The role of surface sealants in the roughness of composites after a simulated toothbrushing test

Objectives: To evaluate the influence of two surface sealants (BisCover/Single Bond) and three application techniques (unsealed/conventional/co-polymerization) on the roughness of two composites (Filtek Z250/Z350) after the toothbrushing test. Methods: Seventy-two rectangular specimens (5 mm x 10 mm x 3 mm) were fabricated and assigned into 12 groups (n = 6). Each sample was subjected to three random roughness readings at baseline, after 100,000 (intermediate), and 200,000 (final) toothbrushing strokes. Roughness (R) at each stage was obtained by the arithmetic mean of the reading of each specimen. Sealant removal was qualitatively examined (optical microscope) and classified into scores (0-3). Data were analyzed by Student`s paired t-test, two-way ANOVA/Tukey`s test, and by Wilcoxon, Kruskal-Wallis and Miller`s test (alpha = 0.05). Results: Z250 groups at baseline did not differ statistically from each other. Unsealed Z350 at baseline had lower R values. All the unsealed groups presented gradual decrease in R from baseline to final brushing. From baseline to the inter-mediate stage, Z250 co-polymerized groups presented a significant reduction in R (score 3). Conventionally sealed groups had no significant changes in R (scores 2-0.8). From baseline to the intermediate stage, the conventionally sealed Z350 Single Bond group had an increase in R (score 1.5). In the final stage, all the conventionally sealed groups presented a reduction in R (scores 0.7-0). Co-polymerized Single Bond groups had a significant reduction in R (scores 2.5-2.7), and co-polymerized BisCover groups an increase in R (scores 2.8-3). Conclusions: At any brushing stage, sealed composites presented superior performance when compared with unsealed composites. (C) 2009 Elsevier Ltd. All rights reserved.

Evaluation of the temperature of different refrigerant sprays used as a pulpal test

The temperature of different refrigerant sprays (Endo-Ice, Endo-Frost, Coolermatic and Sprayon Contact and Tuner Cleaner) used as pulpal tests were evaluated in vitro. A thermocouple placed inside the pulp chamber of a maxillary central incisor was used to register the temperature changes when the refrigerant sprays were applied with a cotton swab, for 10 s. Results indicate that Endo-Ice and Endo-Frost presented the lowest temperatures among the refrigerant sprays tested. Temperatures measured inside the pulp chamber, however, were statistically similar in all groups.

The Effect of Framework Design on Fracture Resistance of Metal-Ceramic Implant-Supported Single Crowns

This study evaluated the effect of framework design on the fracture resistance of metal-ceramic implant-supported crowns. Screw-retained molar crowns with a screw access hole composed of metal or porcelain were compared to a cement-retained crown (control). For each group (n = 10), five crowns were subjected to dynamic loading (1,200,000 x 100 N x 2 Hz at 37 degrees C). Afterward, all specimens were loaded to failure using a universal testing machine. Significant differences could be established between the cement-and screw-retained groups (P <= .05), but no difference was found between the screw-retained groups and the specimens subjected to dynamic loading. Occlusal discontinuity of screw-retained crowns affects their resistance, and the metallic support on the screw access hole did not reinforce the crowns. Int J Prosthodont 2010;23:350-352.

Effect of cantilever length and framework alloy on the stress distribution of mandibular-cantilevered implant-supported prostheses

The purpose of this in vitro study was to analyze the stress distribution on components of a mandibular-cantilevered implant-supported prosthesis with frameworks cast in cobalt-chromium (Co-Cr) or palladium-silver (Pd-Ag) alloys, according to the cantilever length. Frameworks were fabricated on (Co-Cr) and (Pd-Ag) alloys and screwed into standard abutments positioned on a master-cast containing five implant replicas. Two linear strain gauges were fixed on the mesial and distal aspects of each abutment to capture deformation. A vertical static load of 100 N was applied to the cantilever arm at the distances of 10, 15, and 20 mm from the center of the distal abutment and the absolute values of specific deformation were recorded. Different patterns of abutment deformation were observed according to the framework alloy. The Co-Cr alloy framework resulted in higher levels of abutment deformation than the silver-palladium alloy framework. Abutment deformation was higher with longer cantilever extensions. Physical properties of the alloys used for framework interfere with abutment deformations patterns. Excessively long cantilever extensions must be avoided. To cite this article:Jacques LB, Moura MS, Suedam V, Souza EAC, Rubo JH. Effect of cantilever length and framework alloy on the stress distribution of mandibular-cantilevered implant-supported prostheses.Clin. Oral Impl. Res. 20, 2009; 737-741.doi: 10.1111/j.1600-0501.2009.01712.x.

Effect of abutment`s height and framework alloy on the load distribution of mandibular cantilevered implant-supported prosthesis

In cantilevered implant-supported complete prosthesis, the abutments` different heights represent different lever arms to which the abutments are subjected resulting in deformation of the components, which in turn transmit the load to the adjacent bone. The purpose of this in vitro study was to quantitatively assess the deformation of abutments of different heights in mandibular cantilevered implant-supported complete prosthesis. A circular steel master cast with five perforations containing implant replicas (O3.75 mm) was used. Two groups were formed according to the types of alloy of the framework (CoCr or PdAg). Three frameworks were made for each group to be tested with 4, 5.5 and 7 mm abutments. A 100 N load was applied at a point 15 mm distal to the center of the terminal implant. Readings of the deformations generated on the mesial and distal aspects of the abutments were obtained with the use of strain gauges. Deformation caused by tension and compression was observed in all specimens with the terminal abutment taking most of the load. An increase in deformation was observed in the terminal abutment as the height was increased. The use of an alloy of higher elastic modulus (CoCr) also caused the abutment deformation to increase. Abutment`s height and framework alloy influence the deformation of abutments of mandibular cantilevered implant-supported prosthesis. To cite this article:Suedam V, Capello SouzaEA, Moura MS, Jacques LB, Rubo JH. Effect of abutment`s height and framework alloy on the load distribution of mandibular cantilevered implant-supported prosthesis. Clin. Oral Impl. Res. 20, 2009; 196-200.doi: 10.1111/j.1600-0501.2008.01609.x.

Fatigue life and failure modes of crowns systems with a modified framework design

Objectives: To evaluate the effect of framework design on the fatigue life and failure modes of metal ceramic (MC, Ni-Cr alloy core, VMK 95 porcelain veneer), glass-infiltrated alumina (ICA, In-Ceram Alumina/VM7), and veneered yttria-stabilized tetragonal zirconia polycrystals (Y-TZP, IPSe.max ZirCAD/IPS e.max,) crowns. Methods: Sixty composite resin tooth replicas of a prepared maxillary first molar were produced to receive crowns systems of a standard (MCs, ICAs, and Y-TZPs, n = 10 each) or a modified framework design (MCm, ICAm, and Y-TZPm, n = 10 each). Fatigue loading was delivered with a spherical steel indenter (3.18 mm radius) on the center of the occlusal surface using r-ratio fatigue (30-300 N) until completion of 10(6) cycles or failure. Fatigue was interrupted every 125,000 cycles for damage evaluation. Weibull distribution fits and contour plots were used for examining differences between groups. Failure mode was evaluated by light polarized and SEM microscopy. Results: Weibull analysis showed the highest fatigue life for MC crowns regardless of framework design. No significant difference (confidence bound overlaps) was observed between ICA and Y-TZP with or without framework design modification. Y-TZPm crowns presented fatigue life in the range of MC crowns. No porcelain veneer fracture was observed in the MC groups, whereas ICAs presented bulk fracture and ICAm failed mainly through the veneer. Y-TZP crowns failed through chipping within the veneer, without core fractures. Conclusions: Framework design modification did not improve the fatigue life of the crown systems investigated. Y-TZPm crowns showed comparable fatigue life to MC groups. Failure mode varied according to crown system. (C) 2010 Elsevier Ltd. All rights reserved.

Effect of framework design on crown failure

This study evaluated the effect of core-design modification on the characteristic strength and failure modes of glass-infiltrated alumina (In-Ceram) (ICA) compared with porcelain fused to metal (PFM). Premolar crowns of a standard design (PFMs and ICAs) or with a modified framework design (PFMm and ICAm) were fabricated, cemented on dies, and loaded until failure. The crowns were loaded at 0.5 mm min(-1) using a 6.25 mm tungsten-carbide ball at the central fossa. Fracture load values were recorded and fracture analysis of representative samples were evaluated using scanning electron microscopy. Probability Weibull curves with two-sided 90% confidence limits were calculated for each group and a contour plot of the characteristic strength was obtained. Design modification showed an increase in the characteristic strength of the PFMm and ICAm groups, with PFM groups showing higher characteristic strength than ICA groups. The PFMm group showed the highest characteristic strength among all groups. Fracture modes of PFMs and of PFMm frequently reached the core interface at the lingual cusp, whereas ICA exhibited bulk fracture through the alumina core. Core-design modification significantly improved the characteristic strength for PFM and for ICA. The PFM groups demonstrated higher characteristic strength than both ICA groups combined.