Effect of oxalate desensitizers and dentin moisture during total-etch bonding

Purpose: To evaluate the effect of oxalate during total-etch bonding, under different dentin moisture conditions, over time. The null hypothesis tested was that microtensile bond strength (mu TBS) was not affected by oxalate treatment and dentin moisture during two evaluation periods. Methods: Extracted human third molars had their mid-coronal dentin exposed flat and polished with 600-grit SiC paper. The surfaces were etched with 35% phosphoric acid for 15 seconds, washed and blot dried. After etching, a 3% potassium oxalate gel was applied for 120 seconds, except for the control group (no desensitizer). The surface was then washed and left moist (Wet bonding) or air-dried for 30 seconds (Dry bonding). The surfaces were bonded with: (I) two 2-step etch-and-rinse adhesives: Single Bond (SB); Prime & Bond NT (PBNT) and (2) one 3-step etch-and-rinse adhesive: Scotchbond Multi Purpose (SBMP). Composite buildups were constructed incrementally with Tetric Ceram resin composite. Each increment was cured for 40 seconds. After storage in water for 24 hours or 1 year at 37 C, the specimens were prepared for mu TBS testing with a cross-sectional area of approximately 1 mm(2). They were then tested in tension in an Instron machine at 0.5 mm/minute. Data were analyzed by ANOVA and Student-Newman-Keuls at alpha = 0.05. Results: Application of potassium oxalate had no significant effect on the bond strengths of SBMP and PBNT, regardless of the surface moisture condition (P > 0.05). Conversely, reduced bond strengths were observed after oxalate treatment for SB in both moisture conditions, that being significantly lower when using a dry-bonding procedure (P < 0.05). Lower bond strength was obtained for PBNT when a dry-bonding technique was used, regardless of the oxalate treatment (P < 0.05). After aging the specimens for 1 year, bond strengths decreased. Smaller reductions were observed for SBMP, regardless of moisture conditions. For the WB technique, smaller reductions after 1 year were observed without oxalate treatment for SB and after oxalate treatment for PBNT. (Am J Dent 2010;23:137-141).

The influence of storage condition and duration on the resistance to fracture of different fiber post systems

Purpose: To evaluate the effects of storage condition and duration on the resistance to fracture of different fiber post systems (and to morphologically assess the post structure before and after storage. Methods: Three types of fiber posts (DT Light Post, GC Post, FRC Postect Plus) were divided in different groups (n=12) according to the storage condition (dry at 37 degrees C; saline water at 37 degrees C; mineral oil at 37 degrees C and storage inside the roots of extracted human teeth immersed in saline water at 37 degrees C and duration (6, 12 months). A universal testing machine loading at a 90 degrees angle was employed for the three-point bending test. The test was carried out until fracture of the post. A 3-way ANOVA and Tukey`s test (alpha= 0.05) were used to compare the effect of the experimental factors on the fracture strength. Two posts of each group were observed before and after the storage using a scanning electron microscope. Results: Storage condition and post type had a significant effect on post fracture strength (P< 0.05). The interaction between these factors was significant (P< 0.05). Water storage significantly decreased the fracture strength, regardless of the post type and the storage duration. Storage inside roots, in oil, and at dry conditions did not significantly affect post fracture strength. SEM micrographs revealed voids between fibers and resin matrix for posts stored in water. Posts stored under the other conditions showed a compact matrix without porosities. (Am J Dent 2009;22:366-370).

Evaluation of several protocols for the application of ultrasound during the removal of cast intraradicular posts cemented with zinc phosphate cement

To evaluate several protocols for the application of ultrasound during removal of cast posts with varying core configurations cemented with zinc phosphate. Sixty maxillary canines were distributed into three groups (n = 20): group 1 - core with 5 mm diameter/height and post diameter of 1.3 mm; groups 2 and 3 - core with the same diameter as the post (1.3 mm) and heights of 5 mm and 3 mm, respectively. Posts/cores were cemented using a standard technique with zinc phosphate cement. Each group was divided into two subgroups according to the ultrasonic vibration mode: point vibration - ultrasonic vibration applied to the core surface for 5 s, on each face totalling 25 s; alternate vibration - intermittent application of ultrasonic vibration for 10 s to the labial and lingual surfaces, 10 s to the mesial and distal surfaces and 5 s to the incisal surface, totalling 25 s. The specimens were submitted to the tensile test using an Instron machine (1 mm min(-1)) and results were analysed by anova and t-test. The failure type was also analysed. Statistical analysis showed significant differences between groups relating to the core preparations (P < 0.05). The lowest mean values of traction force were obtained for group 3 (46.1 +/- 7.7 N), followed by group 2 (89.0 +/- 2.7 N) and group 1 (160.4 +/- 7.5 N). Regarding ultrasonic vibration, the lowest mean was observed with alternate vibration (81.1 +/- 10.1 N), which was significantly lower than the point vibration (115.9 +/- 9.5 N) (P < 0.05). Cohesive failure occurred in all cases. A reduction in core diameter/height and intermittent ultrasonic application improved the removal of cast posts cemented with zinc phosphate.