Effect of Calcium Pre-rinse and Fluoride Dentifrice on Enamel and on Dental Plaque Formed In Situ

Purpose: The aim of this in situ double-blind randomised crossover study was to investigate the effect of calcium (Ca) pre-rinse on the composition of plaque and on enamel prior to the use of fluoride (F) dentifrice. Materials and Methods: During four phases (14 days each) of this study, 10 volunteers had agreed to wear dental appliances containing two healthy bovine enamel blocks. A fresh solution containing 20% weight/volume (w/v) sucrose was dripped on the enamel blocks ex vivo for 5 min three times a day. Subsequently, the appliances were replaced in the mouth, and the volunteers rinsed their mouth with 10 mL of a Ca (150 mmol/L) or a placebo rinse (1 min). In sequence, a slurry (1:3 w/v) of F (1030 ppm) or placebo dentifrice was dripped onto the blocks ex vivo for 1 min. During this time, the volunteers brushed their teeth with the respective dentifrice. The appliances were replaced in the mouth, and the volunteers rinsed their mouth with water. The plaque formed on the blocks was analysed for F and Ca. The enamel demineralisation as well as the incorporation of F on enamel was evaluated by cross-sectional microhardness and alkali-soluble F analysis, respectively. Data were tested using analysis of variance (P < 0.05). Results: The Ca pre-rinse prior to the use of the F dentifrice led to a three- and sixfold increase in the plaque F and Ca concentrations, respectively. It also did not have any additive effect on the F content on the enamel and the demineralisation of the enamel, in comparison with the use of F dentifrice alone. Conclusions: A Ca lactate rinse used prior to the F dentifrice was able to change the mineral content in the plaque, but it was unable to prevent enamel demineralisation.

A simple and sensitive detection of diquat herbicide using a dental amalgam electrode A comparison using the chromatographic technique

This paper describes the use of a dental amalgam electrode (DAE) to evaluate the electrochemical behaviour and to develop an electroanalytical procedure for determination of diquat herbicide in natural water and potato samples. The work was based on the square wave voltammetry responses of diquat, which presented two well-defined and reversible reduction peaks, at -0.56 V (peak 1) and -1.00V (peak 2). The experimental and voltammetric parameters were optimised, and the analytical curves were constructed and compared to similar curves performed by high performance liquid chromatography coupled to ultraviolet-visible spectrophotometric detector (HPLC/UV-vis). The responses were directly proportional to diquat concentration in a large interval of concentration, and the calculated detection limits were very similar, around 10 mu g L(-1) (10 ppb) for voltammetric and chromatographic experiments. These values were lower than the maximum residue limit established for natural water by the Brazilian Environmental Agency. The recovery percentages in pure electrolyte, natural water and potato samples showed values from 70% to 130%, demonstrating that the voltammetric methodology proposed is suitable for determining any contamination by diquat in different samples, minimising the toxic residues due to the use of liquid mercury or the adsorptive process relative to use of other solid surfaces. (C) 2009 Published by Elsevier B.V.

Evaluation of the light polymerization efficiency of copolymers used in dental formulations by differential scanning calorimetry

Different compositions of visible-light-curable triethylene glycol dimethacrylate/bisglycidyl methacrylate copolymers used in dental resin formulations were prepared through copolymerization photoinitiated by a camphorquinone/ethyl 4-dimethylaminobenzoate system irradiated with an Ultrablue IS light-emitting diode. The obtained copolymers were evaluated with differential scanning calorimetry. From the data for the heat of polymerization, before and after light exposure, obtained from exothermic differential scanning calorimetry curves, the light polymerization efficiency or degree of conversion of double bonds was calculated. The glass-transition temperature also was determined before and after photopolymerization. After the photopolymerization, the glass-transi-tion temperature was not well defined because of the breadth of the transition region associated with the properties of the photocured dimethacrylate. The glass-transition temperature after photopolymerization was determined experimentally and compared with the values determined with the Fox equation. In all mixtures, the experimental value was lower than the calculated value. Scanning electron microscopy was used to analyze the morphological differences in the prepared copolymer structures. (C) 2007 Wiley Periodicals, Inc.

Evaluation of Postpolymerization as a Function of the Storage Time of Triethylene Glycol Dimethacrylate/2,2-Bis[4-(2-Hydroxy-3-Methacryloxy-Prop-1-Oxy)-Phenyl]-propane Bisphenyl-alpha-Glycidyl Ether Dimethacrylate Copolymers Used in Dental Resins by Differential Scanning Calorimetry and Dynamic Mechanical Analysis

The aim of this work was to evaluate the effect of the storage time on the thermal properties of triethylene glycol dimethacrylate/2,2-bis[4-(2-hydroxy-3-methacryloxy-prop-1-oxy)-phenyl]propane bisphenyl-alpha-glycidyl ether dimethacrylate (TB) copolymers used in formulations of dental resins after photopolymerization. The TB copolymers were prepared by photopolymerization with an Ultrablue IS light-emitting diode, stored in the dark for 160 days at 37 degrees C, and characterized with differential scanning calorimetry (DSC), dynamic mechanical analysis (DMA), and Fourier transform infrared spectroscopy with attenuated total reflection. DSC curves indicated the presence of an exothermic peak, confirming that the reaction was not completed during the photopolymerization process. This exothermic peak became smaller as a function of the storage time and was shifted at higher temperatures. In DMA studies, a plot of the loss tangent versus the temperature initially showed the presence of two well-defined peaks. The presence of both peaks confirmed the presence of residual monomers that were not converted during the photopolymerization process. (C) 2009 Wiley Periodicals, Inc. J Appl Polym Sci 112: 679-684, 2009