Short-range structure of Pb(1-x)Ba(x)Zr(0.65)Ti(0.35)O(3) ceramic compounds probed by XAS and Raman scattering techniques

Ti K-edge x-ray absorption near-edge spectroscopy (XANES) and Raman scattering were used to study the solid solution effects on the structural and vibrational properties of Pb(1-x)Ba(x)Zr(0.65)Ti(0.35)O(3) with 0.0 < x < 0.40. Compared with x-ray diffraction techniques, which indicates that the average crystal symmetry changes with the substitution of Pb by Ba ions or with temperature variations for samples with x=0.00, 0.10, and 0.20, local structural probes such as XANES and Raman scattering results demonstrate that at local level, the symmetry changes are much less prominent. Theoretical XANES spectra calculation corroborate with the interpretation of the XANES experimental data.

Structural and magnetic properties of the oxyborate Co(5)Ti(O(2)BO(3))(2)

We present an extensive study of the oxyborate material Co(5)Ti(O(2)BO(3))(2) using x-ray, magnetic, and thermodynamic measurements. This material belongs to a family of oxyborates known as ludwigites which presents low-dimensional subunits in the form of three leg ladders in its structure. Differently from previously investigated ludwigites the present material does not show long-range magnetic order although it goes into a spin-glass state at low temperatures. The different techniques employed in this paper allow for a characterization of the structure, the nature of the low-energy excitations and the magnetic anisotropy of this system. Its unique magnetic behavior is discussed and compared with those of other magnetic ludwigites.

Nanogravimetric and voltammetric studies of a Pt-Rh alloy surface and its behavior for methanol oxidation

This paper describes the preparation of a Pt-Rh alloy surface electrodeposited on Pt electrodes and its electrocatalytic characterization for methanol oxidation. The X-ray photoelectronic spectroscopy ( XPS) results demonstrate that the surface composition is approximately 24 at-% Rh and 76 % Pt. The cyclic voltammetry (CV) and electrochemical quartz crystal (EQCN) results for the alloy were associated, for platinum, to the well known profile in acidic medium. For Rh, on the alloy, the generation of rhodium hydroxide species (Rh(OH)(3) and RhO(OH)(3)) was measured. During the successive oxidation-reduction cycles the mass returns to its original value, indicating the reversibility of the processes. It was not observed rhodium dissolution during the cycling. The 76/24 at % Pt-Rh alloy presented singular electrocatalytic activity for methanol electrooxidation, which started at more negative potentials compared to pure Pt (70 mV). During the sweep towards more negative potentials, there is only weak CO re-adsorption on both Rh and Pt-Rh alloy surfaces, which can be explained by considering the interaction energy between Rh and CO.

Superconducting current path and flux line shape in NbTiTa obtained by inter-diffusion process

This investigation presents a comprehensive characterization of magnetic and transport properties of an interesting superconducting wire, Nb-Ti -Ta, obtained through the solid-state diffusion between Nb-12 at.% Ta alloy and pure Ti. The physical properties obtained from magnetic and transport measurements related to the microstructure unambiguously confirmed a previous proposition that the superconducting currents flow in the center of the diffusion layer, which has a steep composition variation. The determination of the critical field also confirmed that the flux line core size is not constant, and in addition it was possible to determine that, in the center of the layer, the flux line core is smaller than at the borders. A possible core shape design is proposed. Among the wires studied, the one that presented the best critical current density was achieved for a diffusion layer with a composition of about Nb-32% Ti-10% Ta, obtained with a heat treatment at 700 degrees C during 120 h, in agreement with previous studies. It was determined that this wire has the higher upper critical field, indicating that the optimization of the superconducting behavior is related to an intrinsic property of the ternary alloy.

Thermal expansion of the V(5)Si(3) and T(2) phases of the V-Si-B system investigated by high-temperature X-ray diffraction

The thermal expansion anisotropy of the V(5)Si(3) and T(2)-phase of the V-Si-B system were determined by high-temperature X-ray diffraction from 298 to 1273 K. Alloys with nominal compositions V(62.5)Si(37.5) (V5Si3 phase) and V(63)Si(12)B(25) (T(2)-phase) were prepared from high-purity materials through arc-melting followed by heat-treatment at 1873 K by 24 h, under argon atmosphere. The V(5)Si(3) phase exhibits thermal expansion anisotropy equals to 1.3, with thermal expansion coefficients along the a and c-axis equal to 9.3 x 10(-6) K(-1) and 11.7 x 10(-6) K(-1), respectively. Similarly, the thermal expansion anisotropy value of the T(2)-phase is 0.9 with thermal expansion coefficients equal to 8.8 x 10(-6) K(-1) and 8.3 x 10(-6) K(-1) along the, a and c-axis respectively. Compared to other isostructural silicides of the 5:3 type and the Ti(5)Si(3) phase, the V(5)Si(3) phase presents lower thermal expansion anisotropy. The T(2)-phase present in the V-Si-B system exhibits low thermal expansion anisotropy, as the T(2)-phase of the Mo-Si-B, Nb-Si-B and W-Si-B systems. (C) 2009 Elsevier Ltd. All rights reserved.

Near zero magnetostriction of Fe-Ti alloys

Fe(100-x)Ti(x) alloys (x = 10, 15, 20) were studied with respect to their microstructure and magnetostriction. Depending on heat treatment temperature and composition, the sample retained either the alpha-phase (A2 structure) or the alpha-phase plus the TiFe(2) Laves phase (C14 structure). The saturation magnetostriction measured at 238K is negative, about -11 ppm. However, for fields up to 0.4 T the magnetostriction is barely zero, a very interesting result. High values of magnetostriction are of interest for applications mainly in sensors and actuators, but zero magnetostriction is also a remarkable property, desirable for many applications such as electric transformers and fluxgate sensor cores. Therefore, the Fe(100-x)Ti(x) (x < 20 at%) are an attractive option to be considered for these applications.

Magnetostriction of Fe-Ti Alloys

Longitudinal and transverse magnetostriction measurements were performed on polycrystalline Fe(100-x)Ti(x) alloys, for a large Ti concentration range, from x = 8.8 to 34.7 at.%. Our results showed that substituting Fe by Ti does not significantly enhance the magnetostriction. For all Ti concentrations in the magnetically saturated state, the longitudinal magnetostriction values vary from -2 x 10(-6) to 6 x 10(-6). On the other hand, Fe(100-x)Ti(x) alloys exhibit a large forced volume magnetostriction, which increases with increasing Ti-concentration. The magnetostriction behavior could be explained considering investigations of the hyteresis loops and the microstructure.

Equivalence between hot tensile and creep testing data for Kanthal A1 alloy

Hot tensile and creep tests were carried out on Kanthal A1 alloy in the temperature range from 600 to 800 degrees C. Each of these sets of data were analyzed separately according to their own methodologies, but an attempt was made to find a correlation between them. A new criterion proposed for converting hot tensile data to creep data, makes possible the analysis of the two kinds of results according to usual creep relations like: Norton, Monkman-Grant, Larson-Miller and others. The remarkable compatibility verified between both sets of data by this procedure strongly suggests that hot tensile data can be converted to creep data and vice-versa for Kanthal A1 alloy, as verified previously for other metallic materials.

Dynamic behavior analysis of drill-threading process when machining AISI Al-Si-Cu(4) alloy

Conventional threading operations involve two distinct machining processes: drilling and threading. Therefore, it is time consuming for the tools must be changed and the workpiece has to be moved to another machine. This paper presents an analysis of the combined process (drilling followed by threading) using a single tool for both operations: the tap-milling tool. Before presenting the methodology used to evaluate this hybrid tool, the ODS (operating deflection shapes) basics is shortly described. ODS and finite element modeling (FEM) were used during this research to optimize the process aiming to achieve higher stable machining conditions and increasing the tool life. Both methods allowed the determination of the natural frequencies and displacements of the machining center and optimize the workpiece fixture system. The results showed that there is an excellent correlation between the dynamic stability of the machining center-tool holder and the tool life, avoiding a tool premature catastrophic failure. Nevertheless, evidence showed that the tool is very sensitive to work conditions. Undoubtedly, the use of ODS and FEM eliminate empiric decisions concerning the optimization of machining conditions and increase drastically the tool life. After the ODS and FEM studies, it was possible to optimize the process and work material fixture system and machine more than 30,000 threaded holes without reaching the tool life limit and catastrophic fail.

Design and Characterization of Novel Wear Resistant Multilayer CVD Coatings with Improved Adhesion Between Al(2)O(3) and Ti(C,N)

Multilayer CVD coatings for high speed cutting applications were designed to achieve high wear and heat resistance during machining of steel alloys. In this work the microstructure and cutting performance of these novel multilayer CVD coatings are investigated and compared with standard CVD multilayer coatings. 3D-FIB tomography is used to characterize the microstructure of the layers, especially the transition between the Ti(C,N) and the Al(2)O(3) layer. The 3D reconstruction of the surface of the Ti(C,N) layer shows the formation of protruded Ti(C,N) grains with a very particular architecture, which penetrate into the Al(2)O(3) top-layer, providing a mechanical anchoring between both layers. Cemented carbides coated with the novel CVD multilayer present reduced crater and flank wear as well as improved adherence between the Al(2)O(3) top-layer and the Ti(C,N) layer leading to a dramatic improvement of cutting performance.

Topological instability, average electronegativity difference and glass forming ability of amorphous alloys

In this paper, we report the remarkable agreement of the glass forming ability of binary alloys with a new criterion that combines the topological instability parameter (lambda) and the average electronegativity difference among the elements of an alloy, assuming both exert a synergetic effect. The best glass forming compositions for Zr-Cu and Ti-Ni systems are well predicted by this new approach. Although the new criterion needs further refinement, it is concluded that the proposed approach is a promising and simple tool to guide and reduce the tedious and labour intensive work to find good glass former compositions in metallic systems. (C) 2008 Elsevier Ltd. All rights reserved.

Fatigue behaviour of friction stir welded AA2024-T3 alloy: longitudinal and transverse crack growth

The fatigue crack growth properties of friction stir welded joints of 2024-T3 aluminium alloy have been studied under constant load amplitude (increasing-Delta K), with special emphasis on the residual stress (inverse weight function) effects on longitudinal and transverse crack growth rate predictions (Glinka`s method). In general, welded joints were more resistant to longitudinally growing fatigue cracks than the parent material at threshold Delta K values, when beneficial thermal residual stresses decelerated crack growth rate, while the opposite behaviour was observed next to K-C instability, basically due to monotonic fracture modes intercepting fatigue crack growth in weld microstructures. As a result, fatigue crack growth rate (FCGR) predictions were conservative at lower propagation rates and non-conservative for faster cracks. Regarding transverse cracks, intense compressive residual stresses rendered welded plates more fatigue resistant than neat parent plate. However, once the crack tip entered the more brittle weld region substantial acceleration of FCGR occurred due to operative monotonic tensile modes of fracture, leading to non-conservative crack growth rate predictions next to K-C instability. At threshold Delta K values non-conservative predictions values resulted from residual stress relaxation. Improvements on predicted FCGR values were strongly dependent on how the progressive plastic relaxation of the residual stress field was considered.

Thixocasting of an A356 alloy: Fluidity, porosity distribution and thermomechanical fatigue behavior

An extensive set of experiments was performed on a semi-solid A356 alloy in order to assess its flow behavior, mechanical properties, microstructural evolution and porosity level. Three different microstructural conditioning techniques (raw material preparation) were employed: deformation recrystallization, magnetohydrodynamic stirring and low temperature pouring. Measurement of microstructural parameters such as Al-alpha particle size, shape factor, contiguity and entrapped liquid showed a relative equivalency among the various conditioning techniques. It was found that the strongest influence on semi-solid slurry fluidity is exerted by the mould temperature. Tensile properties and porosity levels were measured on a demonstration part produced with different slurry ingate velocities. Results showed similar strength levels among all thixocast samples, a strong correlation between elongation and pore volume fraction and porosity levels much lower than the typical figure for permanent mould or die cast Al-Si alloys. Finally, thermomechanical fatigue tests results were much more favorable to the semi-solid material when compared with the conventionally cast alloy, a result attributed to lower porosity, spheroidal shape of the Al-alpha phase, and refined Si eutectic particles. alpha 2007 Elsevier B.V. All rights reserved.

Selective corrosion of 550 degrees C aged Cu10Ni-3Al-1.3Fe alloy in NaCl aqueous solution

This work studied the electrochemical behavior of a solution treated or 550 degrees C aged Cu10Ni-3Al-1.3Fe alloy, in 0.01 M NaCl aqueous solution, through potentiodynamic polarization in both stagnant condition or under erosion process. Results showed the occurrence of a passivity break potential (E(pb)), related to the beginning of the denickelification process, which occurred as a localized attack under stagnant electrolyte. Under erosion conditions localized denickelification was not observed, despite of the presence of E(pb). This could indicate that selective corrosion of Ni, which caused the observed E(pb), occurred as a dissolution-redeposition process, with removal of the Cu deposits during erosion process. (C) 2011 Elsevier Ltd. All rights reserved.

Microstructure and texture assessment of Al-Mn-Fe-Si (3003) aluminum alloy produced by continuous and semicontinuous casting processes

Aluminum sheets are currently produced by the direct-chill process (DC). The need for low-cost aluminum sheets is a challenge for the development of new materials produced by the twin roll caster (TRC) process. It is expected that sheets produced from these different casting procedures will differ in their microstructure. These differences in microstructure and in the crystallographic texture have great impact on sheet mechanical properties and formability. The present study investigated microstructure and evaluated texture of two strips of Al-Mn-Fe-Si (3003) aluminum alloy produced by TRC and by hot-rolling processes. It was possible to notice that the microstructure, morphology, and grain size of the TRC sample were more homogenous than those found in hot-rolled samples. Both strips, obtained by the two processes, showed strong texture gradient across the thickness.