Using Polycarbonate Membranes as Templates for the Preparation of Au Nanostructures for Surface-Enhanced Raman Scattering

Polycarbonate membranes (PCM) of various pores sizes (400, 200, 100 and 50 nm) were used as templates for gold deposition. The electrodeposition from gold ions resulted in the formation of gold nanotubes when large pores size PCMs (400 and 200 nm) were used. On the other hand, gold nanowires were predominant for the PCMs with smaller pores size (100 and 50 nm). Surface-enhanced Raman scattering (SERS) from the probe molecule 4-mercaptopyridine (4-MPy) was obtained from all these nanostructures. The SERS efficiency of the substrates produced using the PC M templates were compared to two commonly used SERS platforms: a roughened gold electrode and gold nanostructures electrodeposited through organized polystyrene spheres (PSS). The SERS signal of the probe molecule increased as the pore diameter of the PCM template decreased. Moreover, the SERS efficiency from the nanostructures produced using 50 nm PCM templates was four and two times better than the signal from the roughened gold electrode and the PSS template, respectively. The SERS substrates prepared using PCM templates were more homogenous over a larger area (ca. 1 cm(2)), presented better spatial and sample to sample reproducibility than the other substrates. These results show that SERS substrates prepared using PCM templates are promising for the fabrication of planar SERS platforms for analytical/bioanalytical applications.

Surface-Enhanced Resonance Raman Scattering of Polyaniline on Silver and Gold Colloids

The interaction of emeraldine base (PANI-EB) with silver and gold colloids was probed by using Surface-Enhanced Resonance Raman Scattering (SERRS) at 3 different exciting radiations. Due to the great sensitivity of SERRS technique the detection limit of PANI-EB concentration was ca. 2 x 10(-7) mol L(-1) in Ag and Au colloidal suspensions. The UV-vis-NIR spectra of metal colloids in function of PANI-EB concentrations showed that gold colloids present a higher degree of aggregation than silver colloids. SERRS of PANI-EB on metal colloids allowed the study of the polymeric species formed primarily on the metallic surface. The polymer formed after the adsorption of PANI-EB on metallic nanoparticles is strongly dependent on the nature of the metal colloids. The oxidation of PANI-EB to pernigraniline occurred for silver colloids, while a doping process of PANI-EB on Au nanoparticles was evidenced through the observation of the characteristic SERRS spectrum of emeraldine salt at 1064nm.

The role of cross-linking structures to the formation of one-dimensional nano-organized polyaniline and their Raman fingerprint

In the present work. the resonance Raman. UV-vis-NIR and scanning electron microscopic (SEM) data of nanorods (about similar to 300 rim in diameter) and nanofibers (about similar to 93 nm in diameter) of PANI are presented and compared. The PANI samples were synthesized in aqueous media with dodecybenzenesulfonic acid (DBSA) and beta-naphtalenesulfonic acid (beta-NSA) as dopants, respectively. The presence of hands at 578, 1400 and 1632cm(-1) in the Raman spectra of PANI-NSA and PANI-DBSA shows that the formation of cross-linking structures is a general feature of the PANI chains prepared in micellar media. It is proposed that these structures are responsible for the one-dimensional PANI morphology formation. In addition, the Raman band at 609cm(-1) of PANI fibers is correlated with the extended PANI chain coil formation. (C) 2008 Elsevier B.V. All rights reserved.