The effect of an experimental 4% TiF(4) varnish compared to NaF varnishes and 4% TiF(4) solution on dental erosion in vitro

This in vitro study assessed the effect of an experimental 4% TiF(4) varnish compared to commercial NaF and NaF/CaF(2) varnishes and 4% TiF(4) solution on enamel erosion. For this, 72 bovine enamel specimens were randomly allocated to the following treatments: NaF varnish (2.26% F), NaF/CaF(2) varnish (5.63% F), 4% TiF(4) varnish (2.45% F), F-free placebo varnish, 4% TiF(4) solution (2.45% F) and control (not treated). The varnishes were applied in a thin layer and removed after 6 h. The solution was applied to the enamel surface for 1 min. Then, the specimens were alternately de- and remineralized (6 times/day) in an artificial mouth for 5 days at 37 degrees C. Demineralization was performed with the beverage Sprite (1 min, 3 ml/min) and remineralization with artificial saliva (day: 59 min, 0.5 ml/min; during the night: 0.1 ml/min). The mean daily increment of erosion and the cumulative erosion data were tested using ANOVA and ANCOVA, respectively, followed by Tukey`s test (alpha = 0.05). The mean daily erosion increments and cumulative erosion (micrometers) were significantly less for the TiF(4) varnish (0.30 +/- 0.11/0.65 +/- 0.75) than for the NaF varnish (0.58 +/- 0.11/1.47 +/- 1.07) or the NaF/CaF(2) varnish (0.62 +/- 0.10/1.68 +/- 1.17), which in turn showed significantly less erosion than the placebo varnish (0.78 +/- 0.12/2.05 +/- 1.43), TiF(4) solution (0.86 +/- 0.11/2.05 +/- 1.49) and control (0.77 +/- 0.16/2.06 +/- 1.49). In conclusion, the TiF(4) varnish seems to be a promising treatment to reduce enamel loss under mild erosive conditions. Copyright (C) 2008 S. Karger AG, Basel.

Efficacy of Profile .04 taper series 29 in removing filling materials during root canal retreatment-an in vitro study

Objective. The aim of this study was to compare Profile .04 taper series 29 instruments and hand files for gutta-percha removal. Study design. Twenty maxillary central incisors with a single straight canal were instrumented and filled. The teeth were divided into 2 groups of 10 specimens each, according to gutta-percha removal techniques: Group 1- Profile series 29 and Group 2- hand files and solvent. The amount of time for gutta-percha removal and the number of fractured instruments were evaluated. Radiographs were taken and the teeth were grooved longitudinally and split. The area of residual debris was measured using computer software. Results. The time for filling material removal was significantly shorter when Profile series 29 was used (P = .00). Regarding cleanliness, there were no statistical differences in the teeth halves evaluations (P = .05). Hand instruments cleaned the canals significantly better than Profiles, in the radiographic analysis considering the whole canal. Overall, the radiographic analysis showed a smaller percentage of residual debris than the teeth halves analysis. Conclusion. The Profile series 29 instruments proved to be faster than hand instruments in removing root filling materials; however, hand instruments yielded better root canal cleanliness. Some residual debris was not visualized by radiographs. (Oral Surg Oral Med Oral Pathol Oral Radiol Endod 2009; 108: e46-e50)

In vitro wear, surface roughness and hardness of propanal-containing and diacetyl-containing novel composites and copolymers based on bis-GMA analogs

Objective. To evaluate the effect of two additives, aldehyde or diketone, on the wear, roughness and hardness of bis-GMA-based composites/copolymers containing TEGDMA, propoxylated bis-GMA (CH(3)bis-GMA) or propoxylated fluorinated bis-GMA (CF(3)bis-GMA). Methods. Fifteen experimental composites and 15 corresponding copolymers were prepared combining bis-GMA and TEGDMA, CH3bis-GMA or CF3bis-GMA, with aldehyde (24mol% and 32 mol%) or diketone (24 mol% and 32 mol%) totaling 30 groups. For composites, hybrid treated filler (barium aluminosilicate glass/pyrogenic silica; 60 wt%) was added to monomer mixtures. Photopolymerization was affected by 0.2 wt% each of camphorquinone and N,N-dimethyl-p-toluidine. Wear (W) test was conducted in a toothbrushing abrasion machine (n = 6) and quantified using a profilometer. Surface roughness (R) changes, before and after abrasion test, were determined using a rugosimeter. Microhardness (H) measurements were performed for dry and wet samples using a Knoop microindenter (n = 6). Data were analyzed by one-way ANOVA and Tukey`s test (alpha = 0.05). Results. Incorporation of additives led to improved W and H values for bis-GMA/TEGDMA and bis-GMA/CH(3)bis-GMA systems. Additives had no significant effect on the W and H changes of bis-GMA/CF(3)bis-GMA. With regard to R changes, additives produced decreased values for bis-GMA/CH3bis-GMA and bis-GMA/CF3bis-GMA composites. Bis-GMA/TEGDMA and bis-GMA/CH(3)bis-GMA copolymers with additives became smoother after abrasion test. Significance. The findings correlate with additives ability to improve degree of conversion of some composites/copolymers thereby enhancing mechanical properties. Published by Elsevier Ltd on behalf of Academy of Dental Materials

Preventive effect of iron gel with or without fluoride on bovine enamel erosion in vitro

Background: The aim of this study was to evaluate the preventive effect in vitro of experimental gel containing iron and/or fluoride on the erosion of bovine enamel. Methods: To standardize the blocks (n = 80), specimens (4 x 4 mm) were previously selected to measure the initial microhardness. The blocks were randomly allocated into four groups of 20 samples each: C (control, placebo gel); F (fluoride gel, 1.23% NaF); Fe (iron gel, 10 mmol/L FeSO(4)) and F + Fe (fluoride + iron gel). The gels were applied and removed after 1 minute. The blocks were then submitted to six alternating remineralization and demineralization cycles. The beverage Coca-Cola (R) (10 minutes, 30 mL) was used for demineralization, and artificial saliva (1 hour) for remineralization. The effect of erosion was measured by wear analysis (profilometry). Data were analysed by ANOVA and the Tukey test for individual comparisons (p <0.05). Results: The mean wear (+/- SD, mu m) was C: 0.94 +/- 0.22; F: 0.55 +/- 0.12; Fe: 0.49 +/- 0.11 and F + Fe: 0.55 +/- 0.13. When the experimental gels were used, there was statistically significant reduction in enamel wear in comparison with the control (p <0.001). However, the experimental gels did not differ significantly among them. Conclusions: The gels containing iron with or without fluoride are capable of interfering with the dissolution dental enamel in the presence of erosive challenge.

Preventive effect of an iron varnish on bovine enamel erosion in vitro

Objective: The aim of this study was to evaluate, in vitro, the effect of an experimental varnish containing iron on the dissolution of bovine enamel by carbonated beverage. Methods: Eighty specimens were randomly allocated to four groups (n = 20 per group), according to the following treatments: Fe varnish (FeV, 10 mmoL/L Fe), F varnish (FV, 2.71% F), placebo varnish (PV) and control (not treated, NT). The varnishes were applied in a thin layer and removed after 6 h. Then, the samples were submitted to six cycles, alternating re- and demineralisation (only 1 day). Demineralisation was performed with the beverage Coca-Cola (R) (10 min, 30 mL/block) and remineralisation with artificial saliva for I h. In order to determine the amount of enamel dissolved, the wear was analysed by profilometry. Data were analysed by ANOVA and Tukey`s test (p < 0.05). Results: The mean wear (+/- S.E.) was significantly lesser for the FeV (0.451 +/- 0.018 mu m) when compared to the other treatments. The FV caused significantly less wear (0.554 +/- 0.022 mu m) when compared to PV (0.991 +/- 0.039 mu m) and NT (1.014 +/- 0.033), which did not significantly differ from each other. Conclusions: The results suggest that the iron varnish can interfere with the dissolution of dental enamel in the presence of acidic beverages. (C) 2008 Elsevier Ltd. All rights reserved.