Fluorescent probes with malononitrile side group in methyl methacrylate copolymers

Fluorescent probes derivated from auramine, 1-aminopyrene, and 9-aminoacridine containing a malononitrile group are copolymerized with methyl methacrylate. These new fluorescent polymeric materials are studied in solution of different solvents by steady-state and time-resolved emission techniques. Their spectroscopic properties and excited state dynamics are driven by charge transfer from the aromatic group to the electron withdrawing CN groups, and this factor is responsible for the non-exponential emission decay behavior. (c) 2008 Elsevier B.V. All rights reserved.

Study of Water-Gas-Shift Reaction over La((1-y))Sr(y)Ni(x)Co((1-x))O(3) Perovskite as Precursors

The performance of La((1-y))Sr(y)Ni(x)Co((1-x))O(3) perovskites for the water gas shift reaction (WGSR) was investigated. The samples were prepared by the co- precipitation method and were performed by the BET method, XRD, TPR, and XPS. The catalytic tests were performed at 300 and 400 A degrees C and H(2)O(v)/CO = 2.3/1 (molar ratio). The sample with the highest surface area is La(0.70)Sr(0.30)NiO(3). The XRD results showed the formation of perovskite structure for all samples, and the La(0.70)Sr(0.30)NiO(3) sample also presented peaks corresponding to La(2)NiO(4) and NiO, indicating that the solubility limit of Sr in the perovskite lattice was surpassed. The replacement of Co by Ni favored the reduction of the species at lower temperatures, and the sample containing Sr presented the highest amount of reducible species, as identified by TPR results. All samples were active, the Sr containing perovskite appearing the most active due to the highest surface area, presence of the La(2)NiO(4) phase, and higher content of Cu in the surface, as detected by XPS. Among the samples containing Co, the most active one was that with x = 0.70 (60% of CO conversion).

Effects of the partial replacement of La by M (M=Ce, Ca and Sr) in La(2-x)M(x)CuO(4) perovskites on catalysis of the water-gas shift reaction

The performance of La(2-x)M(x)CuO(4) perovskites (where M = Ce, Ca or Sr) as catalysts for the water-gas shift reaction was investigated at 290 degrees C and 360 degrees C. The catalysts were characterized by EDS, XRD, N(2) adsorption-desorption, XPS and XANES. The XRD results showed that all the perovskites exhibited a single phase (the presence of perovskite structure), suggesting the incorporation of metals in the perovskite structure. The XPS and XANES results showed the presence of Cu(2+) on the surface. The perovskites that exhibited the best catalytic performance were La(2-x)Ce(x)CuO(4) perovslcites, with CO conversions of 85%-90%. Moreover, these perovskites have higher surface areas and larger amounts of Cu on the surface. And Ce has a higher filled energy level than the other metals, increasing the energy of the valence band of Ce and providing more electrons for the reaction. Besides, the La(1.80)Ca(0.20)CuO(4) perovskite showed a good catalytic performance.

CuO and CuO-ZnO catalysts supported on CeO(2) and CeO(2)-LaO(3) for low temperature water-gas shift reaction

This paper describes an investigation on CuO and CuO-ZnO catalysts supported on CeO(2) and CeO(2)-La(2)O(3) oxides, which were designed for the low temperature water-gas shift reaction (WGSR). Bulk catalysts were prepared by co-precipitation of metal nitrates and characterized by energy-dispersive spectroscopy (EDS), X-ray diffraction (XRD), surface area (by the BET method), X-ray photoelectron spectroscopy (XPS), and in situ X-ray absorption near edge structure (XANES). The catalysts` activities were tested in the forward WGSR, and the CuO/CeO(2) catalyst presented the best catalytic performance. The reasons for this are twofold: (1) the presence of Zn inhibits the interaction between Cu and Ce ions, and (2) lanthanum oxide forms a solid solution with cerium oxide, which will cause a decrease in the surface area of the catalysts. Also the CuO/CeO(2) catalyst presented the highest Cu content on the surface, which could influence its catalytic behavior. Additionally, the Cu and Cu(1+) species could influence the catalytic activity via a reduction-oxidation mechanism, corroborating to the best catalytic performance of the Cu/Ce catalyst. (c) 2010 Elsevier B.V. All rights reserved.