Selective corrosion of 550 degrees C aged Cu10Ni-3Al-1.3Fe alloy in NaCl aqueous solution

This work studied the electrochemical behavior of a solution treated or 550 degrees C aged Cu10Ni-3Al-1.3Fe alloy, in 0.01 M NaCl aqueous solution, through potentiodynamic polarization in both stagnant condition or under erosion process. Results showed the occurrence of a passivity break potential (E(pb)), related to the beginning of the denickelification process, which occurred as a localized attack under stagnant electrolyte. Under erosion conditions localized denickelification was not observed, despite of the presence of E(pb). This could indicate that selective corrosion of Ni, which caused the observed E(pb), occurred as a dissolution-redeposition process, with removal of the Cu deposits during erosion process. (C) 2011 Elsevier Ltd. All rights reserved.

Magnetic losses evolution of a semi-processed steel during forced aging treatments

An ultra-low carbon steel (30 ppm after decarburization) containing Al and Si was aged for distinct soaking times at 210 degrees C. The core loss increased continuously until around 24 h. After that, only slight changes were verified. It was found that only the hysteresis loss component changed during the aging treatment. By internal friction test and transmission electron microscopy it was seen that carbon precipitation caused the magnetic aging. By scanning electron microscopy it could be concluded that the increase of aging index was attributed to the high number of carbides larger than 0.1 mu m. (C) 2008 Elsevier B. V. All rights reserved.

Degradation of Poly(ethylene glycol) in Aqueous Solution by Photo-Fenton and H(2)O(2)/UV Processes

This article reports experimental results obtained in a laboratory-scale photochemical reactor on the photodegradation of poly(ethylene glycol) (PEG) in aqueous solutions by means of the photo-Fenton and H(2)O(2)/UV processes. Dilute water solutions of PEG were fed to a batch reactor, mixed with pertinent reactants, and allowed to react under different conditions. Reaction progress was evaluated by sampling and analyzing the concentration of the total organic carbon (TOC) in solution as a function of the reaction time. Organic acids formed during oxidation were determined by HPLC analyses. The main acids detected in both processes were acetic and formic. Glycolic acid was detected only in the photo-Fenton process, and malonic acid was detected only in the H(2)O(2)/UV treatment, indicating that different reaction paths occur in these processes. The characteristics of both processes are discussed, based on the evolution of the TOC-time curves and the concentration profiles of the monitored organic acids. The experimental results constitute a contribution to the design of industrial processes for the treatment of wastewaters containing soluble polymers with similar properties.

Coalescence of Water Droplets in Crude Oil Emulsions: Analytical Solution

In petroleum refineries, water is used in desalting units to remove the salt contained in crude oil. Typically, 7% of the volume of hot crude oil is water, forming a water-and-oil emulsion. The emulsion flows between two electrodes and is subjected to an electric field. The electrical forces promote the coalescence of small droplets of water dispersed in crude oil, and these form bigger droplets. This paper calculates the forces acting on the droplets, highlighting particularly the mechanisms proposed for droplet-droplet coalescence under the influence of an applied electric field. Moreover, a model is developed in order to calculate the displacement speed of the droplets and the time between droplet collisions. Thus, it is possible to simulate and optimize the process by changing the operational variables (temperature, electrical field, and water quantity). The main advantage of this study is to show that it is feasible to increase the volume of water recycled in desalting processes, thus reducing the use of freshwater and the generation of liquid effluents in refineries.

QUALITY EVALUATION OF MINIMALLY PROCESSED `REGIS` PEACH

The aim of this work was evaluate the effect of citric acid at 1% and 2% in the maintenance of the quality of minimally processed `Regis` peaches, during 9 days storage under refrigeration (5+/-1 degrees C, 85-87% RU) and passive modified atmospheres. The following analyses were realized: color, firmness, texture, soluble solids, titratable acidity, pH, CO(2) and O(2). Increasing in a value and decreasing in b and L values on minimally processed peaches were observed, independent of the citric acid treatment, indicating a browning on the product mainly on the 9(th) day of storage. Overall, the levels of titratable acidity and pH changed at the storage period and at the concentrations studied, unlike the content of soluble solids that remained unchanged. The texture, CO(2) and O(2) changed only for the storage period unlike texture that was higher with the treatment of citric acid 2%. It can be concluded that neither tested concentration of citric acid was effective in preventing enzymatic browning of minimally processed peaches stored the 5+/-1 degrees C and 85-87% RU and passive modified atmosphere.

New Analytic Solution Related to the Richards, Philip, and Green-Ampt Equations for Infiltration

Based on physical laws of similarity, an analytic solution of the soil water potential form of the Richards equation was derived for water infiltration into a homogeneous sand. The derivation assumes a similarity between the soil water retention function and that of the soil water content profiles taken at fixed times. The new solution successfully described soil water content profiles experimentally measured for water infiltrating downward, upward, and horizontally into a homogeneous sand and agrees with that presented by Philip in 1957. The utility of this analysis is still to be verified, but it is expected to hold for soils that have a narrow pore-size distribution before wetting and that manifest a sharp increase of water content at the wetting front during infiltration. The effect of van Genuchten`s parameters alpha and n on the application of the solution to other porous media was investigated. The solution also improves and provides a more realistic description of the infiltration process than that pioneered by Green and Ampt in 1911.

New Analytic Solution of Boltzmann Transform for Horizontal Water Infiltration into Sand

The use of the Boltzmann transform function, lambda(theta), to solve the Richards equation when the diffusivity, D, is a function of only soil water content,., is now commonplace in the literature. Nevertheless, a new analytic solution of the Boltzmann transform lambda(h) as a function of matric potential for horizontal water infiltration into a sand was derived without invoking the concept or use of D(theta). The derivation assumes that a similarity exists between the soil water retention function and the Boltzmann transform lambda(theta). The solution successfully described soil water content profiles experimentally measured for different infiltration times into a homogeneous sand and agrees with those presented by Philip in 1955 and 1957. The applicability of this solution for all soils remains open, but it is anticipated to hold for soils whose air-filled pore-size distribution before wetting is sufficiently narrow to yield a sharp increase of water content at the wetting front during infiltration. It also improves and provides a versatile alternative to the well-known analysis pioneered by Green and Ampt in 1911.

Distribution and storage characterization of soil solution for drip irrigation

The increased use of marginal quality water with drip irrigation requires sound fertigation practices that reconcile environmental concerns with viable crop production objectives. We conducted experiments to characterize dynamics and patterns of soil solution within wet bulb formed by drip irrigation. Time-domain reflectometry probes were used to monitor the distribution of potassium nitrate (KNO(3)) and water distribution from drippers discharging at constant flow rates of 2, 4 and 8 L h(-1) in soil-filled containers. Considering results from different profiles, we observed greater solute storage near the dripper decreasing gradually towards the wetting front. About half of the applied KNO(3) solution (48%) was stored in the first layer (0-0.10 m) for all experiments, 29% was stored in the next layer (0.10-0.20 m). Comparing different dripper flow rates, we observed higher solution storage for 4 L h(-1), with 45, 53 and 47% of applied KNO(3) solution accumulating in the first layer (0-0.10 m) for dripper flow rates of 2, 4 and 8 L h(-1), respectively. The results suggest that based on the volume and frequency used in this experiment, it would be advantageous to apply small amounts of solution at more frequent intervals to reduce deep percolation losses of applied water and solutes.

Nickel adsorption in two Oxisols and an Alfisol as affected by pH, nature of the electrolyte, and ionic strength of soil solution

Background, aim, and scope The retention of potentially toxic metals in highly weathered soils can follow different pathways that variably affect their mobility and availability in the soil-water-plant system. This study aimed to evaluate the effects of pH, nature of electrolyte, and ionic strength of the solution on nickel (Ni) adsorption by two acric Oxisols and a less weathered Alfisol. Materials and methods The effect of pH on Ni adsorption was evaluated in surface and subsurface samples from a clayey textured Anionic `Rhodic` Acrudox ( RA), a sandy-clayey textured Anionic `Xantic` Acrudox (XA), and a heavy clayey textured Rhodic Kandiudalf (RK). All soil samples were equilibrated with the same concentration of Ni solution (5.0 mg L(-1)) and two electrolyte solutions (CaCl(2) or NaCl) with different ionic strengths (IS) (1.0, 0.1 and 0.01 mol L(-1)). The pH of each sample set varied from 3 to 10 in order to obtain sorption envelopes. Results and discussion Ni adsorption increased as the pH increased, reaching its maximum of nearly pH 6. The adsorption was highest in Alfisol, followed by RA and XA. Competition between Ni(2+) and Ca(2+) was higher than that between Ni(2+) and Na(+) in all soil samples, as shown by the higher percentage of Ni adsorption at pH 5. At pH values below the intersection point of the three ionic strength curves (zero point of salt effect), Ni adsorption was generally higher in the more concentrated solution (highest IS), probably due to the neutralization of positive charges of soil colloids by Cl(-) ions and consequent adsorption of Ni(2+). Above this point, Ni adsorption was higher in the more diluted solution (lowest ionic strength), due to the higher negative potential at the colloid surfaces and the lower ionic competition for exchange sites in soil colloids. Conclusions The effect of ionic strength was lower in the Oxisols than in the Alfisol. The main mechanism that controlled Ni adsorption in the soils was the ionic exchange, since the adsorption of ionic species varied according to the variation of pH values. The ionic competition revealed the importance of electrolyte composition and ionic strength on Ni adsorption in soils from the humid tropics. Recommendations and perspectives The presence of NaCl or CaCl(2) in different ionic strengths affects the availability of heavy metals in contaminated soils. Therefore, the study of heavy metal dynamics in highly weathered soils must consider this behavior, especially in soils with large amounts of acric components.

Prevalence and counts of Salmonella spp. in minimally processed vegetables in Sao Paulo, Brazil

Minimally processed vegetables (MPV) may be important vehicles of Salmonella spp. and cause disease. This study aimed at detecting and enumerating Salmonella spp. in MPV marketed in the city of Sao Paulo, Brazil. A total of 512 samples of MPV packages collected in retail stores were tested for Salmonella spp. and total coliforms and Escherichia coil as indication of the hygienic status. Salmonella spp. was detected in four samples, two using the detection method and two using the counting method, where the results were 8.8 x 10(2) CFU/g and 2.4 x 10(2) CFU/g. The serovars were Salmonella Typhimurium (three samples) and Salmonella enterica subsp. enterica O:47:z4,z23:- (one sample). Fourteen samples (2.7%) presented counts of E. coli above the maximum limit established by the Brazilian regulation for MPV (10(2) CFU/g). Therefore, tightened surveillance and effective intervention strategies are necessary in order to address consumers and governments concerns on safety of MPV. (C) 2011 Elsevier Ltd. All rights reserved.

Acceptability of minimally processed and irradiated pineapple and watermelon among Brazilian consumers

This study aimed at evaluating the acceptance of MP watermelon and pineapple exposed to 1.0 and 2.5kGy compared to non-irradiated samples. No significant differences were observed in liking between irradiated and non-irradiated samples, and also between doses of 1.0 and 2.5 kGy. significant differences in sourness (pineapple) or sweetness (watermelon) and between intention of purchase of irradiated and non-irradiated fruits were riot observed as well. Results showed that MP watermelon and pineapple could be irradiated with doses up to 2.5 kGy without significant changes in acceptability. (C) 2008 Elsevier Ltd. All rights reserved.

Radioresistance of Salmonella species and Listeria monocytogenes on minimally processed arugula (Eruca sativa Mill.): Effect of irradiation on flavonoid content and acceptability of irradiated produce

This work studied the radiation resistance of Listeria monocytogenes and Salmonella species and the effect of irradiation on leaf flavonoid content and sensory acceptability of minimally processed arugula. Immersion in ozone-treated water reduced the analyzed microorganisms by 1 log. L. monocytogenes and Salmonella were not isolated from samples. Samples of this vegetable were inoculated with a cocktail of Salmonella spp. and L. monocytogenes and exposed to gamma irradiation. D-10 values for Salmonella ranged from 0.16 to 0.19 kGy and for L. monocytogenes from 0.37 to 0.48 kGy. Kaempferol glycoside levels were 4 and ca. 3 times higher in samples exposed to 1 and 2 kGy, respectively, than in control samples. An increase in quercetin glycoside was also observed mainly in samples exposed to 1 kGy. In sensory evaluation, arugula had good acceptability, even after exposure to 2 and 4 kGy. These results indicate that irradiation has potential as a practical processing step to improve the safety of arugula.

Electrospray MS-based characterization of beta-carbolines - mutagenic constituents of thermally processed meat

The beta-carbolines 1-methyl-9H-pyrido [3,4-b]indole and 9H-pyrido[3,4b]indole have been implicated as having causative roles in a number of human diseases, such as Parkinson`s disease and cancer. As they can be formed during the heating of protein-rich food, a number of analytical methodologies have been proposed for their detection and quantification in foodstuff For this purpose, LC-MS and LC-MS/MS have emerged as the most specific analytical methods, and the quantification is based on the occurrence of unusual ions, such as [M+H-(H(center dot))](+) and [M + H-2H](+). In this study, we have investigated the formation of these ions by accurate-mass electrospray MS/MS and demonstrated that these ions are formed from gas-phase ion-molecule reactions between water vapor present in the collision cell and the protonated molecule of 1-methyl-9H-pyrido [3,4-b]indole and 9H-pyrido[3,4b]indole. Although this reaction has been previously described for heterocyclic amine ions, it has been overlooked in the most of recent LC-MS and LC-MS/MS studies, and no complete data of the fragmentation are reported. Our results demonstrate that additional attention should be given with respect to eliminating water vapor residues in the mass spectrometer when analysis of beta-carbolines is performed, as this residue may affect the reliability in the results of quantification.

Novel and facile solution-phase synthesis of 2,5-diketopiperazines and O-glycosylated analogs

This work describes the synthesis in Solution of a series of related diketopiperazines with potential biological activities: cyclo(L-Pro-L-Ser), cyclo(L-Phe-L-Ser), cyclo(D-Phe-L-Ser) and the corresponding glycosylated analogs of the latter, cyclo[D-Phe-L-Ser(alpha GlcNAc)] and cyclo[D-Phe-L-Ser(beta GlcNAc)]. The synthetic approach involved coupling reactions of -OH or O-glycosylated serine benzyl esters with NFmoc-protected amino acids (Pro or Phe), followed by one-pot deprotection-cyclization reaction in the presence of 20% piperidine in DMF. (C) 2009 Elsevier Ltd. All rights reserved.

Microbiological quality of ready-to-eat minimally processed vegetables consumed in Brazil

Minimally processed leafy vegetables are ready-to-eat (RTE) products very attractive to consumers looking for healthy and convenient meals. However, the microbiological safety of these foods is of special concern due to the absence of lethal treatments during processing. In the present study, indicator microorganisms, Listeria spp. and Salmonella spp. were determined for 162 samples of minimally processed leafy vegetables commercialized in Brazil. Psychrotrophic aerobic bacterial populations >5 log CFU/g were found in 96.7% of the samples, while total and thermotolerant coliforms were detected respectively in 132 (81.5%) and 107 (66%) of vegetables analyzed. Escherichia coil was present in 86 (53.1%) samples analyzed and Listeria spp. and Salmonella spp. were detected respectively in 6 (3.7%) and 2 (1.2%) samples. These results indicate the need of implementing quality programs in the production chain of RTE vegetables to improve shelf life and microbiological safety. (C) 2011 Elsevier Ltd. All rights reserved.