Evaluation of pH and Calcium Ion Release of Root-end Filling Materials Containing Calcium Hydroxide or Mineral Trioxide Aggregate

Introduction: To evaluate calcium ion release and pH of Sealer 26 (S26) (Dentsply, Rio de Janeiro, RJ, Brazil), white mineral trioxide aggregate (MTA), Endo CPM Sealer (CPM1) (EGEO SRL Bajo licencia MTM Argentina SA, Buenos Aires, Argentina), Endo CPM Sealer in a thicker consistency (CPM 2), and zinc oxide and eugenol cement (ZOE). Methods: Material samples (n = 10) were placed in polyethylene tubes and immersed in 10 mL of distilled water. After 3, 6,12,24, and 48 hours and 7,14, and 28 days, the water pH was determined with a pH meter, and calcium release was assessed by atomic absorption spectrophotometry. An empty tube was used as the control group. Results: The control group presented a pH value of 6.9 at all studied periods and did not show the presence of calcium ion. S26 presented greater hydroxyl ion release up to 12 hours (p < 0.05). From 24 hours until 28 days, S26, MTA, CPM1, and CPM2 had similar results. in ail periods, ZOE presented the lowest hydroxyl ion release. CPM1, followed by CPM2, released the most calcium ions until 24 hours (p < 0.05). Between 48 hours and 7 days, CPM1 and CPM2 had the highest release. A greater calcium ion release was observed for CPM2, followed by CPM1 at 14 days and for S26, CPM1, and CPM2 at 28 days. ZOE released the least calcium ions in all periods. Conclusion: Sealer 26, MTA, and Endo CPM sealer at normal or thicker consistency release hydroxyl and calcium ions. Endo CPM sealer may be an alternative as root-end filling material. (J Endod 2009;35:1418-1421)

Evaluation of pH and calcium ion release of new root-end filling materials

Objective. The purpose of this study was to evaluate the pH and calcium ion release of 6 materials used for root-end filling and perforation repair. Study design. Gray ProRoot MTA, gray MTA-Angelus, white MTA-Angelus, and CPM were compared to 2 experimental ones: MTA-exp, also based in Portland cement with a modified mixing liquid, and MBPc, an epoxy-resin based cement containing calcium hydroxide. After 3, 24, 72, and 168 hours the water in which each sample had been immersed was tested to determine the ph and calcium ion release. Results. All the analyzed materials showed alkaline pH and capacity to release calcium ions; however, a tendency of reduction of these characteristics was noted for all the analyzed materials, except for the MBPc, which showed a slight increase of pH among the 3 initial periods. Conclusion. The results suggest that all materials investigated presented alkaline pH and ability of release of calcium ions. (Oral Surg Oral Med Oral Pathol Oral Radiol Endod 2009; 108: 135-139)

Radiopacity of Portland Cement Associated With Different Radiopacifying Agents

This study evaluated the radiopacity of Portland cement associated with the following radiopacifying agents: bismuth oxide, zinc oxide, lead oxide, bismuth subnitrate, bismuth carbonate, barium sulfate, iodoform, calcium tungstate, and zirconium oxide. A ratio of 20% radiopacifier and 80% white Portland cement by weight was used for analysis. Pure Portland cement and dentin served as controls. Cement/radiopacifier and dentin disc-shaped specimens were fabricated, and radiopacity testing was performed according to the ISO 6876/2001 standard for dental root sealing materials. Using Insight occlusal films, the specimens were radiographed near to a graduated aluminum stepwedge varying from 2 to 16 mm in thickness. The radiographs were digitized and radiopacity compared with the aluminum stepwedge using Digora software (Orion Corporation Soredex, Helsinki, Finland). The radiographic density data were converted into mmAl and analyzed statistically by analysis of variance and Tukey-Kramer test (alpha = 0.05). The radiopacity of pure Portland cement was significantly lower (p < 0.05) than that of dentin, whereas all cement/radiopacifier mixtures were significantly more radiopaque than dentin and Portland cement alone (p < 0.05). Portland cement/bismuth oxide and Portland cement/lead oxide presented the highest radiopacity values and differed significantly from the other materials (p < 0.05), whereas Portland cement/zinc oxide presented the lowest radiopacity values of all mixtures (p < 0.05). All tested substances presented higher radiopacity than that of dentin and may potentially be added to the Portland cement as radiopacifying agents. However, the possible interference of the radiopacifiers with the setting chemistry, biocompatibility, and physical properties of the Portland cement should be further investigated before any clinical recommendation can be done. (J Endod 2009,35:737-740)

Mineral trioxide aggregate with or without calcium chloride in pulpotomy

The aim of this study was to evaluate the reaction of the pulp tissue against mineral trioxide aggregate (MTA) with or without 10% calcium chloride (CaCl2). Pulpotomies were performed in 4 canines and 8 premolars of two 8-month-old dogs. MTA with or without CaCl2 was applied on the pulp tissue. The animals were killed after 90 days, and the specimens were processed for the microscopic analysis. Pulp tissue response was similar for MTA with and without CaCl2 Pulp vitality was present in all specimens, along with pulp repair with formation of mineralized tissue bridging. The addition of CaCl2 to MTA did not change its biologic properties in formation of mineralized barrier after pulpotomy.

The effectiveness of mineral trioxide aggregate, calcium hydroxide and formocresol for pulpotomies in primary teeth

Aim To compare the effectiveness of mineral trioxide aggregate (MTA), calcium hydroxide (CH) and formocresol (FC) as pulp dressing agents in carious primary teeth. Methodology Forty-five primary mandibular molars with dental caries in 23 children [AUTHOR QUERY: How many children?] between 5 and 9 years old were treated by a conventional pulpotomy technique. The teeth were randomly assigned to the experimental ( CH or MTA) or control ( FC) groups. After coronal pulp removal and haemostasis, remaining pulp tissue was covered with MTA paste or CH powder in the experimental groups. In the control group, diluted FC was placed with a cotton pellet over the pulp tissue for 5 min and removed; the pulp tissue was then covered with zinc oxide-eugenol (ZOE) paste. All teeth were restored with reinforced ZOE base and resin modified glass-ionomer cement. Clinical and radiographic successes and failures were recorded at 3, 6, 12, 18 and 24 month follow-up. Results Forty-three teeth were available for follow-up. In the FC and MTA groups, 100% of the available teeth were clinically and radiographically successful at all follow-up appointments; dentine bridge formation could be detected in 29% of the teeth treated with MTA. In the CH group, 64% of the teeth presented clinical and radiographic failures detected throughout the follow-up period, and internal resorption was a frequent radiographic finding. Conclusions Mineral trioxide aggregate was superior to CH and equally as effective as FC as a pulpotomy dressing in primary mandibular molars. Internal resorption was the most common radiographic finding up to 24 month after pulpotomies performed with CH.

Study of the pozzolanic reaction kinetics in sugar cane bagasse-clay ash/calcium hydroxide system: kinetic parameters and pozzolanic activity

This paper presents a study of the pozzolanic reaction kinetics between calcium hydroxide and a mixture of sugar cane bagasse with 20 and 30% of clay, burned at 800 and 1000 degrees C (SCBCA) by electrical conductivity measurements. A kinetic-diffusive model produced in previous studies by some of the authors was used. The model was fitted to the experimental data, which allowed the computation of the kinetic parameters of the pozzolanic reaction (reaction rate constant and free energy of activation) that rigorously characterised the pozzolanic activity of the materials. The results show that SCBCA demonstrated reactivity and good pozzolanic qualities in the range 800-1000 degrees C.

Study on the observation of Eu(2+) and Eu(3+) valence states in low silica calcium aluminosilicate glasses

The optical, magnetic and structural properties of Eu doped low silica calcium aluminosilicate glasses were investigated. The optical absorption coefficient presented two bands at 39 246 and 29 416 cm(-1), which were assigned respectively to the 4f(7) ((8)S(7/2)) -> 4f(6) (4F(J)) 5d (T(2g)), and 4f(7) ((8)S(7/2)) -> 4f(6) (4F(J)) 5d (E(g)) transitions of Eu(2+). The fluorescence measured at 300 K on a sample doped with 0.5 wt% of Eu(2)O(3) exhibited a broad band centered at 17 350 cm(-1), which is attributed to the 4f(6)5d -> 4f(7) transition of Eu(2+), whereas the additional peaks are due to the (5)D(0) -> (7)F(J) (J = 1, 2, 4) transitions of Eu(3+). From magnetization and XANES data it was possible to evaluate the fractions of Eu(2+) and Eu(3+) for the sample doped with 0.5 and 5.0 wt% of Eu(2)O(3), the values of which were approximately 30 and 70%, respectively.

Pulpotomies with portland cement in human primary molars

Two clinical cases in which Portland cement (PC) was applied as a medicament after pulpotomy of mandibular primary molars in children are presented. Pulpotomy using PC was carried out in two mandibular first molars and one mandibular second molar, which were further followed-up. At the 3, 6 and 12-month follow-up appointments, clinical and radiographic examinations of the pulpotomized teeth and their periradicular area revealed that the treatments were successful in maintaining the teeth asymptomatic and preserving pulpal vitality. Additionally, the formation of a dentin bridge immediately below the PC could be observed in the three molars treated. PC may be considered as an effective alternative for primary molar pulpotomies, at least in a short-term period. Randomized clinical trials with human teeth are required in order to determine the suitability of PC before unlimited clinical use can be recommended.

Comparasion of two minimally invasive methods on the longevity of glass ionomer cement restorations: short-term results of a pilot study

The purpose of this study was to evaluate the clinical performance of glass ionomer cement (GIC) restorations comparing two minimally invasive methods in permanent teeth after 12 months. Fifty pregnant women (second trimester of pregnancy), mean age 22 ± 5.30 years, were treated by two previously trained operators. The treatment approaches tested were: chemomechanical method (CarisolvTM; MediTeam) and atraumatic restorative treatment (ART). A split-mouth study design was used in which the two treatments were randomly placed in 50 matched pairs of permanent teeth. The chemomechanical method (CM) was the test group and the ART was the control group. The treatments were performed in Public Health Centers. The tested restorative material was a high-strength GIC (Ketac Molar; 3M/ESPE). The restorations were placed according to the ART guidelines. Two calibrated independent examiners evaluated the restorations in accordance with ART criteria. The inter-examiner kappa was 0.97. Data were analyzed using 95% confidence interval on the binomial distribution and Fisher's exact test at 5% significance level. In a 12-month follow-up, 86% of the restorations were evaluated. In the test group (CM), 100% (CI=93.3-100%) of the restorations were considered successful. In the control group (ART) 97.6% (CI=87.4-99.9%) of the restorations were considered successful and 2.4% unsuccessful (marginal defect >0.5 mm). There was no statistically significant difference between the 12-mounth success rate for both groups (Fisher's exact test: P=0.49) and between the two operators (Fisher's exact test: P=1.00). Both minimally invasive methods, chemomechanical method and ART, showed a similar clinical performance after 12 months of follow up.

Fluoride release profile of a nanofilled resin-modified glass ionomer cement

The present study aimed to compare the fluoride (F-) release pattern of a nanofilled resin-modified glass ionomer cement (GIC) (Ketac N100 - KN) with available GICs used in dental practice (resin-modified GIC - Vitremer - V; conventional GIC - Ketac Molar - KM) and a nanofilled resin composite (Filtek Supreme - RC). Discs of each material (n=6) were placed into 4 mL of deionized water in sealed polyethylene vials and shaken, for 15 days. F- release (μg F-/cm²) was measured each day using a fluoride-ion specific electrode. Cumulative F- release means were statistically analyzed by linear regression analysis. In order to analyze the differences among materials and the influence of time in the daily F- release, 2-way ANOVA test was performed (α=0.05). The linear fits between the cumulative F- release profiles of RC and KM and time were weak. KN and V presented a strong relationship between cumulative F- release and time. There were significant differences between the daily F- release overtime up to the third day only for GICs materials. The daily F- release means for RC were similar overtime. The results indicate that the F- release profile of the nanofilled resin-modified GIC is comparable to the resin-modified GIC.

Effect of cement type and water storage time on the push-out bond strength of a glass fiber post

This study investigated the effects of the cement type and the water storage time on the push-out bond strength of a glass fiber post. Glass fiber posts (Fibrekor, Jeneric Pentron) were luted to post spaces using a self-cured resin cement (C&B Cement [CB]), a glass ionomer cement (Ketac Cem [KC]) or a resin-modified glass ionomer cement (GC FujiCEM [FC]) according to the manufacturers’ instructions. For each luting agent, the specimens were exposed to one of the following water storage times (n=5): 1 day (T1), 7 days (T7), 90 days (T90) and 180 days (T180). Push-out tests were performed after the storage times. Control specimens were not exposed to water storage, but subjected to the push-out test 10 min after post cementation. Data (in MPa) were analyzed by Kruskal-Wallis and Dunn`s test (α=0.05). Cement type and water storage time had a significant effect (p<0.05) on the push-out bond strength. CB showed significantly higher values of retention (p<0.05) than KC and FC, irrespective of the water storage time. Water storage increased significantly the push-out bond strength in T7 and T90, regardless of the cement type (p<0.05). The results showed that fiber posts luted to post spaces with the self-cured resin cement exhibited the best bonding performance throughout the 180-day water storage period. All cements exhibited a tendency to increase the bond strength after 7 and 90 days of water storage, decreasing thereafter.

Large apical periodontitis healing following root canal dressing with calcium hydroxide: a case report

PURPOSE: The objective of this paper is to report the clinical case of a patient who presented a chronic apical periodontitis, arising from internal inflammatory resorption followed by pulp necrosis, and a long-term success of a root canal therapy using calcium hydroxide as root canal dressing. CASE DESCRIPTION: A 20-year-old male patient presented for routine dental treatment. By radiographic examination we noted an extensive radioluscent area, laterally to the permanent maxillary right lateral incisor, with possibility of communication with the lateral periodontium, suggestive of a chronic apical periodontitis. Due to external root resorption detection, we used a calcium hydroxide root canal dressing, changed every 15 days, for a period of 2 months. Root canal filling was performed using gutta-percha cones by lateral condensation technique Radiographic follow up held after 19 years of treatment indicated a periodontium in conditions of normality, with the presence of lamina dura. CONCLUSION: Calcium hydroxide is a suitable material to be used as root canal dressing in teeth with apical periodontitis. Long-term evaluation demonstrated the satisfactory clinical outcome following root canal treatment.

Histopathological evaluation of root canal filling materials for primary teeth

This study aimed to assess the response of apical and periapical tissues of dogs' teeth after root canal filling with different materials. Forty roots from dogs' premolars were prepared biomechanically and assigned to 4 groups filled with: Group I: commercial calcium hydroxide and polyethylene glycol-based paste (Calen®) thickened with zinc oxide; Group II: paste composed of iodoform, Rifocort® and camphorated paramonochlorophenol; Group III: zinc oxide-eugenol cement; Group IV: sterile saline. After 30 days, the samples were subjected to histological processing. The histopathological findings revealed that in Groups I and IV the apical and periapical regions exhibited normal appearance, with large number of fibers and cells and no resorption of mineralized tissues. In Group II, mild inflammatory infiltrate and mild edema were observed, with discrete fibrogenesis and bone resorption. Group III showed altered periapical region and thickened periodontal ligament with presence of inflammatory cells and edema. It may be concluded that the Calen paste thickened with zinc oxide yielded the best tissue response, being the most indicated material for root canal filling of primary teeth with pulp vitality.

Antibacterial activity of root canal filling materials for primary teeth: zinc oxide and eugenol cement, Calen paste thickened with zinc oxide, Sealapex and EndoREZ

This study evaluated in vitro the antibacterial activity of 4 root canal filling materials for primary teeth - zinc oxide and eugenol cement (ZOE), Calen paste thickened with zinc oxide (Calen/ZO), Sealapex sealer and EndoREZ sealer - against 5 bacterial strains commonly found in endodontic infections (Kocuria rhizophila, Enterococcus faecalis, Streptococcus mutans, Escherichia coli and Staphylococcus aureus) using the agar diffusion test (agar-well technique). Calen paste, 1% chlorhexidine digluconate (CHX) and distilled water served as controls. Seven wells per dish were made at equidistant points and immediately filled with the test and control materials. After incubation of the plates at 37oC for 24 h, the diameter of the zones of bacterial growth inhibition produced around the wells was measured (in mm) with a digital caliper under reflected light. Data were analyzed statistically by analysis of variance and Tukey's post-hoc test (?=0.05). There were statistically significant differences (p<0.0001) among the zones of bacterial growth inhibition produced by the different materials against all target microorganisms. K. rhizophila was inhibited more effectively (p<0.05) by ZOE, while Calen/ZO had its highest antibacterial activity against E. faecalis (p<0.05). S. mutans was inhibited by Calen/ZO, Sealapex and ZOE in the same intensity (p>0.05). E. coli was inhibited more effectively (p<0.05) by ZOE, followed by Calen/ZO and Sealapex. Calen/ZO and ZOE were equally effective (p>0.05) against S. aureus, while Sealapex had the lowest antibacterial efficacy (p<0.05) against this microorganism. EndoREZ presented antibacterial activity only against K. rhizophila and S. aureus. The Calen paste and Calen/ZO produced larger zones of inhibition than 1% CHX when the marker microorganism was E faecalis. In conclusion, the in vitro antibacterial activity of the 4 root canal filling materials for primary teeth against bacterial strains commonly found in endodontic infections can be presented in a decreasing order of efficacy as follows: ZOE>Calen/ZO>Sealapex>EndoREZ.

Subcutaneous tissue response of isogenic mice to calcium hydroxide-based pastes with chlorhexidine

This study was evaluated the response of subcutaneous connective tissue of isogenic mice to calcium hydroxide-based pastes with chlorhexidine digluconate (CHX). Seventy isogenic male BALB/c mice aged 6-8 weeks and weighing 15-20 g were randomly assigned to 8 groups. The animals received polyethylene tube implants as follows: Groups I, II, and III (n=10) - Calen® paste mixed with 0.4% CHX (experimental paste; Calen/CHX) for 7, 21, and 63 days, respectively; Groups IV, V, and VI (n=10) - UltraCal™ paste mixed with 2% CHX (experimental paste supplied by Ultradent Products Inc.; Ultracal/CHX) for 7, 21, and 63 days, respectively; and Groups VII and VIII (n=5): empty tube for 7 and 21 days, respectively. At the end of the experimental periods, the implants were removed together with the surrounding tissues (skin and subcutaneous connective tissue). The biopsied tissues were subjected to routine processing for histological analysis. Using a descriptive analysis and a four-point (0-3) scoring system, the following criteria were considered for qualitative and quantitative analysis of the tissue around the implanted materials: collagen fiber formation, tissue thickness and inflammatory infiltrate. A quantitative analysis was performed by measuring the thickness (µm), area (µm²) and perimeter (µm) of the reactionary granulomatous tissue formed at the tube ends. Data were analyzed statistically by the Kruskal-Wallis test and Dunn's post-test (α=0.05). Calen/CHX showed biocompatibility with the subcutaneous and reactionary tissues, with areas of discrete fibrosis and normal conjunctive fibrous tissue, though without statistically significant difference (p>0.05) from the control groups. In Groups I to III, there was a predominance of score 1, while in Groups IV to VI scores 2 and 3 predominated for all analyzed parameters. UltraCal/CHX, on the other hand, induced the formation of an inflammatory infiltrate and abundant exudate, suggesting a persistent residual aggression from the material, even 63 days after implant placement. In conclusion, the Calen paste mixed with 0.4% CHX allowed an adequate tissue response, whereas the UltraCal paste mixed with 2% CHX showed unsatisfactory results.