Flow injection analysis using carbon film resistor electrodes for amperometric determination of ambroxol

Flow injection analysis (FIA) using a carbon film sensor for amperometric detection was explored for ambroxol analysis in pharmaceutical formulations. The specially designed flow cell designed in the lab generated sharp and reproducible current peaks, with a wide linear dynamic range from 5 x 10(-7) to 3.5 x 10(-4) mol L-1, in 0.1 mol L-1 sulfuric acid electrolyte, as well as high sensitivity, 0.110 A mol(-1) L cm(-2) at the optimized flow rate. A detection limit of 7.6 x 10(-8) mol L-1 and a sampling frequency of 50 determinations per hour were achieved, employing injected volumes of 100 mu L and a flow rate of 2.0 mL min(-1). The repeatability, expressed as R.S.D. for successive and alternated injections of 6.0 x 10(-6) and 6.0 x 10(-5) mol L-1 ambroxol solutions, was 3.0 and 1.5%, respectively, without any noticeable memory effect between injections. The proposed method was applied to the analysis of ambroxol in pharmaceutical samples and the results obtained were compared with UV spectrophotometric and acid-base titrimetric methods. Good agreement between the results utilizing the three methods and the labeled values was achieved, corroborating the good performance of the proposed electrochemical methodology for ambroxol analysis. (C) 2008 Elsevier B.V. All rights reserved.

Histological evaluation of chitosan-based biomaterials used for the correction of critical size defects in rat`s calvaria

Chitosan, a biopolymer obtained from chitin, and its derivates, such as chitosan hydrochloride, has been reported as wound healing accelerators and as possible bone substitutes for tissue engineering, and therefore these Substances could be relevant in dentistry and periodontology. The purpose of this investigation was to make a histological evaluation of chitosan and chitosan hydrochloride biomaterials (gels) used in the correction of critical size bone defects made in rat`s calvaria. Bone defects of 8 mm in diameter were surgically created in the calviria of 50 Holtzman (Rattus norvegicus) rats and filled with blood clot (control), low molecular weight chitosan, high molecular weight chitosan, low molecular weight chitosan hydrochloride, and high molecular weight chitosan hydrochloride, numbering 10 animals, divided into two experimental periods (15 and 60 days), for each biomaterial. The histological evaluation was made based on the morphology of the new-formed tissues in defect`s region, and the results indicated that there was no statistical difference between the groups when the new bone formation in the entire defect`s area were compared (p > 0.05) and, except in the control groups, assorted degrees of inflammation Could be Seen. In Conclusion, chitosan and chitosan hydrochloride biomaterials used in this study were not able to promote new bone formation in critical size defects made in rat`s calvaria. (C) 2009 Wiley Periodicals, Inc. J Biomed Mater Res 93A: 107-114, 2016

Thermal and spectrophotometric studies of new crosslinking method for collagen matrix with glutaraldehyde acetals

Despite the many existing crosslinking procedures, glutaraldehyde (GA) is still the method of choice used in the manufacture of bioprosthesis. The major problems with GA are: (a) uncontrolled reactivity due to the chemical complexity or GA solutions; (b) toxicity due to the release of GA from polymeric crosslinks; and (c) tissue impermeabilization due to polymeric and heterogeneous crosslinks formation, partially responsible for the undesirable calcification of the bioprosthesis. A new method of crosslinking glutaraldehyde acetals has been developed with GA in acid ethanolic solution, and after the distribution inside de matrix, GA is released to crosslinking. Concentrations of hydrochloride acid in ethanolic solutions between 0.1 and 0.001 mol/L with GA concentration between 0.1 and 1.0% were measured in an ultraviolet spectrophotometer to verify the presence of free aldehyde groups and polymeric compounds of GA. After these measurements, the solutions were used to crosslink bovine pericardium. The spectrophotometric results showed that GA was better protected in acetal forms for acid ethanolic solution with HCl at 0.003 mol/L and GA 1.0%(v/v). The shrinkage temperature results of bovine pericardium crosslinked with acetal solutions showed values near 85 C after the exposure to triethylamine vapors.

Electrochemical Behavior of Verapamil at Graphite-Polyurethane Composite Electrodes: Determination of Release Profiles in Pharmaceutical Samples

A solid graphite-polyurethane composite electrode has been used to determine release profiles of verapamil, a calcium-channel blocker. The electro-oxidation process was characterized by cyclic voltammetry and electrochemical impedance spectroscopy and showed no adsorption of analyte or oxidation products, unlike at other carbon-based electrodes. Quantification gave linear ranges up to 40molL-1 with cyclic voltammetry and detection limits of 0.7molL-1 by differential pulse and square-wave voltammetry. Commercial product samples were successfully analyzed with results equal to those from spectrophotometry. Because no electrode surface renewal is needed, this electrode material has many advantages.