Corrosion behavior of pure titanium in artificial saliva solution

The biocompatibility of commercially pure (cp) titanium stems from its chemical stability within an organism, due to a fine film of impermeable titanium oxide covering the metal surface, which guarantees its resistance to corrosion. Despite its biocompatible characteristic, this material does not promote the formation of a hydroxyapatite layer, therefore, many research groups have sought to alter the material`s surface, introducing modifications that might influence corrosion resistance. The electrochemical behavior of cp Ti, with hydroxyapatite coating and without hydroxyapatite coating, commonly used in implant materials, was investigated using an artificial saliva solution at 25 degrees C and pH=7.4. In the conditions of the study it was observed that the hydroxyapatite layer influences the properties of corrosion resistance. This study of the behavior of cp Ti with and without hydroxyapatite coating, in naturally aerated artificial saliva solution at 25 degrees C, was based on open circuit potential measurements and potentiodynamic polarization curves. At approximately 1x10(-6) A/cm(2) the potential for cp Ti with and without hydroxyapatite coating begins to increase at a faster rate, but at -74mV (SCE) for coated cp Ti and at 180mV (SCE) for uncoated cp Ti the increase in potential begins to slow. This behavior, characterized by a partial stabilization of current density, indicates that in those potential ranges a protective passive film is formed.

Template-based quadrilateral mesh generation from imaging data

This paper describes a novel template-based meshing approach for generating good quality quadrilateral meshes from 2D digital images. This approach builds upon an existing image-based mesh generation technique called Imeshp, which enables us to create a segmented triangle mesh from an image without the need for an image segmentation step. Our approach generates a quadrilateral mesh using an indirect scheme, which converts the segmented triangle mesh created by the initial steps of the Imesh technique into a quadrilateral one. The triangle-to-quadrilateral conversion makes use of template meshes of triangles. To ensure good element quality, the conversion step is followed by a smoothing step, which is based on a new optimization-based procedure. We show several examples of meshes generated by our approach, and present a thorough experimental evaluation of the quality of the meshes given as examples.

Unravelling the Chemical Morphology of a Mesoporous Titanium Dioxide Interface by Confocal Raman Microscopy: New Clues for Improving the Efficiency of Dye Solar Cells and Photocatalysts

The presence of anatase and rutile domains on nanocrystalline films of P25 TiO(2), as well as the distinct coordination modes of carboxylates on those phases, were revealed by confocal Raman microscopy, a technique that showed to be suitable for imaging the chemical morphology down to submicrometric size.

Surface Properties of Calcinated Titanium Dioxide Probed by Solvatochromic Indicators: Relevance to Catalytic Applications

Titanium dioxide was obtained by hydrolysis of the corresponding ethoxide, followed by washing, drying, and calcination at 80, 160, 240, 320, 400, and 700 C, respectively. The following surface properties of the solids obtained were determined as a function of the calcinations temperature: T(Calcn); area by the BET method; BrOnsted acidity by titration with sodium hydroxide; empirical polarity, ET(30); Lewis acidity, alpha(Surf); Lewis basicity, beta(Surf); and dipolarity/polarizability pi*(Sturf), by use of solvatochromic indicators. Except for le surf whose value increased slightly, heating the samples resulted in a decrease of all of the above-mentioned surface properties, due to the decrease of surface hydroxyl groups. This conclusion has been corroborated by FTIR. Values of E(T)(30), alpha(Surf), and pi*(Surf) are higher than those of water and alcohols; the BrOnsted and Lewis acidities of the samples correlate linearly. The advantages of using solvatochromic indicators to probe the surface properties and relevance of the results to the applications of TiO(2) are discussed.

Effects of alloying elements on the cytotoxic response of titanium alloys

Titanium alloys, alloys, especially beta-type alloys containing beta-stabilizing elements, constitute a highly versatile category of metallic materials that have been under constant development for application in orthopedics and dentistry. This type of alloy generally presents a high mechanical strength-to-weight ratio, excellent corrosion resistance and low elastic modulus. The purpose of this study is to evaluate the cytotoxicity and adhesion of fibroblast cells on titanium alloy substrates containing Nb, Ta, Zr, Cu, Sn and Mo alloying elements. Cells cultured on polystyrene were used as controls. In vitro results with Vero cells demonstrated that the tested materials, except Cu-based alloy, presented high viability in short-term testing. Adhesion of cells cultured on disks showed no differences between the materials and reference except for the Ti-Cu alloy, which showed reduced adhesion attributed to poor metabolic activity. Titanium alloys with the addition of Nb, Ta, Zr, Sn and Mo elements show a promising potential for biomedical applications. (C) 2011 Elsevier B.V. All rights reserved.

Relation between implant/abutment vertical misfit and torque loss of abutment screws

This study investigated whether there is a direct correlation between the level of vertical misfit at the abutment/implant interface and torque losses (detorque) in abutment screws. A work model was obtained from a metal matrix with five 3.75 x 9 mm external hex implants with standard platform (4.1 mm). Four frameworks were waxed using UCLA type abutments and one-piece cast in commercially pure titanium. The misfit was analyzed with a comparator microscope after 20 Ncm torque. The highest value of misfit observed per abutment was used. The torque required to loose the screw was evaluated using a digital torque meter. The torque loss values, measured by the torque meter, were assumed as percentage of initial torque (100%) given to abutment screws. Pearson's correlation (α=0.05) between the misfit values (29.08 ± 8.78 µm) and the percentage of detorque (50.71 ± 11.37%) showed no statistically significant correlation (p=0.295). Within the limitations of this study, it may be concluded that great vertical misfits dot not necessarily implies in higher detorque values.

Influence of Hero Apical instruments on cleaning ovoid-shaped root canals

The cleaning capacity of Hero 642 nickel-titanium files, complemented by the Hero Apical instruments in flattened roots, was determined by histological analysis, considering the area of action of the instruments on the coronal walls and the presence of remaining debris. Twenty-four single-canal, human mandibular incisors were divided into three groups and prepared as follows: GI, instrumented with Hero 642 NiTi files 30/.06, 25/.06, 20/.06, 25/.06, and 30/.06; GII, instrumented as GI followed by Hero Apical size 30/.06; GIII, instrumented as GI followed by Hero Apical sizes 30/.06 and 30/.08, then returning to 30/.06 with pendulum movements. The apical thirds were prepared for histological processing, analyzed at 40× magnification and the images were examined morphometrically. Statistical analysis showed that GIII presented the best results for removing debris (5.22% ± 4.13), with more contact between the instruments and the root canal walls (19.31% ± 0.15). This differed statistically from GI (14.04% ± 4.96 debris removal, with 42.96% ± 7.11 instrument contact) and GII (12.62% ± 5.76 debris removal, with 35.01% ± 0.15 instrument contact). Root canal preparation with Hero 642, complemented by Hero Apical instruments (30/.06 and 30/.08, then re-instrumented with Hero Apical 30/.06 using pendulum movements), was more efficient for debris removal and allowed more contact of the instruments with the root canal walls. GII presented the worst results.

Removal torque of zirconia abutment screws under dry and wet conditions

The aim of this study was to verify whether screw abutment lubrication can generate higher preload values compared to non-lubricated screws, a titanium abutment was screwed onto an implant analog and scanned with the Procera System to generate 20 zirconia abutments. MKIII Brånemark implants were clamped to a precision torque device, and the abutments were distributed in dry and wet groups with 10 specimens each. In the wet groups, the inner threads of the implants were filled with artificial saliva. All abutments were fastened with a Torqtite screw under 32 Ncm. Ten detorque measurements were performed per group pushing the reverse button of the Torque controller soon after screw tightening with values registered. The mean detorque values were calculated and compared by a Student's t test (?=0.05). The wet condition presented significantly higher mean detorque than the dry condition (31.5 ± 1.2 versus 27.5 ± 1.5 Ncm, respectively; p=0.0000024). In conclusion, there was always a loss in the initial torque values when the removal torque was measured under both conditions. The wet condition presented higher mean torque than the dry condition. Better preload values were established in the wet group, suggesting that the abutment screw must be lubricated in saliva to avoid further loosening.

Swine deep bedding ashes as a mineral additive for cement based mortar

The sustainability of intensive swine production demands alternative destinations for the generated residues. Ashes from swine rice husk-based deep bedding were tested as a mineral addition for cement mortars. The ashes were obtained at 400 to 600ºC, ground and sieved through a 325 mesh sieve (# 0.045 mm). The characterization of the ashes included the determination of the index of pozzolanic activity with lime. The ashes were also tested as partial substitutes of Portland cement. The mortars were prepared using a cement:sand proportion of 1:1.5, and with water/cement ratio of 0.4. Three percentages of mass substitution of the cement were tested: 10, 20 and 30%. Mortar performances were assessed at 7 and 28 days determining their compressive strength. The chosen condition for calcinations at the laboratory scale was related to the maximum temperature of 600ºC since the resulting ashes contained vitreous materials and presented satisfactory values for the pozzolanic index under analysis. The pozzolanic activity indicated promising results for ashes produced at 600ºC as a replacement of up to 30% in cement masses.

Synthesis of Fe/Ti oxides from a single source alkoxide precursor under inert atmosphere

The heterometal alkoxide [FeCl{Ti2(OPr i)9}] (1) was employed as a single source precursor for the preparation of Fe/Ti oxides under inert atmosphere. Three different synthetic procedures were adopted in the processing of 1, either employing aqueous HNO3 or HCl solutions, or in the absence of mineral acids. Products were characterised by powder X-ray diffractometry, scanning electron microscopy combined with energy dispersive X-ray spectroscopy (SEM/EDS) and Raman, electron paramagnetic resonance (EPR) and Mössbauer spectroscopies. Oxide products contained titanium(IV) and either iron(III) or iron(II), depending on reaction conditions and thermal treatment temperatures. An interesting iron(III)→iron(II) reduction was observed at 1000 ºC in the HNO3-containing system, leading to the detection of ilmenite (FeTiO3). SEM/EDS studies revealed a highly heterogeneous metal distribution in all products, possibly related to the presence of a significant content of carbon and of structural defects (oxygen vacancies) in the solids.

Ichthyoplankton distribution and abundance in the northern Todos os Santos and Camamu Bays, Bahia State - Brazil

The occurrence, distribution and abundance of ichthyoplankton in Todos os Santos and Camamu Bays were analyzed based on four samplings (winter 2003, summer 2003, winter 2004 and summer 2005). Samples were obtained by surface horizontal hauls, using a 200-µm mesh conical-cylinder plankton net. The distribution and abundance of eggs indicate a remarkable seasonal and annual variation of spawning activity in the region, especially when the two summer campaigns are compared. In summer 2003 the highest quantitative values were recorded, especially for Camamu, where the maximum reached 106.56 eggs.m-3, with an overall average of 43.46 eggs.m-3 for the two areas. In summer 2005 values were relatively low, the overall average being 3.49 eggs.m-3. The larval taxonomic composition is characterized by the predominance of gobiids, with small variation from summer to winter. Considering all the campaigns and samplings undertaken in both areas, larvae of 11 families were identified: Engraulidae, Clupeidae, Mugilidae, Atherinopsidae, Hemiramphidae, Syngnathidae, Blenniidae, Carangidae, Gobiidae, Achiridae and Tetraodontidae.

Obesidade na adolescência e seus principais fatores determinantes

O objetivo deste trabalho foi discutir os principais fatores ambientais determinantes do sobrepeso e da obesidade em adolescentes, fundamentando-se em uma revisão crítica sobre o assunto. Para a revisão do tema foram consultadas as principais bases de dados nacionais e internacionais, entre elas, Medline/Pubmed, Web of Science, SciELO, Lilacs, compreendendo o período de 1975 a 2009. Os descritores e termos MeSH utilizados na busca foram: "sobrepeso", "obesidade", "adolescência", "adolescentes", "atividade física", "ingestão alimentar". Os resultados das pesquisas indicam que as mudanças ocorridas nos padrões alimentares nas últimas décadas, como o aumento do consumo de açúcares simples, alimentos industrializados e ingestão insuficiente de frutas e hortaliças, estão diretamente associadas ao ganho de peso dos adolescentes. Além disso, a redução progressiva da prática de atividade física combinada ao maior tempo dedicado às atividades de baixa intensidade, como assistir televisão, usar computador e jogar videogame, também tem contribuído para o aumento de peso dos jovens. Conclui-se, portanto, que as variáveis relacionadas ao padrão alimentar e de atividade física devem ser priorizadas nas intervenções voltadas para a prevenção da obesidade entre adolescentes.

Estudo randômico da correção cirúrgica do prolapso uterino através de tela sintética de polipropileno tipo I comparando histerectomia versus preservação uterina

OBJETIVO: Comparar os resultados anatômicos pós-operatórios de pacientes portadoras de prolapso uterino tratadas utilizando tela de polipropileno para correção dos defeitos do assoalho pélvico, comparando histerectomia vaginal com a preservação do útero. MÉTODO: Estudo randomizado com 31 mulheres portadoras de prolapso uterino estádio III ou IV (POP-Q) divididas em dois grupos: Grupo HV- 15 mulheres submetidas à histerectomia vaginal e reconstrução da anatomia do assoalho pélvico com tela de polipropileno tipo I (Nazca R-Promedon) e Grupo HP- 16 mulheres mulheres submetidas à reconstrução da anatomia do assoalho pélvico com tela de polipropileno tipo I (Nazca R-Promedon) preservando o útero. Raça, urgência miccional, constipação intestinal, dor sacral, sangramento e tempo de operação foram os parâmetros analisados. RESULTADOS: O tempo de seguimento médio foi de nove meses. Não se observou diferença entre os grupos nas complicações funcionais. O tempo cirúrgico foi 120 minutos para grupo HV versus 58.9 minutos para grupo HP ( p < 0.001 ) e o volume de perda sanguínea intraoperatória foi 120 mL no grupo HV versus 20 mL para grupo HP ( p < 0.001*). A taxa de sucesso objetivo foi 86.67% para grupo HV e 75% para grupo HP (p = 0,667). A taxa de erosão de tela foi 20% (3/15) de extrusão no grupo HV versus 18,75% (3/16) no grupo HP (p = 1,000). CONCLUSÃO: A correção cirúrgica do assoalho pélvico com telas nas portadoras de prolapso uterino apresentaram similaridade quer sendo ela feita com histeropexia quer com histerectomia. Contudo, o tempo cirúrgico e o volume da perda sanguínea foram significantemente maiores no grupo com histerectromia (HV). Operações vaginais com telas são procedimentos efetivos para a correção do prolapso.

Qualidade de luz na biometria e anatomia foliar de plântulas de Cattleya loddigesii L. (Orchidaceae) micropropagadas

A qualidade de luz pode alterar a morfogênese das plantas por meio de uma série de processos mediados por receptores de luz, principalmente na região do vermelho e azul. O objetivo do presente estudo foi verificar alterações anatômicas foliares e características biométricas de Cattleya loddigesii 'Tipo', cultivadas in vitro, sob diferentes malhas coloridas com nível de radiação de 50% de sombreamento. Plântulas oriundas de autopolinização e sementes germinadas in vitro, com aproximadamente 1,0cm de comprimento e com raízes, foram inoculadas em meio WPM e submetidas a diferentes condições de incubação. Testou-se o efeito de sombrites coloridos (vermelho e azul) sobre os frascos cultivados em casa de vegetação (CV) e sala de crescimento (SC), além dos tratamentos, nos dois ambientes, sem utilização das telas coloridas. A avaliação foi efetuada 180 dias após inoculação. Com os resultados obtidos, observou-se que o ambiente de cultivo promove alterações anatômicas e biométricas em plântulas de Cattleya loddigesii 'Tipo' micropropagadas. As alterações promovidas pelo cultivo em luz natural evidenciam maior capacidade fotossintética, por meio de maior diferenciação dos tecidos clorofilianos, promovendo uma superfície foliar anatomicamente adaptada à fase de aclimatização.

Evaluation of Ti(3)Si Phase Stability from Heat-Treated, Rapidly Solidified Ti-Si Alloys

Ti-base alloys containing significant amounts of silicon have been considered for high temperature structural applications. Thus, information concerning phase stability on the Ti-Si system is fundamental and there are not many investigations covering the phase stability of the Ti(3)Si phase, specially its dependence on oxygen/nitrogen contamination. In this work the stability of this phase has been evaluated through heat-treatment of rapidly solidified Ti-rich Ti-Si alloys at 700 A degrees C and 1000 A degrees C. The rapidly solidified splats presented nanometric scale microstructures which facilitated the attainment of equilibrium conditions. The destabilization of Ti(3)Si due to oxygen/nitrogen contamination has been noted.