Structural Phase Transition Studies on PMN-0.35PT using Infrared Spectroscopy

The purpose of the present work is to report studies on structural phase transition for PMN-xPT ferroelectric, with melt PbTiO3 composition around the MPB (x = 0.35 mol %), using infrared spectroscopy technique. The study was centered on monitoring the behavior of the 1-(NbO), 1-(TiO) and 1-(MgO) stretching modes as a function of temperature. The increasing as a function of temperature for 1-(TiO) and 1-(MgO) modes, observed between 230 and 300 K, can be related to the monoclinic (MC) + tetragonal (T) phase coexistence in the PMN-PT.

Electrophoretic deposition of Ba0.77Ca0.23TiO3 nanopowders

Ba0.77Ca0.23TiO3 (BCT23) nanometric powders, synthesized by the modified Pechini method, were used as precursor to produce thick films (50-130 mu m) employing the electrophoretic deposition (EPD) technique. The BCT23 powder presented a single crystalline phase with an average particle size and a crystallite size of similar to 60 nm and similar to 20 nm, respectively, when calcined at 800 degrees C/2h. BCT23 thick films were deposited on platinum substrates starting from different suspensions prepared by dispersion of the powder into: isopropyl alcohol (IPA) or a mixture of acetylacetone (Acac) and ethanol (EtOH) (1:1, volumetric ratio). A milling process was used to deagglomerate the powders in order to increase the suspension stability and improving the deposition. Dense and crack free thick films with uniform microstructure were obtained after sintering at 1300 degrees C/2 h from Acac+EtOH solution. (C) 2007 Elsevier B.V. All rights reserved.

Effect of polyol excess on the electrical property of vegetable-polyurethane film

Freestanding castor oil-based polyurethane (PU) film was obtained using spin-coating method. The effect of polyol content was analysed by means of thermally stimulated depolarisation current and AC dielectric measurements techniques. Two relaxation peaks were observed in the temperature range of -40 to 60 degrees C for PU with different polyol contents. The presence of polyol excess provides a shift to lower temperature of the a relaxation and the decrease in the activation energy of the transition in this region might be attributed to the plasticising effect of the polyol. The peak at higher temperature is due to the Maxwell-Wagner-Sillars relaxation, which also shifts in the low temperature direction as the polyol content is increased.