Fatigue and damage accumulation of veneer porcelain pressed on Y-TZP

Objectives: This study compared the reliability and fracture patterns of zirconia cores veneered with pressable porcelain submitted to either axial or off-axis sliding contact fatigue. Methods: Forty-two Y-TZP plates (12 mm x 12 mm x 0.5 mm) veneered with pressable porcelain (12 mm x 12 mm x 1.2 mm) and adhesively luted to water aged composite resin blocks (12 mm x 12 mm x 4 mm) were stored in water at least 7 days prior to testing. Profiles for step-stress fatigue (ratio 3:2:1) were determined from single load to fracture tests (n = 3). Fatigue loading was delivered on specimen either on axial (n = 18) or off-axis 30 degrees angulation (n = 18) to simulate posterior tooth cusp inclination creating a 0.7 mm slide. Single load and fatigue tests utilized a 6.25 mm diameter WC indenter. Specimens were inspected by means of polarized-light microscope and SEM. Use level probability Weibull curves were plotted with 2-sided 90% confidence bounds (CB) and reliability for missions of 50,000 cycles at 200 N (90% CB) were calculated. Results: The calculated Weibull Beta was 3.34 and 2.47 for axial and off-axis groups, respectively, indicating that fatigue accelerated failure in both loading modes. The reliability data for a mission of 50,000 cycles at 200 N load with 90% CB indicates no difference between loading groups. Deep penetrating cone cracks reaching the core-veneer interface were observed in both groups. Partial cones due to the sliding component were observed along with the cone cracking for the off-axis group. No Y-TZP core fractures were observed. Conclusions: Reliability was not significantly different between axial and off-axis mouth-motion fatigued pressed over Y-TZP cores, but incorporation of sliding resulted in more aggressive damage on the veneer. (C) 2009 Elsevier Ltd. All rights reserved.

Clinical evaluation of two packable posterior composites A five-year follow-up

Background. Research has suggested that packable resin-based composites inserted with a placement technique similar to amalgam condensation can reduce the sensitivity associated with posterior restorations. The authors evaluated the clinical performance, including associated sensitivity, of two packable composites in a randomized five-year clinical trial. Methods. A single operator randomly placed two restorations in each of 33 patients: one restoration consisting of Alert (Jeneric/Pentron, Wallingford, Conn.) and the other consisting of SureFil (Dentsply/Caulk, Milford, Del.). There were 30 Class I and 36 Class II restorations. Two independent evaluators evaluated the restorations by using modified U.S.; Public Health Service criteria. The authors analyzed data by means of the Fisher, chi(2) and McNemar tests at P < .05. Results. Of 60 restorations evaluated at five years, two Class II restorations (one SureFil, one Alert) failed. All other restorations received the highest score possible for sensitivity and vitality. The only difference between the composites at the five-year recall was the significantly better surface texture of SureFil. The authors observed significantly different scores between the baseline and at five years for marginal discoloration (Alert and SureFil), surface texture (Alert and SureFil) and color (SureFil). Conclusions. Both packable resin-based composites showed excellent durability during the five-year follow-up. Clinical Implications. The investigated resin-based composites are suitable for posterior restorations.

Osteoinductivity potential of rhBMP-2 associated with two carriers in different dosages

The objective of this study was to evaluate bone formation after application of different doses of recombinant human bone morphogenetic protein-2 (rhBMP-2) combined with monoolein or poloxamer gels, in critical bone defects of rats. Forty-five Wistar rats were divided into nine treatment groups with five animals each: I: application of 1 A mu g rhBMP-2 + monoolein; II: 3 A mu g rhBMP-2 + monoolein; III: 7 A mu g rhBMP-2 + monoolein; IV: 1 A mu g rhBMP-2 + poloxamer; V: 3 A mu g rhBMP-2 + poloxamer; VI: 7 A mu g rhBMP-2 + poloxamer; VII: monoolein only; VIII: poloxamer only; and IX: critical bone defect only. A critical-sized defect of 6 mm diameter was produced in the left parietal bone and it was filled with gels of the above mentioned treatments. After 2 weeks, the calvarial bones were removed for histological processing. Bone formation in the groups that received poloxamer gel and rhBMP-2 was not significantly different from the control group (IX). Groups receiving monoolein and rhBMP-2 (1 and 3 A mu g) and those that received only the carriers (VII and VIII) had less bone formation in relation to the control. The association of rhBMP-2 to both poloxamer and monoolein did not exhibit any significant differentiation in bone formation in comparison with the control group.

The anatomy of two-rooted mandibular canines determined using micro-computed tomography

P>Aim To investigate the internal and external anatomy of extracted human mandibular canines with two roots and two distinct canals using micro-computed tomography (mu CT). Methodology Fourteen two-rooted human mandibular canines were scanned using a high-resolution mu CT system (SkyScan 1174v2; SkyScan N.V., Kontich, Belgium). The images were processed to evaluate the size of the roots, the furcation regions, the presence of accessory canals, the mean distances between several anatomical landmarks, the position of the apical foramina, the direction of root curvatures, the cross-sectional appearances (SMI index), the volume and surface areas of the root canals. Results Root bifurcation was located in both apical (44%, n = 6) and middle (58%, n = 8) thirds of the root. The size of the buccal and lingual roots was similar in 29% of the sample. From a buccal view, no curvature towards the lingual or buccal direction occurred in either roots. From a proximal view, no straight lingual root occurred. In both views, S-shaped roots were found in 21% of the specimens. Location of the apical foramen varied considerably, tending to the mesio-buccal aspect of both roots. Lateral and furcation canals were observed mostly in the cervical third in 29% and 65% of the sample, respectively. The structure model index (SMI) index ranged from 1.87 to 3.86, with a mean value of 2.93 +/- 0.46. Mean volume and area of the root canals were 11.52 +/- 3.44 mm3 and 71.16 +/- 11.83 mm2, respectively. Conclusions The evaluation of two-rooted mandibular canines revealed that bifurcations occurred in the apical and middle third. S-shaped roots were found in 21% of the specimens. Mean volume, surface area and SMI index of the root canals were 11.52 mm3, 71.16 mm2 and 2.93, respectively.

Microleakage into and from Two-Stage Implants: An In Vitro Comparative Study

Purpose: Gaps between an abutment and a dental implant are unavoidable, and microleakage may occur, leading to problems such as malodor and peri-implantitis. The aim of the present in vitro study was to investigate leakage of Staphylococcus aureus through the implant/abutment interface by the method of bacterial culture, and to compare the leakage rates of two different types of implant-abutment connections. Materials and Methods: Twenty Morse taper implants with abutments were divided into two groups: group A, which were evaluated for microleakage into the inner part of the implants, and group B, which were evaluated for microleakage from the inner part of the implants. Twenty internal-hexagon implants with abutments were also divided into two groups: group C, which were evaluated for microleakage into the inner part of the implants, and group D, which were evaluated for microleakage from the inner part of the implants. For the evaluation of leakage from the implants, the assemblies had the inner parts inoculated with S aureus, and each assembly was incubated in sterile brain heart infusion broth for 1 week. For assessment of leakage into the implants, each assembly was submerged in 4 mL S aureus culture in tubes and incubated for 2 weeks. The microleakage of the two implant connections was compared. Results: Microbial leakage occurred in all groups, and there was no statistically significant difference between groups A and C or between groups B and D. Conclusions: In vitro, S aureus leakage through the implant/abutment interface occurred with both Morse taper and internal-hexagon implants. INT J ORAL MAXILLOFAC IMPLANTS 2011;26:56-62