Effect of a bleaching agent on abrasion of resin-based restoratives

Purpose: To evaluate the effect of a 10% carbamide peroxide-containing bleaching agent on brushing abrasion of esthetic restorative materials. Methods: Using a randomized complete block design, 150 specimens (n = 15) measuring 3 x 3 x 2 mm were fabricated into acrylic resin cylinders, using one of the restorative materials: a microfilled resin composite (At), a hybrid resin composite (Ch), a flowable resin composite (Wa), a resin-modified glass-ionomer cement (Fj) and a polyacid-modified resin composite (Dy). The bleaching agent or artificial saliva (control) was applied for 2 hours/day. After that, 120 brushing strokes were simulated automatically and the samples were kept in artificial saliva. Such bleaching/brushing cycle was performed daily for 21 days. Wear depth was assessed using profilometry. Results: Bleaching did not show significant effect on wear depth. There was a significant difference among the restorative materials. Tukey`s test showed that (Al=Ch) < (Wa) < (Fj) and that Dy was only different from Fj. (Am J Dent 2009;22:171-174).

A New Periapical Index Based on Cone Beam Computed Tomography

The purpose of this study was to evaluate a new periapical index based on cone beam computed tomography (CBCT) for identification of apical periodontitis (AP). The periapical index proposed in this study (CBCTPAI) was developed on the basis of criteria established from measurements corresponding to periapical radiolucency interpreted on CBCT scans. Radiolucent images suggestive of periapical lesions were measured by using the working tools of Planimp software on CBCT scans in 3 dimensions: buccopalatal, mesiodistal, and diagonal. The CBCTPAI was determined by the largest lesion extension. A 6-point (0-5) scoring system was used with 2 additional variables, expansion of cortical bone and destruction of cortical bone. A total of 1014 images (periapical radiographs and CBCT scans) originally taken from 596 patients were evaluated by 3 observers by using the CBCTPAI criteria. AP was identified in 39.5% and 60.9% of cases by radiography and CBCT, respectively (P<.01). The CBCTPAI offers an accurate diagnostic method for use with high-resolution images, which can reduce the incidence of false-negative diagnosis, minimize observer interference, and increase the reliability of epidemiologic studies, especially those referring to AP prevalence and severity. (J Endod 2008;34:1325-1331)

The Effect of Coating Patterns with Spinel-Based Investment on the Castability and Porosity of Titanium Cast into Three Phosphate-Bonded Investments

Purpose: This study evaluated the effect of pattern coating with spinel-based investment Rematitan Ultra (RU) on the castability and internal porosity of commercially pure (CP) titanium invested into phosphate-bonded investments. The apparent porosity of the investment was also measured. Materials and Methods: Square patterns (15 x 15 x 0.3 mm(3)) were either coated with RU, or not and invested into the phosphate-bonded investments: Rematitan Plus (RP), Rema Exakt (RE), Castorit Super C (CA), and RU (control group). The castings were made in an Ar-arc vacuum-pressure machine. The castability area (mm(2)) was measured by an image-analysis system (n = 10). For internal porosity, the casting (12 x 12 x 2 mm(3)) was studied by the X-ray method, and the projected porous area percentage was measured by an image-analysis system (n = 10). The apparent porosity of the investment (n = 10) was measured in accordance with the ASTM C373-88 standard. Results: Analysis of variance (One-way ANOVA) of castability was significant, and the Tukey test indicated that RU had the highest mean but the investing technique with coating increased the castability for all phosphate-bonded investments. The analysis of the internal porosity of the cast by the nonparametric test demonstrated that the RP, RE, and CA with coating and RP without coating did not differ from the control group (RU), while the CA and RE casts without coating were more porous. The one-way ANOVA of apparent porosity of the investment was significant, and the Tukey test showed that the means of RU (36.10%) and CA (37.22%) were higher than those of RP (25.91%) and RE (26.02%). Conclusion: Pattern coating with spinel-based material prior to phosphate-bonded investments can influence the castability and the internal porosity of CP Ti.

Color stability of silorane-based composites submitted to accelerated artificial ageing-An in situ study

Objectives: To assess the in situ color stability, surface and the tooth/restoration interface degradation of a silorane-based composite (P90, 3M ESPE) after accelerated artificial ageing (AAA), in comparison with other dimethacrylate monomer-based composites (Z250/Z350, 3M ESPE and Esthet-X, Dentsply). Methods: Class V cavities (25 mm(2) x 2 mmdeep) were prepared in 48 bovine incisors, which were randomly allocated into 4 groups of 12 specimens each, according to the type of restorative material used. After polishing, 10 specimens were submitted to initial color readings (Easyshade, Vita) and 2 to analysis by scanning electronic microscopy (SEM). Afterwards, the teeth were submitted to AAA for 384 h, which corresponds to 1 year of clinical use, after which new color readings and microscopic images were obtained. The values obtained for the color analysis were submitted to statistical analysis (1-way ANOVA, Tukey, p < 0.05). Results: With regard to color stability, it was verified that all the composites showed color alteration above the clinically acceptable levels (Delta E >= 3.3), and that the silorane-based composite showed higher Delta E (18.6), with a statistically significant difference in comparison with the other composites (p < 0.05). The SEM images showed small alterations for the dimethacrylate-based composites after AAA and extensive degradation for the silorane-based composite with a rupture at the interface between the matrix/particle. Conclusion: It may be concluded that the silorane-based composite underwent greater alteration with regard to color stability and greater surface and tooth/restoration interface degradation after AAA. (C) 2011 Elsevier Ltd. All rights reserved.