Failure modes of Y-TZP crowns at different cusp inclines

Objectives To compare the reliability of the disto-facial (DF) and mesio-lingual (ML) cusps of an anatomically correct zirconia (Y-TZP) crown system The research hypotheses tested were (1) fatigue reliability and failure mode are similar for the ML and DF cusps, (2) failure mode of one cusp does not affect the failure of the other Methods The average dimensions of a mandibular first molar crown were imported into CAD software, a tooth preparation was modelled by 1 5 mm marginal high reduction of proximal walls and occlusal surface by 2 0 mm The CAD-based tooth preparation was milled and used as a die to fabricate crowns (n = 14) with porcelain veneer on a 0 5 mm Y-TZP core. Crowns were cemented on composite reproductions of the tooth preparation The crowns were step-stress mouth motion fatigued with sliding (0 7 mm) a tungsten-carbide indenter of 6 25 mm diameter down on the inclines of either the DF or ML cusps Use level probability Weibull curve with use stress of 200 N and the reliability for completion of a mission of 50,000 cycles at 200 N load were calculated Results Reliability for a 200 N at 50,000 cycles mission was not different between tested cusps SEM imaging showed large cohesive failures within the veneer for the ML and smaller for the DF Fractures originated from the contact area regardless of the cusp loaded Conclusion No significant difference on fatigue reliability was observed between the DF compared to the ML cusp Fracture of one cusp did not affect the other (c) 2010 Elsevier Ltd All rights reserved

Fatigue and damage accumulation of veneer porcelain pressed on Y-TZP

Objectives: This study compared the reliability and fracture patterns of zirconia cores veneered with pressable porcelain submitted to either axial or off-axis sliding contact fatigue. Methods: Forty-two Y-TZP plates (12 mm x 12 mm x 0.5 mm) veneered with pressable porcelain (12 mm x 12 mm x 1.2 mm) and adhesively luted to water aged composite resin blocks (12 mm x 12 mm x 4 mm) were stored in water at least 7 days prior to testing. Profiles for step-stress fatigue (ratio 3:2:1) were determined from single load to fracture tests (n = 3). Fatigue loading was delivered on specimen either on axial (n = 18) or off-axis 30 degrees angulation (n = 18) to simulate posterior tooth cusp inclination creating a 0.7 mm slide. Single load and fatigue tests utilized a 6.25 mm diameter WC indenter. Specimens were inspected by means of polarized-light microscope and SEM. Use level probability Weibull curves were plotted with 2-sided 90% confidence bounds (CB) and reliability for missions of 50,000 cycles at 200 N (90% CB) were calculated. Results: The calculated Weibull Beta was 3.34 and 2.47 for axial and off-axis groups, respectively, indicating that fatigue accelerated failure in both loading modes. The reliability data for a mission of 50,000 cycles at 200 N load with 90% CB indicates no difference between loading groups. Deep penetrating cone cracks reaching the core-veneer interface were observed in both groups. Partial cones due to the sliding component were observed along with the cone cracking for the off-axis group. No Y-TZP core fractures were observed. Conclusions: Reliability was not significantly different between axial and off-axis mouth-motion fatigued pressed over Y-TZP cores, but incorporation of sliding resulted in more aggressive damage on the veneer. (C) 2009 Elsevier Ltd. All rights reserved.

Morphodigital study of bone quality in the mandibular angle in patients with third molar impacted

The aim of this study was to analyze if the presence of impacted third molars, and their positions in the mandibular angle, can change the bone quality in this area, considering the measure of the cortical thickness in this region as representative or not for mandible fracture risk. Software was used to analyze 50 digital images from panoramic radiographs of patients who had one or two impacted third molars in the mandible, and 30 digital images of patients with agenesis of the mandibular third molar. The thickness of the cortical region of the mandible was measured; it was possible to draw a parallel line to the posterior portion of the mandible and a parallel line to the body of this bone on each side of the image. At the intersection of these lines near the distal portion of the second molar, another line was set up to serve as reference in the cortical thickness measurement. It could be concluded that the cortical thickness of the mandibular angle in male patients without impacted third molars was greater than the thickness in patients with these teeth, and no difference in thickness was found for the female group.

Bone repair in mandibular body osteotomy after using 2.0 miniplate system - histological and histometric analysis in dogs

The objective of this study was to evaluate the bone repair along a mandibular body osteotomy after using a 2.0 miniplate system. Nine adult mongrel dogs were subjected to unilateral continuous defect through an osteotomy between the mandibular 3rd and 4th premolars. Two four-hole miniplates were placed in accordance with the Arbeitgeimeinschaft fur Osteosynthesefragen Manual. Miniplates adapted to the alveolar processes were fixed monocortically with 6.0-mm-length titanium alloy self-tapping screws, whereas miniplates placed near the mandible bases were fixed bicortically. At 2, 6 and 12 weeks, three dogs were sacrificed per period, and the osteotomy sites were removed, divided into three thirds (Tension Third, TT; Intermediary Third, IT; Compression Third, CT) and prepared for conventional and polarized light microscopy. At 6 weeks, while the CT repaired faster and showed bone union by woven bone formation, the TT and IT exhibited a ligament-like fibrous connective tissue inserted in, and connecting, newly formed woven bone overlying the parent lamellar bone edges. At 12 weeks, bone repair took place at all thirds. Histometrically, proportions of newly formed bone did not alter at TT, IT and CT, whereas significantly enhanced bone formation was observed for the 12-week group, irrespective of the third. The results demonstrated that although the method used to stabilize the mandibular osteotomy allowed bone repair to occur, differences in the dynamics of bone healing may take place along the osteotomy site, depending on the action of tension and compression forces generated by masticatory muscles.

IN VITRO FRACTURE RESISTANCE OF GLASS-FIBER AND CAST METAL POSTS WITH DIFFERENT LENGTHS

Statement of problem. Dental fractures can occur in endodontically treated teeth restored with posts. Purpose. The purpose of this study was to evaluate the in vitro fracture resistance of roots with glass-fiber and metal posts of different lengths. Material and methods. Sixty endodontically treated maxillary canines were embedded in acrylic resin, except for 4 mm of the cervical area, after removing the clinical crowns. The post spaces were opened with a cylindrical bur at low speed attached to a surveyor, resulting in preparations with lengths of 6 mm (group 6 mm), 8 mm (group 8 mm), or 10 mm (group 10 mm). Each group was divided into 2 subgroups according to the post material: cast post and core or glass-fiber post (n=30). The posts were luted with dual-polymerizing resin cement (Panavia F). Cast posts and cores of Co-Cr (Resilient Plus) crowns were made and cemented with zinc phosphate. Specimens were subjected to increasing compressive load (N) until fracture. Data were analyzed with 2-way ANOVA and the Tukey-Kramer test (alpha=.05). Results. The ANOVA analysis indicated significant differences (P<.05) among the groups, and the Tukey test revealed no significant difference among the metal posts of 6-mm length (26.5 N +/- 13.4), 8-mm length (25.2 N +/- 13.9), and 10-mm length (17.1 N +/- 5.2). Also, in the glass-fiber post group, there was no significant difference when posts of 8-mm length (13.4 N +/- 11.0) were compared with the 6-mm (6.9 N +/- 4.6) and 10-mm (31.7 N +/- 13.1) groups. The 10-mm-long post displayed superior fracture resistance, and the 6-mm-long post showed significantly lower mean values (P<.001). Conclusions. Within the limitations of this study, it was concluded that the glass-fiber post represents a viable alternative to the cast metal post, increasing the resistance to fracture of endodontically treated canines. (J Prosthet Dent 2009;101:183-188)