Clinical feasibility of mandibular implant overdenture retainers submitted to immediate load

Clinical feasibility of mandibular implant overdenture retainers submitted to immediate load Introduction: Millions of people around the world do not have access to the benefits of osseointegration. Treatments involving oral rehabilitation with overdentures have been widely used by specialists in the oral medicine field. This is an alternative therapy for retention and stability achievement in total prosthesis with conventional treatment, and two implants are enough to establish a satisfactory overdenture. Objective: The objectives of the study were to evaluate 16 patients of both sexes, with an average age of 47.4 +/- 4 years, using electromyographic analysis of masseter and temporal muscles and analyse the increase of incisive and molar maximal bite force with their existing complete dentures and following mandibular implant overdenture therapy to assess the benefits of this treatment. Materials and methods: For these tests, the Myosystem-BR1 electromyograph and the IDDK Kratos dynamometer were used. Statistical analysis was performed using the repeated measures test (SPSS 17.0). Results: A decrease in electromyographic activity during the rest, lateral and protrusion movements and increase of the maximal incisive and molar bite force after 15 months with a mandibular implant overdenture was observed. Conclusion: All the patients in this study reported a considerable improvement in the masticatory function and prostheses stability following treatment. It is possible to propose that the use of mandibular implants overdenture should become the selected treatment for totally edentulous patients to facilitate oral function and quality of life.

Laboratory evaluation of the physicochemical properties of a new root canal sealer based on Copaifera multijuga oil-resin

Aim To compare a new root canal sealer based on Copaifera multijuga oil-resin (Biosealer) using three other established sealers (Sealer 26 (R), Endofill (R) and AH plus (R)) in terms of their physicochemical properties. Methodology The study was carried out according to the requirements of Specification Number 57 of the American Dental Association (ADA) and consisted of the following tests: setting time, flow, film thickness, dimensional stability, radiopacity and solubility/disintegration. Data were analysed statistically using anova and Tukey`s test for multiple comparisons. The significance level was set at 5% for all analyses. Results Sealer 26 (R) and AH Plus (R) had the longest setting time (P < 0.05). All materials presented flow in with the ADA`s guidelines. Regarding film thick-ness, Sealer 26 (R) did not have a satisfactory performance, as it had a higher mean value than the maximum allowed by the ADA (0.05 mm), being significantly different from the other materials (P < 0.05), which had mean values for film thickness in accordance with the ADA`s recommendations. Regarding the solubility and disintegration, only Endofill (R) did not meet the ADA`s specifications and presented the worst results of all materials (P < 0.05). Sealer 26 (R) presented the greatest dimensional changes and differed significantly from all other sealers (P < 0.05). Biosealer had the lowest radiopacity values and was significantly different from the other sealers (P < 0.05). Conclusion The experimental sealer based on Copaifera multijuga oil-resin presented satisfactory results in the physicochemical tests required by the ADA.

Color stability of silorane-based composites submitted to accelerated artificial ageing-An in situ study

Objectives: To assess the in situ color stability, surface and the tooth/restoration interface degradation of a silorane-based composite (P90, 3M ESPE) after accelerated artificial ageing (AAA), in comparison with other dimethacrylate monomer-based composites (Z250/Z350, 3M ESPE and Esthet-X, Dentsply). Methods: Class V cavities (25 mm(2) x 2 mmdeep) were prepared in 48 bovine incisors, which were randomly allocated into 4 groups of 12 specimens each, according to the type of restorative material used. After polishing, 10 specimens were submitted to initial color readings (Easyshade, Vita) and 2 to analysis by scanning electronic microscopy (SEM). Afterwards, the teeth were submitted to AAA for 384 h, which corresponds to 1 year of clinical use, after which new color readings and microscopic images were obtained. The values obtained for the color analysis were submitted to statistical analysis (1-way ANOVA, Tukey, p < 0.05). Results: With regard to color stability, it was verified that all the composites showed color alteration above the clinically acceptable levels (Delta E >= 3.3), and that the silorane-based composite showed higher Delta E (18.6), with a statistically significant difference in comparison with the other composites (p < 0.05). The SEM images showed small alterations for the dimethacrylate-based composites after AAA and extensive degradation for the silorane-based composite with a rupture at the interface between the matrix/particle. Conclusion: It may be concluded that the silorane-based composite underwent greater alteration with regard to color stability and greater surface and tooth/restoration interface degradation after AAA. (C) 2011 Elsevier Ltd. All rights reserved.

Effects of Ethanol on the Surface and Bulk Properties of a Microwave-Processed PMMA Denture Base Resin

Purpose: This study evaluated the effect of different concentrations of ethanol on hardness, roughness, flexural strength, and color stability of a denture base material using a microwave-processed acrylic resin as a model system. Materials and Methods: Sixty circular (14 x 4 mm) and 60 rectangular microwave-polymerized acrylic resin specimens (65 x 10 x 3 mm(3)) were employed in this study. The sample was divided into six groups according to the ethanol concentrations used in the immersion solution, as follows: 0% (water), 4.5%, 10%, 19%, 42%, and 100%. The specimens remained immersed for 30 days at 37 degrees C. The hardness test was performed by a hardness tester equipped with a Vickers diamond penetrator, and a surface roughness tester was used to measure the surface roughness of the specimens. Flexural strength testing was carried out on a universal testing machine. Color alterations (Delta E) were measured by a portable spectrophotometer after 12 and 30 days. Variables were analyzed by ANOVA/Tukey`s test (alpha = 0.05). Results: For the range of ethanol-water solutions for immersion (water only, 4.5%, 10%, 19.5%, 42%, and 100%), the following results were obtained for hardness (13.9 +/- 2.0, 12.1 +/- 0.7, 12.9 +/- 0.9, 11.2 +/- 1.5, 5.7 +/- 0.3, 2.7 +/- 0.5 VHN), roughness (0.13 +/- 0.01, 0.15 +/- 0.07, 0.13 +/- 0.05, 0.13 +/- 0.02, 0.23 +/- 0.05, 0.41 +/- 0.19 mu m), flexural strength (90 +/- 12, 103 +/- 18, 107 +/- 16, 90 +/- 25, 86 +/- 22, 8 +/- 2 MPa), and color (0.8 +/- 0.6, 0.8 +/- 0.3, 0.7 +/- 0.4, 0.9 +/- 0.3, 1.3 +/- 0.3, 3.9 +/- 1.5 Delta E) after 30 days. Conclusions: The findings of this study showed that the ethanol concentrations of tested drinks affect the physical properties of the investigated acrylic resin. An obvious plasticizing effect was found, which could lead to a lower in vivo durability associated with alcohol consumption.

Physical Properties of an Acrylic Resin after Incorporation of an Antimicrobial Monomer

Purpose: This study evaluated the effect of the incorporation of the antimicrobial monomer methacryloyloxyundecylpyridinium bromide (MUPB) on the hardness, roughness, flexural strength, and color stability of a denture base material. Materials and Methods: Ninety-six disk-shaped (14-mm diameter x 4-mm thick) and 30 rectangular (65 x 10 x 3.3 mm(3)) heat-polymerized acrylic resin specimens were divided into three groups according to the concentration of MUPB (w/w): (A) 0%, (B) 0.3%, (C) 0.6%. Hardness was assessed by a hardness tester equipped with a Vickers diamond penetrator. Flexural strength and surface roughness were tested on a universal testing machine and a surface roughness tester, respectively. Color alterations (Delta E) were measured by a portable spectrophotometer after 12 and 36 days of immersion in water, coffee, or wine. Variables were analyzed by ANOVA/Tukey HSD test (alpha = 0.05). Results: The following mean results (+/-SD) were obtained for hardness (A: 15.6 +/- 0.6, B: 14.6 +/- 1.7, C: 14.8 +/- 0.8 VHN; ANOVA: p = 0.061), flexural strength (A: 111 +/- 17, B: 105 +/- 12, C: 88 +/- 12 MPa; ANOVA: p = 0.008), and roughness (A: 0.20 +/- 0.11, B: 0.20 +/- 0.11, C: 0.24 +/- 0.08 mu m; ANOVA: p = 0.829). Color changes of immersed specimens were significantly influenced by solutions and time (A: 9.1 +/- 3.1, B: 14.8 +/- 7.5, C: 13.3 +/- 6.1 Delta E; ANOVA: p < 0.05). Conclusions: The incorporation of MUPB affects the mechanical properties of a denture base acrylic resin; however, the only significant change was observed for flexural strength and may not be critical. Color changes were slightly higher when resin containing MUPB was immersed in wine for a prolonged time; however, the difference has debatable clinical relevance.