First-order-reversal-curve analysis of Pr-Fe-B-based nanocomposites

Ribbons of nominal composition (Pr(9.5)Fe(84.5)B(6))(0.96)Cr(0.01)(TiC)(0.03) were produced by arc-melting and melt-spinning the alloys on a Cu wheel. X-ray diffraction reveals two main phases, one based upon alpha-Fe and the other upon Pr(2)Fe(14)B. The ribbons show exchange spring behavior with H(c)=12.5 kOe and (BH)(max)= 13.6 MGOe when these two phases are well coupled. Transmission electron microscopy revealed that the coupled behavior is observed when the microstructure consists predominantly of alpha-Fe grains(diameter similar to 100 nm.) surrounded by hard material containing Pr(2)Fe(14)B. A first-order-reversal-curve (FORC) analysis was performed for both a well-coupled sample and a partially-coupled sample. The FORC diagrams show two strong peaks for both the partially-coupled sample and for the well coupled material. In both cases, the localization of the FORC probability suggests demagnetizing interactions between particles. Switching field distributions were calculated and are consistent with the sample microstructure. (C) 2009 Elsevier B.V. All rights reserved.

Influence of calcination temperature on the morphology and magnetic properties of Ni-Zn ferrite applied as an electromagnetic energy absorber

An evaluation was made of the influence of calcination temperatures on the structure, morphology and eletromagnetic properties of Ni-Zn ferrite powders. To this end, Ni(0.5)Zn(0.5)Fe(2)O(4) ferrite powders were prepared by combustion reaction and calcined at temperatures of 800, 1000 and 1200 degrees C/2 h. The resulting powders were characterized by XRD, SEM and reflectivity measurements in the frequency bands of 8-12 GHz. The results demonstrated that raising the calcination temperature increased the particle sizes of the powders of all the systems in question, improving the reflectivity of the materials. (C) 2008 Elsevier B.V. All rights reserved.

Structural and magnetic properties of chromium-doped ferrite nanopowders

This paper reports on a study of Cr(3+)-doped nanosized Ni-Zn ferrites produced by combustion reaction, and evaluates their morphological and magnetic properties. The powders were characterized by X-ray diffraction (XRD) and SEM and magnetic properties. All the compositions showed the formation of the inverse spinel phase of Ni-Zn ferrite. The average crystallite size ranged from 21 to 26 nm. The saturation magnetization was found to be in the range of 53-43 emu/g. The increase in Cr(3+) concentration in the Ni-Zn ferrite caused a reduction in hysteresis losses and a slight reduction in the saturation magnetization. (C) 2008 Elsevier B.V. All rights reserved.

Single-step chemical synthesis of ferrite hollow nanospheres

We report a single-step chemical synthesis of iron oxide hollow nanospheres with 9.3 nm in diameter. The sample presents a narrow particle diameter distribution and chemical homogeneity. The hollow nature of the particles is confirmed by HRTEM and HAADF STEM analysis. Electron and x-ray diffraction show that the outer material component is constituted by 2 nm ferrite crystals. Mossbauer data provide further evidence for the formation of iron oxide with high structural disorder, magnetically ordered at 4.2 K and superparamagnetism at room temperature. An unusual magnetic behavior under an applied field is reported, which can be explained by the large fraction of atoms existing at both inner and outer surfaces.