Effect of repeated cycles of chemical disinfection on the roughness and hardness of hard reline acrylic resins

Objective: The aim of this study was to assess the effect of repeated cycles of five chemical disinfectant solutions on the roughness and hardness of three hard chairside reliners. Methods: A total of 180 circular specimens (30 mm x 6 mm) were fabricated using three hard chairside reliners (Jet; n = 60, Kooliner; n = 60, Tokuyama Rebase II Fast; n = 60), which were immersed in deionised water (control), and five disinfectant solutions (1%, 2%, 5.25% sodium hypochlorite; 2% glutaraldehyde; 4% chlorhexidine gluconate). They were tested for Knoop hardness (KHN) and surface roughness (mu m), before and after 30 simulated disinfecting cycles. Data was analysed by the factorial scheme (6 x 2), two-way analysis of variance (anova), followed by Tukey`s test. Results: For Jet (from 18.74 to 13.86 KHN), Kooliner (from 14.09 to 8.72 KHN), Tokuyama (from 12.57 to 8.28 KHN) a significant decrease in hardness was observed irrespective of the solution used on all materials. For Jet (from 0.09 to 0.11 mu m) there was a statistically significant increase in roughness. Kooliner (from 0.36 to 0.26 mu m) presented a statistically significant decrease in roughness and Tokuyama (from 0.15 to 0.11 mu m) presented no statistically significant difference after 30 days. Conclusions: This study showed that all disinfectant solutions promoted a statistically significant decrease in hardness, whereas with roughness, the materials tested showed a statistically significant increase, except for Tokuyama. Although statistically significant values were registered, these results could not be considered clinically significant.

Effect of 980-nanometer diode laser on root canal permeability after dentin treatment with different chemical solutions

This study evaluated the effect of 980-nm diode laser at different parameters on root canal dentin permeability associated with different irrigants. Seventy-five canines were sectioned at 15 mm from the apex, prepared mechanically up to #40 .02 instrument, and irrigated with 2 mL distilled water. Final irrigation (10 mL) was used as follows: (1) distilled water; (2) 1% NaOCl; (3) 17% ethylenediaminetetraacetic acid + a cationic surfactant cetyltrimethylammonium bromide (EDTAC). Laser was applied at 1.5 or 3.0 W as either continuous wave or pulsed wave (100 Hz). The teeth were then processed histochemically, the percentage of copper ion penetration into the dentin of the canal walls was counted, and the data were analyzed statistically with the Tukey-Kramer test (alpha < .01). When laser was associated with water, an increase in permeability was found, whereas permeability decreased when associated with EDTAC. Dentin permeability after laser irradiation was directly dependent on the solution used for final irrigation.