polymers impregnated with nanosilver was evaluated using both microorganisms, Staphylococcus aureus and Escherichia coli. The antimicrobial activity of the poly-{trans-[RuCl(2)(vpy)(4)]-styrene-divinylbenzene} filled with nanosilver was confirmed by the presence of an inhibition halo of the bacterial growth in seeded culture media, but was not confirmed to the styrene-divinylbenzene-vinylpiridine. The present work suggest that trans - [RuCl(2)(vpy)(4)] complex facilitate the release of silver ion from the media.

Polyaniline/layered zirconium phosphate nanocomposites: Secondary-like doped polyaniline obtained by the layer-by-layer technique

In the present work, nanocomposites of polyaniline (PANI) and layered alpha-Zr(HPO4)(2).H2O (alpha-ZrP) were prepared using two different approaches: (i) the in situ aniline polymerization in the presence of the layered inorganic material and (ii) the layer-by-layer (LBL) assembly using an aqueous solution of the polycation emeraldine salt (ES-PANI) and a dispersion of exfoliated negative slabs of alpha-ZrP. These materials were characterized spectroscopically using mainly resonance Raman scattering at four exciting radiations and electronic absorption in the UV-VIS-NIR region. Structural and textural characterizations were carried out using powder X-ray diffraction (XRD) and scanning electron microscopy (SEM). The polymer obtained by the in situ aniline polymerization is located primarily in the external surface of the inorganic material although aniline monomers were intercalated between alpha-ZrP interlayer regions before oxidative polymerization. Through resonance Raman spectroscopy, it was observed that the formed polymer has semiquinone units (ES-PANI) and also azo bonds (-N = N-), showing that this method results in a polymer with a different structure from the usual ""head-to-tail"" ES-PANI. The LBL assembly of pre-formed ES-PANI and exfoliated alpha-ZrP particles produces homogeneous films with reproducible deposition from layer to layer, up to 20 bilayers. Resonance Raman (lambda(0) = 632.8 nm) spectrum of PANI/ZrP LBL film shows an enhancement in the intensity of the polaronic band at 1333 cm(-1) (nu C-N center dot+) and the decrease of the band intensity at 1485 cm(-1) compared to bulk ES-PANI. Its UV-VIS-NIR spectrum presents an absorption tail in the NIR region assigned to delocalized free charge carrier. These spectroscopic features are characteristic of highly conductive secondary doped PANI suggesting that polymeric chains in PANI/ZrP LBL film have a more extended conformation than in bulk ES-PANI.

Oxidation of anilinium ions intercalated in montmorillonite clay by electrochemical route

Resonance Raman, FTIR, X-ray diffraction, UV-vis-NIR, electron paramagnetic resonance, X-ray absorption at Si K-edge and electron microscopy were employed for characterizing the products formed through electrochemical oxidation of intercalated anilinium ions inside the cationic montmorillonite (MMT) clay. The layer silicate structure was not affected by the anilinium oxidation between the layers. The intercalated products present only an electronic absorption band at 400 nm, very low conductivity (ca. 10(-7) S cm(-1)) and their Raman spectrum displays bands, with high relative intensities, assigned to the benzidine dication, indicating that this product was formed in high amount. Nevertheless, bands that can be correlated to phenazine-like segments and 1,4-phenylenediamine repeat units (PANI like segments) are also observed. The very low EPR signal indicates that diamagnetic species are predominant. All results are compared to those obtained by anilinium-MMT chemically oxidized by persulfate and the differences are pointed out. (C) 2008 Elsevier B.V. All rights reserved.

Spectroscopic investigation of conjugated polymers derived from nitroanilines

For the first time, the resonance Raman spectroscopy was used to characterize polymers derived from meta- and para-nitroanilines. In order to improve the polymer structure analysis, other techniques were also used such as FTIR, UV-vis, XRD, XPS, EPR and N K-XANES. The insertion of strong electron-withdrawing groups (NO2) in polyaniline (PANI)-like backbone causes drastic changes in the lower energy charge transfer states, related to the polymer effective conjugation length. The resonance Raman data show that the NO2 moiety has a minor contribution on the CT state in poly(meta-nitroaniline), PMN, while in the poly(para-nitroaniline), PPN, the quinoid structure induced by para-substitution increases the charge density of NO2 groups, causing a more localized chromophore. The characterization of the imine nitrogen and of the protonated segments was done by XPS, N K-XANES and EPR spectroscopies and the lower polymerization degree of PPN, in comparison to PMN, is confirmed by XRD and TG data. (C) 2007 Elsevier B.V. All rights reserved.

Microwave-Assisted Derivatization of Cellulose in an Ionic Liquid: An Efficient, Expedient Synthesis of Simple and Mixed Carboxylic Esters

Microwave (MW)-assisted cellulose dissolution in ionic liquids (ILs) has routinely led either to incomplete biopolymer solubilization, or its degradation. We show that these problems can be avoided by use of low-energy MW heating, coupled with efficient stirring. Dissolution of microcrystalline cellulose in the IL 1-allyl-3-methylimidazolium chloride has been achieved without changing its degree of polymerization; regenerated cellulose showed pronounced changes in its index of crystallinity, surface area, and morphology. MW-assisted functionalization of MCC by ethanoic, propanoic, butanoic, pentanoic, and hexanoic anhydrides has been studied. Compared with conventional heating, MW irradiation has resulted in considerable decrease in dissolution and reaction times. The value of the degree of substitution (DS) was found to be DS(ethanoate) > DS(propanoate) > DS(butanoate). The values of DS(pentanoate) and DS(hexanoate) were found to be slightly higher than DS(ethanoate). This surprising dependence on the chain length of the acylating agent has been reported before, but not rationalized. On the basis of the rate constants and activation parameters of the hydrolysis of ethanoic, butanoic, and hexanoic anhydrides in aqueous acetonitrile (a model acyl transfer reaction), we suggest that this result may be attributed to the balance between two opposing effects, namely, steric crowding and (cooperative) hydrophobic interactions between the anhydride and the cellulosic surface, whose lipophilicity has increased, due to its partial acylation. Four ethanoate-based mixed esters were synthesized by the reaction with a mixture of the two anhydrides; the ethanoate moiety predominated in all products. The DS is reproducible and the IL is easily recycled. (C) 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 134-143, 2010

Application of 1-Allyl-3-(1-butyl)imidazolium Chloride in the Synthesis of Cellulose Esters: Properties of the Ionic Liquid, and Comparison with Other Solvents

The ionic liquid (IL), 1-allyl-3-(1-butyl)imidazolium chloride (AlBuImCl), has been synthesized and its properties determined. Increase in the temperature increased its conductivity and decreased its density, polarity, and viscosity. Microcrystalline cellulose (MCC), dissolves in thisIL by heating at 80 degrees C; this did not affect its degree of polymerization, decreased its index of crystallinity (Ic), and changed in morphology after regeneration. Convenient acylation of MCC was achieved by using 50% excess anhydride at 80 degrees C, for 24 or 48 h for acetic and butyric anhydride, respectively. The composition of the mixed esters depended on the initial ratio of the anhydrides, and their order of addition.

Acetylation of cellulose in LiCl-N,N-dimethylacetamide: first report on the correlation between the reaction efficiency and the aggregation number of dissolved cellulose

The acylation of three cellulose samples by acetic anhydride, Ac(2)O, in the solvent system LiCl/N,N-dimethylacetamide, DMAc (4 h, 110 A degrees C), has been revisited in order to investigate the dependence of the reaction efficiency on the structural characteristics of cellulose, and its aggregation in solution. The cellulose samples employed included microcrystalline, MCC; mercerized cotton linters, M-cotton, and mercerized sisal, M-sisal. The reaction efficiency expresses the relationship between the degree of substitution, DS, of the ester obtained, and the molar ratio Ac(2)O/AGU (anhydroglucose unit of the biopolymer); 100% efficiency means obtaining DS = 3 at Ac(2)O/AGU = 3. For all celluloses, the dependence of DS on Ac(2)O/AGU is described by an exponential decay equation: DS = DS(o) - Ae(-[(Ac2O/AGU)/B]); (A) and (B) are regression coefficients, and DS(o) is the calculated maximum degree of substitution, achieved under the conditions of each experiment. Values of (B) are clearly dependent on the cellulose employed: B((M-cotton)) > B((M-sisal)) > B((MCC)); they correlate qualitatively with the degree of polymerization of cellulose, and linearly with the aggregation number, N(agg), of the dissolved biopolymer, as calculated from static light scattering measurements: (B) = 1.709 + 0.034 N(agg). To our knowledge, this is the first report on the latter correlation; it shows the importance of the physical state of dissolved cellulose, and serves to explain, in part, the need to use distinct reaction conditions for MCC and fibrous celluloses, in particular Ac(2)O/AGU, time, temperature.

A physical organic chemistry approach to dissolution of cellulose: effects of cellulose mercerization on its properties and on the kinetics of its decrystallization

The effects of alkali treatment on the structural characteristics of cotton linters and sisal cellulose samples have been studied. Mercerization results in a decrease in the indices of crystallinity and the degrees of polymerization, and an increase in the alpha-cellulose contents of the samples. The relevance of the structural properties of cellulose to its dissolution is probed by studying the kinetics of cellulose decrystallization, prior to its solubilization in LiCl/N,N-dimethylacetamide (DMAc). Our data show that the decrystallization rate constants and activation parameters are only slightly dependent on the physico-chemical properties of the starting celluloses. This multi-step reaction is accompanied by a small enthalpy and large, negative, entropy of activation. These results are analyzed in terms of the interactions within the biopolymer chains during decrystallization, as well as those between the two ions of the electrolyte and both DMAc and cellulose.

Spectroscopic Characterization of Oligoaniline Microspheres Obtained by an Aniline-Persulfate Approach

This paper investigates the structure of the pro; ducts obtained from the polymerization of aniline with ammonium persulfate in a citrate/phosphate buffer solution at pH 3 by resonance Raman, NMR, FTIR, and UV-vis-NIR spectroscopies. All the spectroscopic data showed that the major product presented segments that were formed by a 1,4-Michael reaction between aniline and p-benzoquinone monoimine, ruling out the formation of polyazane structure that has been recently proposed. The characterization of samples obtained at different stages of the reaction indicated that, as the reaction progressed, phenazine units were formed and 1,4-Michael-type adducts were hydrolyzed/oxidized to yield benzoquinone. Raman mapping data suggested that phenazine-like segments could be related to the formation of the microspheres morphology.

Charge-transfer behavior of polyaniline single wall carbon nanotubes nanocomposites monitored by resonance Raman spectroscopy

Highly dispersed nanocomposites of polyaniline(PANI) and oxidized single wall carbon nanotubes(SWNTs) have been prepared using dodecylbenzenesulfonic acid as dispersant. The materials were characterized via resonance Raman and electronic absorption spectroscopies. The behavior of the composites as a function of the applied potential was also investigated using in situ Raman electrochemical measurements. The results obtained at E(laser) = 1.17 eV suggest that a charge-transfer process occur between PANI and semiconducting nanotubes for samples where the metallic tubes are previously oxidized. The spectroelectrochemical data show that the presence of SWNTs prevents the oxidation of PANI rings. Copyright (C) 2010 John Wiley & Sons, Ltd.

Synthesis and spectroscopic characterization of polymer and oligomers of ortho-phenylenediamine

Poly(ortho-phenylenediamine) and oligomers of ortho-phenylenediamine were chemically synthesized and characterized by UV-vis, (1)H and (13)C NMR, FTIR and resonance Raman spectroscopies. Polymerization of ortho-phenylenediamine in HCl medium with ammonium persulfate only leads the trimer compound, in disagreement with some previous reports. Nevertheless, in acetic acid medium it was possible to prepare a polymer constituted by ladder phenazinic segments with different protonation levels and quinonediimine rings (polyaniline-like). X-ray absorption at N K-edge (N K XANES), X-ray photoelectron (XPS) and Electron paramagnetic resonance (EPR) spectroscopies were used to determine the different kinds of nitrogen presents in this class of polymer. N K XANES spectrum of poly(ortho-phenylenediamine) shows the band of -N=nitrogen of non-protonated phenazinic rings at 398.2 eV. In addition, XPS and N K XANES data confirm the presence of different types of protonated nitrogens in the polymeric poly(ortho-phenylenediamine) chain and the EPR spectrum shows that the polymer has a very weak polaronic signal. (C) 2009 Elsevier Ltd. All rights reserved.

Structure of chemically prepared poly-(para-phenylenediamine) investigated by spectroscopic techniques

The structure of chemically prepared poly-p-phenylenediamine (PpPD) was investigated by Resonance Raman (RR), FTIR, UV-VIS-NIR, X-ray photoelectron (XPS), X-ray Absorption at Nitrogen K edge (N K XANES), and Electron paramagnetic Resonance (EPR) spectroscopies. XPS, EPR and N K XANES data reveal that polymeric structure is formed mainly by radical cations and dication nitrogens. It excludes the possibility that PpPD chains have azo or phenazinic nitrogens, as commonly is supposed in the literature. The RR spectrum of PpPD shows two characteristic bands at 1527 cm(-1) and 1590 cm(-1) that were assigned to nu C=N and nu C=C of dication units, respectively, similar to polyaniline in pernigraniline base form. The presence of radical cations was confirmed by Raman data owing to the presence of bands at 1325/1370 cm(-1), characteristic of nu C-N of polaronic segments. Thus, all results indicate that PpPD has a doped PANT-like structure, with semi-quinoid and quinoid rings, and has no phenazinic rings, as observed for poly-o-phenylenediamine. (C) 2009 Elsevier Ltd. All rights reserved.

The role of cross-linking structures to the formation of one-dimensional nano-organized polyaniline and their Raman fingerprint

In the present work. the resonance Raman. UV-vis-NIR and scanning electron microscopic (SEM) data of nanorods (about similar to 300 rim in diameter) and nanofibers (about similar to 93 nm in diameter) of PANI are presented and compared. The PANI samples were synthesized in aqueous media with dodecybenzenesulfonic acid (DBSA) and beta-naphtalenesulfonic acid (beta-NSA) as dopants, respectively. The presence of hands at 578, 1400 and 1632cm(-1) in the Raman spectra of PANI-NSA and PANI-DBSA shows that the formation of cross-linking structures is a general feature of the PANI chains prepared in micellar media. It is proposed that these structures are responsible for the one-dimensional PANI morphology formation. In addition, the Raman band at 609cm(-1) of PANI fibers is correlated with the extended PANI chain coil formation. (C) 2008 Elsevier B.V. All rights reserved.

Laponite RD/polystyrenesulfonate nanocomposites obtained by photopolymerization

The present paper describes the synthesis and characterization by dynamic light scattering, X-ray diffraction, scanning electron microscopy and atomic force microscopy of Laponite RD/Sodium polystyrenesulfonate nanocomposites obtained by radical photopolymerization initiated by the cationic dye safranine. The presence of the clay mineral does not affect the hydrotropic aggregation of the monomers, but allows a better deaggregation of the initiator molecules, decreasing the quenching of the excited states that leads to the radicals that initiate polymerization. Increasing the amount of clay mineral loading in the polymerization mixture promotes higher monomer conversion and faster polymerization. The size of the nanocomposite particles, measured by light scattering decreases from 400 to 80 nm for clay mineral loadings of 1.0 wt.%. The X-ray diffraction patterns indicate that the clay mineral does not present a regular crystalline structure in the nanocomposite. Atomic force microscopy studies show films of sodium polystyrenesulfonate polymer with embedded Laponite platelets in its structure, forming 1-8 nm height and 25-100 nm diameter aggregates. (C) 2011 Elsevier B.V. All rights reserved.