Effects of Ultramorphological Changes on Adhesion to Lased Dentin-Scanning Electron Microscopy and Transmission Electron Microscopy Analysis

Dentin irradiation with erbium lasers has been reported to alter the composite resin bond to this treated surface. There is still a lack of studies reporting the effect of erbium lasers on dentin organic content and elucidating how laser treatment could interfere in the quality of the resin-dentin interface. This study aimed to evaluate the effect of erbium laser irradiation on dentin morphology and microtensile bond strength (lTBS) of an adhesive to dentin. Seventy-two dentin disks were divided into nine groups (n = 8): G1-Control (600-grit SiC paper); Er:YAG groups: G2-250 mJ/4 Hz; G3-200 mJ/4 Hz; G4-180 mJ/10 Hz; G5-160 mJ/10 Hz; Er, Cr:YSGG groups: G6-2 W/20 Hz; G7-2.5 W/20 Hz; G8-3 W/20 Hz; G9-4 W/20 Hz. Specimens were processed for cross-sectional analysis by scanning electron microscopy (SEM) (n = 3), transmission electron microscopy (TEM) (n = 2), and adhesive interface (n = 3). Forty-five dentin samples (n = 5) were restored and submitted to lTBS testing. ANOVA (alpha = 5%) revealed that G1 presented the highest lTBS values and irradiated groups did not differ from each other. TEM micrographs showed a superficial layer of denatured collagen fibrils. For SEM micrographs, it was possible to verify the laser effects extending to dentin subsurface presenting a rough aspect. Cross-sectional dentin micrographs of this hybridized surface revealed a pattern of modified tags with ringlike structures around it. This in vitro study showed that erbium laser irradiation interacts with the dental hard tissue resulting in a specific morphological pattern of dentin and collagen fibrils that negatively affected the bond strength to composite resin. Microsc. Res. Tech. 74:720-726, 2011. (C) 2010 Wiley-Liss, Inc.

Comparison of dentin root canal permeability and morphology after irradiation with Nd:YAG, Er:YAG, and diode lasers

The aim of this study was to compare the effects of Nd:YAG, Er:YAG, and diode lasers on the morphology and permeability of root canal walls. The three laser wavelengths mentioned interact differently with dentin and therefore it is possible that the permeability changes caused will determine different indications during endodontic treatment. Twenty-eight human single-rooted teeth were instrumented up to ISO 40 and divided into four groups: group C, control (GC), non-laser irradiated; group N (GN), irradiated with Nd:YAG laser; group E (GE), with Er:YAG laser and group D (GD) with diode laser. After that, the roots were filled with a 2% methylene blue dye, divided into two halves and then photographed. The images were analyzed using Image J software and the percentage of dye penetration in the cervical, middle, and apical root thirds were calculated. Additional scanning electron microscopy (SEM) analyses were also performed. The analysis of variance (ANOVA) showed significant permeability differences between all groups in the middle and cervical thirds (p < 0.05). The Tukey test showed that in the cervical third, GN presented means of dye penetration statistically significantly lower than all of the other groups. In the middle third, GE and GD showed statistically higher dye penetration means than GC and GN. SEM analysis showed melted surfaces for GN, clean wall surfaces with open dentinal tubules for GE, and mostly obliterated dentinal tubules for GD. Er:YAG (2,094 nm) laser and diode laser (808 nm) root canal irradiation increase dentinal permeability and Nd:YAG (1,064 nm) laser decreases dentin permeability, within the studied parameters.

Durability of Enamel Bonding Using One-step Self-etch Systems on Ground and Unground Enamel

Objective: To examine the morphological, early and long-term microtensile bond strengths (mu TBS) of one-step self-etch systems to unground and ground enamel. Materials and Methods: Resin composite (Filtek Z250) buildups were bonded to the buccal and lingual enamel surfaces (unground, bur-cut or SiC-roughened enamel) of third molars after adhesive application using the following adhesives: Clearfil S(3) Bond (CS3); Adper Prompt L-Pop (ADP); iBond (iB) and, as the control, Clearfil SE Bond (CSE). Six tooth halves were assigned for each condition. After storage in water (24 hours/37 degrees C), the bonded specimens were sectioned into beams (0.8 mm(2)) and subjected to pTBS (0.5 mm/min) either immediately (IM) or after six (6M) or 12 months (12M) of water storage. The data were analyzed by three-way repeated measures ANOVA and Tukey`s test (alpha=0.05). Surface conditioning was observed under scanning electron microscopy (SEM). Results: The mu TBS in the Si-C paper and diamond bur groups were similar and higher than the unground group. No significant difference was observed among the different storage periods, except for CS3, which showed an increase in the pTBS after 12M. The etching pattern was more retentive on ground enamel. Conclusions: One-step self-etch adhesives showed higher bond strengths on ground enamel and no reductions in resin-enamel bonds were observed after 12M of water storage.

Roughness of Human Enamel Surface Submitted to Different Prophylaxis Methods

The purpose of this in vitro study was to evaluate alterations in the surface roughness and micromorphology of human enamel submitted to three prophylaxis methods. Sixty-nine caries-free molars with exposed labial surfaces were divided into three groups. Group I was treated with a rotary instrument set at a low speed, rubber clip and a mixture of water and pumice; group II with a rotary instrument set at a low speed, rubber cup and prophylaxis paste Herjos-F (Vigodent S/A Industria e Comercio, Rio de Janeiro, Brazil); and group III with sodium bicarbonate spray Profi II Ceramic (Dabi A dante Indtistrias Medico Odontologicas Ltda, Ribeirao Preto, Brazil). All procedures were performed by the same operator for 10 s, and samples were rinsed and stored in distilled water. Pre and post-treatment surface evaluation was completed using a surface profilometer (Perthometer S8P Marh, Perthen, Germany) in 54 samples. In addition, the other samples were coated with gold and examined in a scanning electron microscope (SEM). The results of this study were statistically analyzed with the paired t-test (Student), the Kruskal-Wallis test and the Dunn (5%) test. The sodium bicarbonate spray led to significantly rougher surfaces than the pumice paste. The use of prophylaxis paste showed no statistically significant difference when compared with the other methods. Based on SEM analysis, the sodium bicarbonate spray presented an irregular surface with granular material and erosions. Based on this study, it can be concluded that there was an increased enamel stuface roughness when teeth were treated with sodium bicarbonate spray when compared with teeth treated with pumice paste.

Durability of enamel bonding using two-step self-etch systems on ground and unground enamel

This study examined the early and long-term microtensile bond strengths (mu TBS) and interfacial enamel gap formation (IGW) of two-step selfetch systems to unground and ground enamel. Resin composite (Filtek Z250) buildups were bonded to proximal enamel surfaces (unground, bur-cut or SiC-treated enamel) of third molars after the application of four self-etch adhesives: a mild (Clearfil SE Bond [SE]), two moderate (Optibond Solo Plus Self-Etch Primer [SO] and AdheSE [AD]) and a strong adhesive (Tyrian Self Priming Etchant + One Step Plus [TY]) and two etch-and-rinse adhesive systems (Single Bond [SB] and Scotchbond Multi-Purpose Plus [SBMP]). Ten tooth halves were assigned for each adhesive. After storage in water (24 hours/37 degrees C), the bonded specimens were sectioned into beams (0.9 mm(2)) and subjected to mu TBS (0.5 mm/minute) or interfacial gap width measurement (stereomicroscope at 400x) either immediately (IM) or after 12 months (12M) of water storage. The data were analyzed by three-way repeated measures ANOVA and Tukey`s test (alpha=0.05). No gap formation was observed in any experimental condition. The mu TBS in the Si-C paper and diamond bur groups were similar and greater than the unground group only for the moderate self-etch systems (SO and AD). No reductions in bond strength values were observed after 12 months of water storage, regardless of the adhesive evaluated.

Incidence, morphology and morphometry of the foramen of Vesalius: complementary study for a safer planning and execution of the trigeminal rhizotomy technique

The foramen of Vesalius (FV) is located in the greater wing of the sphenoid bone between the foramen ovale (FO) and the foramen rotundum in an intracranial view. The FO allows the passage of the mandibular branch of trigeminal nerve, which is the target of the trigeminal radiofrequency rhizotomy. We analyzed its location, morphology, morphometry and interrelation among other foramina. 400 macerated adult human skulls were examined. A digital microscope (Dino-Lite plus(A (R))) was used to capture images from the FV. A digital caliper was used to perform the measurements of the distance between the FV and other foramina (FO, foramen spinosum and the carotid canal) in an extracranial view of the skull base. In the 400 analyzed skulls, the FV was identified in 135 skulls (33.75%) and absent on both sides in 265 skulls (66.25%). The FV was observed present bilaterally in 15.5% of the skulls. The incidence of unilateral foramen was 18.25% of the skulls of which 7.75% on right side and 10.5% on left side. The diameter of the FV was measured and we found an average value of 0.65 mm, on right side 0.63 mm and on the left side 0.67 mm. We verified that positive correlations were statistically significant among the three analyzed distances. This study intends to offer specific anatomical data with morphological patterns (macroscopic and mesoscopic) to increase the understanding of the FV features as frequency, incidence and important distances among adjacent foramina.

Effect of Different Fluoride Concentrations of Experimental Dentifrices on Enamel Erosion and Abrasion

It has been suggested that fluoride products are able to reduce erosive tooth wear. Thus, the purpose of this in vitro study was to evaluate the effect of dentifrices with different fluoride concentrations as well as of a low-fluoridated dentifrice supplemented with trimetaphosphate (TMP) on enamel erosion and abrasion. One hundred twenty bovine enamel blocks were assigned to the following experimental dentifrices: placebo, 1,100 mu g F/g, 500 mu g F/g plus 3% TMP and 5,000 mu g F/g. The groups of enamel blocks were additionally subdivided into conditions of erosion (ERO) and of erosion plus abrasion (ERO + ABR). For 7 days, the blocks were subjected to erosive challenges (immersion in Sprite (R) 4 times a day for 5 min each time) followed by a remineralizing period (immersion in artificial saliva between erosive challenges for 2 h). After each erosive challenge, the blocks were exposed to slurries of the dentifrices (10 ml/sample for 15 s). Sixty of the blocks were additionally abraded by brushing using an electric toothbrush (15 s). The alterations of the enamel were quantified using the Knoop hardness test and profilometry (measurements in micrometers). The data were analyzed using a 2-way ANOVA test followed by a Bonferroni correction (p < 0.05). In in vitro conditions, the 5,000 mu g F/g and 500 mu g F/g plus 3% TMP dentifrices had a greater protective effect when compared with the 1,100 mu g F/g dentifrice, under both ERO and ERO + ABR conditions. The results suggest that dentifrices alone are not capable of completely inhibiting tooth wear. Copyright (C) 2010 S. Karger AG, Basel

Cross-Sectional Microhardness of Human Enamel Subjected to Erosive, Cariogenic or Combined Erosive/Cariogenic Challenges

This in situ study evaluated the interaction between caries and erosion processes. In the first phase, enamel specimens were subjected to erosion without dental plaque (EO) or to erosion with plaque (EP); in the second phase, they were subjected to erosion plus cariogenic challenge (EC) or cariogenic challenge (CO), both with plaque accumulation. Cross-sectional hardness data (10-330 mu m depth) were tested using ANOVA (alpha = 0.05). EO and EP showed surface softening to 10 mu m depth. CO and EC produced subsurface lesions, of similar depth (up to 220 mu m), with CO showing higher integrated loss of hardness than EC, indicating that cariogenic and erosive challenges did not have an additive effect. Copyright (C) 2010 S. Karger AG, Basel

Preventive Effect of Commercial Desensitizing Toothpastes on Bovine Enamel Erosion in vitro

This study evaluated in vitro commercial desensitizing toothpastes with respect to the prevention of erosion and explored the effect of their agents alone or in combination with fluoride. Bovine enamel blocks were randomly allocated to five groups of 20 and exposed to: Sensodyne ProNamel (1,425 ppm F as NaF, 5% KNO(3)), Sensodyne Original (no fluoride, 10% SrCl(2)), Colgate Sensitive (1,450 ppm F as sodium monofluorophosphate, 5% K citrate), Crest (fluoride-only toothpaste, 1,100 ppm F as NaF) and water (negative control). A second experiment was conducted with experimental dentifrices containing fluoride (NaF, 1,100 ppm F), 10% SrCl(2), 5% KNO(3) or 5% K citrate alone or the latter three combined with F. The samples were submitted to four cycles, alternating demineralization (cola, 10 min) and remineralization (artificial saliva, 1 h). Before and between cyclic de- and remineralization, blocks were treated with slurries of the respective toothpastes or water (1 min). Erosive tissue loss was analyzed by profilometry. Data were analyzed by Kruskal-Wallis and Dunn`s tests (p < 0.05). The mean erosion depth (+/- SE, mu m) was significantly less for Colgate Sensitive (0.04 +/- 0.00), Sensodyne Original (0.06 +/- 0.01) and Crest (0.07 +/- 0.01) than for Sensodyne ProNamel (2.36 +/- 0.25) or water (2.92 +/- 0.24), which did not significantly differ from each other. Both F and the desensitizing agents alone reduced erosion, but no additive effect was found. In addition, the combination of F and KNO(3) did not reduce erosion. These in vitro results suggest that the presence of fluoride or desensitizing substances in toothpastes, alone or in combination, can reduce erosion of enamel, but this is not valid for all the formulations. Copyright (C) 2010 S. Karger AG, Basel

Comparison of Cross-Sectional Hardness and Transverse Microradiography of Artificial Carious Enamel Lesions Induced by Different Demineralising Solutions and Gels

The aims of this study were: (1) to correlate surface (SH) and cross-sectional hardness (CSH) with microradiographic parameters of artificial enamel lesions; (2) to compare lesions prepared by different protocols. Fifty bovine enamel specimens were allocated by stratified randomisation according to their initial SH values to five groups and lesions produced by different methods: MC gel (methylcellulose gel/lactic acid, pH 4.6, 14 days); PA gel (polyacrylic acid/lactic acid/hydroxyapatite, pH 4.8, 16 h); MHDP (undersaturated lactate buffer/methyl diphosphonate, pH 5.0, 6 days); buffer (undersaturated acetate buffer/fluoride, pH 5.0, 16 h), and pH cycling (7 days). SH of the lesions (SH(1)) was measured. The specimens were longitudinally sectioned and transverse microradiography (TMR) and CSH measured at 10- to 220-mu m depth from the surface. Overall, there was a medium correlation but non-linear and variable relationship between mineral content and root CSH. root SH(1) was weakly to moderately correlated with surface layer properties, weakly correlated with lesion depth but uncorrelated with integrated mineral loss. MHDP lesions showed the highest subsurface mineral loss, followed by pH cycling, buffer, PA gel and MC gel lesions. The conclusions were: (1) CSH, as an alternative to TMR, does not estimate mineral content very accurately, but gives information about mechanical properties of lesions; (2) SH should not be used to analyse lesions; (3) artificial caries lesions produced by the protocols differ, especially considering the method of analysis. Copyright (C) 2009 S. Karger AG, Basel

Effect of ion supplementation of a commercial soft drink on tooth enamel erosion

Acidic soft drinks are potentially erosive for dental hard tissues. This in vitro study evaluated the effect of calcium, fluoride, iron and phosphate, supplemented alone or in combination to a commercial citric acid-based carbonated beverage on dental erosion. Ninety enamel samples (4 x 4 x 3 mm) were randomly allocated to nine groups (n = 10): G1 - pure beverage (control); G2 - with 1 mM Ca; G3 - with 0.047 mM F; G4 - with 1 mM Fe; G5 - with 1 mM P; G6 - with 1 mM Ca and 0.047 mM F; G7 - with 1 mM Ca and 1 mM P; G8 - with 1 mM Fe and 0.047 mM F; and G9 - with 1 mM Ca, 1 mM P, 0.047 mM F and 1.0 mM Fe. The samples were subjected to six pH cycles over a 24-h period. In each cycle, the samples were immersed in pure or modified beverage (1 min) and in artificial saliva (59 min). During the remaining period (18 h), the samples were maintained in artificial saliva. Enamel loss was assessed by profilometry (mm). Data were tested using ANOVA and Tukey`s tests (p < 0.05). Highest enamel losses were observed in the control group (G1) and in the groups containing Fe (G4 and G8). The groups containing Ca (G2 and G6) showed significantly less wear compared to control. In conclusion, the modification of an erosive soft drink with low concentrations of Ca with or without F may reduced its erosive potential.

Effect of erosive pH cycling on different restorative materials and on enamel restored with these materials

This in vitro study evaluated the effect of erosive pH cycling on the percentage of surface micro-hardness change (%SMHC) and wear of different restorative materials and bovine enamel restored with these materials. Eighty enamel specimens were randomly divided into eight groups according to the restorative materials and immersion media used: GI/GV-resin-modifled glass-ionomer, GII/GVI-conventional glass-ionomer, GIII/GVII-resin composite and GIV/GVIII-amalgam. Over a period of seven days, groups GI to GIV were immersed in a cola drink (ERO) for 5 minutes, 3x/day and kept in artificial saliva between erosive cycles. Groups GV to GVIII were immersed in artificial saliva (SAL) throughout the entire experimental period (control). Data were tested for significant differences using ANOVA and Tukey`s tests (p < 0.05). For %SMHC, considering the restorative materials, no significant differences were detected among the materials and immersion media. Mean wear was higher for the resin modified glass ionomer cement when compared to conventional cement, but those materials did not significantly differ from the others. For enamel analyses, erosive pH cycling promoted higher wear and %SMHC compared to saliva. There were no significant differences in wear and %SMHC of enamel around the different restorative materials, regardless of the distance from the restorative material (50, 150 or 300 mu m). In conclusion, there were only subtle differences among the materials, and these differences were not able to protect the surrounding enamel from erosion.

Effect of a 4% titanium tetrafluoride (TiF4) varnish on demineralisation and remineralisation of bovine enamel in vitro

Objectives: This in vitro study assessed the effect of a 4% TiF4 varnish on demineralisation and remineralisation of sound enamel and artificial carious enamel lesions, respectively. Methods: Bovine sound and carious enamel (n = 110) were randomly allocated to each type of varnish: Duraphat (R))-D (NaF, 2.26%F, pH 4.5, Colgate-Brazil, n = 30), Duofluorid (R)-F (NaF, 2.71%F, pH 8.0, FGM-Brazil, n = 30), TiF4-T (2.45%F, pH 1.0, FGM-Brazil, n = 30) and no-fluoride-P (FGM-Brazil, pH 5.0, n = 20). For the formation of artificial enamel caries, half of the blocks were immersed in 32 mL buffer acetate solution (16 h), whereas the other half was maintained sound. The varnishes were applied onto the enamel surfaces. Thus, the samples were subjected to pH cycles (37 degrees C) for 7 days. The response variables tested were surface and cross-sectional hardness. Data were tested using Kruskal-Wallis test (p < 0.05). Results: All F varnishes significantly reduced demineralisation and increased remineralisation in comparison to placebo. The TiF4 did not significantly reduce the surface enamel softening when compared with the other F varnishes, but it decreased the loss of subsurface hardness to the same extent. In enamel blocks with previous artificial carious lesions, the TiF4 significantly improved the rehardening compared to the other varnishes up to 30 mu m depth. Conclusions: The TiF4 varnish was able to decrease the demineralisation and increase the remineralisation of previously sound and carious enamel, respectively. It was equally effective compared to NaF varnishes on reducing the demineralisation at subsurface, but it was more effective on improving the remineralisation at surface and subsurface. (c) 2007 Elsevier Ltd. All rights reserved.

Effects of Erosive, Cariogenic or Combined Erosive/Cariogenic Challenges on Human Enamel An in situ/ex vivo Study

Individuals with cariogenic diet can also consume erosive beverages. Thus, it seems necessary to investigate a possible caries/erosion interaction. To test in situ/ex vivo a combination of these challenges, 11 subjects wore intraoral appliances containing four enamel blocks randomly assigned. In the first 2-week phase, the appliances were immersed in a cola drink 3 times/day. Two blocks were free of plaque (erosion only: EO) and two blocks were covered with plaque (erosion + plaque: EP). In the second 2-week phase, four new blocks were all covered with plaque and subjected to a sucrose solution 8 times/day. Among the four new blocks, two were also subjected to the cola drink 3 times/day (erosion + caries: EC) while the other two were not (caries only: CO). Thus, in EO, the specimens were fixed at the intraoral appliance level. In EP, EC and CO they were fixed 1.0 mm under the appliance level and covered with plastic meshes for dental plaque accumulation. Changes in wear and hardness were measured. Data were tested using ANOVA and Tukey`s test (p < 0.05). Mean values of wear (mu m) and change in hardness (kp/mm(2)) were: EO 4.82/310; EP 0.14/48; EC 0.34/245; CO 0.42/309. With respect to surface softening, EP and EC differed significantly from each other and from EO and CO, which did not differ significantly. EO presented significantly higher wear than the other groups. The data suggest that the presence of dental plaque can decrease the acid attack of an erosive drink and the association of erosive and cariogenic challenges showed less enamel alterations when compared to erosive or cariogenic challenges only. Copyright (C) 2008 S. Karger AG, Basel

Enamel Wetness Effects on Bond Strength Using Different Adhesive Systems

Objective: To evaluate, through the application of different dentin bonding systems, the influence of wetness on shear bond strength in enamel. Methods: This study evaluated three etch-and-rinse adhesive systems (Scotchbond MP [used with and without primer]; Singlebond; and Prime&Bond 2.1) and two self-etching adhesive systems (Clearfil SE Bond; and Xeno IV). Flat bovine enamel surfaces were either air-dried for 30 seconds or blotted with absorbent paper after acid-etching for the conventional bonding agents or before the application of self-etching bonding agents. The resin composite EsthetX was bonded to flat surfaces that had been treated with one of the adhesives, following the manufacturer`s instructions. After being stored in water at 37 degrees C for one week, bonded specimens were broken in shear. Data were evaluated with two-way analysis of variance (ANOVA) and Student-Newman-Keuls tests (alpha=0.05). For comparing each condition individually, regardless of the adhesive or wetness condition, a one-way ANOVA and a Student-Newman-Keuls test (alpha=0.05) were applied. Results: The two-way ANOVA showed significant differences among adhesive systems. An interaction effect was also observed (p < 0.05), but wetness did not influence shear bond strength (p=0.98). The one-way ANOVA showed that the all-in-one adhesive was the only material influenced by the presence of water at the enamel`s surface. Conclusion: The all-in-one adhesive behaved differently depending on whether the enamel surface was dry or wet.