Influence of the Additional Er:YAG Laser Conditioning Step on the Microleakage of Class V Restorations

The purpose of this study was to evaluate the influence of an additional Er:YAG laser conditioning step after laser cavity preparations, on the microleakage of class V composite restorations. Forty-eight bovine incisors were randomly divided into four groups: G1(control) cavities prepared with bur, G2- cavities prepared with laser (400 mJ/2 Hz), G3-cavities prepared and subsequently conditioned with Er:YAG laser (60 mJ/2 Hz); G4-idem for G3, but the laser conditioning was carried out without water-spray. All the cavities were restored using Clearfill SE Bond (R) and Z-250 (R) composite resin. The samples were thermal cycled for 700 cycles and then immersed in 50% silver nitrate solution. The sectioned restorations were exposed to a photoflood lamp to reveal silver nitrate penetration. The Kruskal-Walis one-way analyses of variance test and post hoc Wilcoxon pair-wise comparison were used to compare microleakage degrees. At the gingival margin G2 showed a lower microleakage mean than the control bur-prepared cavities (p = 0.0003). At occlusal margins there were no statistically significant differences between the groups (p = 0.28). It may be concluded that Er:YAG laser class V cavity preparations do not need to be followed by an additional laser conditioning step to result in levels of microleakage similar to or lower than those obtained after bur preparations. (C) 2008 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater 87B: 538-543, 2008

One-year stability of resin-dentin bonds created with a hydrophobic ethanol-wet bonding technique

Dentin bonding performed with hydrophobic resins using ethanol-wet bonding should be less susceptible to degradation but this hypothesis has never been validated. Objectives. This in vitro study evaluated stability of resin-dentin bonds created with an experimental three-step BisGMA/TEGDMA hydrophobic adhesive or a three-step hydrophilic adhesive after one year of accelerated aging in artificial saliva. Methods. Flat surfaces in mid-coronal dentin were obtained from 45 sound human molars and randomly divided into three groups (n = 15): an experimental three-step BisGMA/TEGDMA hydrophobic adhesive applied to ethanol (ethanol-wet bonding-GI) or water-saturated dentin (water-wet bonding-GII) and Adper Scotchbond Multi-Purpose [MP-GIII] applied, according to manufacturer instructions, to water-saturated dentin. Resin composite crowns were incrementally formed and light-cured to approximately 5 mm in height. Bonded specimens were stored in artificial saliva at 37 degrees C for 24h and sectioned into sticks. They were subjected to microtensile bond test and TEM analysis immediately and after one year. Data were analyzed with two-way ANOVA and Tukey tests. Results. MP exhibited significant reduction in microtensile bond strength after aging (24 h: 40.6 +/- 2.5(a); one year: 27.5 +/- 3.3(b); in MPa). Hybrid layer degradation was evident in all specimens examined by TEM. The hydrophobic adhesive with ethanol-wet bonding preserved bond strength (24 h: 43.7 +/- 7.4(a); one year: 39.8 +/- 2.7(a)) and hybrid layer integrity, with the latter demonstrating intact collagen fibrils and wide interfibrillar spaces. Significance. Coaxing hydrophobic resins into acid-etched dentin using ethanol-wet bonding preserves resin-dentin bond integrity without the adjunctive use of MMPs inhibitors and warrants further biocompatibility and patient safety`s studies and clinical testing. (C) 2009 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.