Solubility of Epiphany Endodontic Sealer Prepared with Resinous Solvent

Purpose: To evaluate in vitro the solubility of the Epiphany endodontic filling material Epiphany (Pentron Clinical Technologies, Wallingford, CT) prepared with its resinous solvent. Methods: The specimens were prepared in the following experimental conditions: (1) GI, epiphany without photoactivation; (2) GII, Epiphany prepared with resinous solvent without photoactivation; (3) Gill, Epiphany followed by photoactivation; and (4) GIV, Epiphany prepared with resinous solvent followed by photoactivation. Ten specimens of each group were obtained from Teflon molds with 80% reduction in volume of the specimen`s dimensions based on American National Standard Institute/American Dental Association (ANSI/ADA) Specification No. 57. The samples were weighted and immersed in distilled water for 7 days. After this period, they were removed, dried, and weighed again. Solubility was calculated by using samples weight loss (%). The immersion liquid was evaluated through atomic absorption spectrometry. Results: The sealers without photoactivation were statistically similar (p > 0.05) between themselves (GI = 6.93% and GII = 6.39%) and different from the uncured sealers, which were statistically different between themselves (p < 0.05) (GIII = 3.56% and GIV = 0.47%). Only the Epiphany sealer prepared with resinous solvent followed by photoactivation presented solubility values within ANSI/ADA requirements, liberating the following amounts of ions: 114.43 mu g of Ca(2+)/mL, 2.4 mu g of Mg(2+)/mL, 0.33 mu g of Fe(2+)/mL, 0.11 mu 4g of Zn(2+)/mL, 1.31 mu g of Ni(2+)/mL, and 7.1 mu g of Na(+)/mL. Conclusion: The association of resinous solvent to the Epiphany sealer followed by photoactivation resulted in a filling material with low solubility and expressive liberation of calcium ions. (J Endod 2009;35:715-718)

Interfacial evaluation of experimentally weakened roots restored with adhesive materials and fibre posts: An SEM analysis

Objectives: To evaluate the bonding interface in experimentally weakened roots reinforced with adhesive restorative materials and quartz fibre posts, varying the light-exposure time of the composite resin used for root reinforcement. Methods: Twelve extracted human maxillary incisors teeth were used. The crowns were removed and the roots were endodontically treated. After post space preparation, the roots were assigned to four groups. The thickness of the root dentine was reduced and adhesively restored with composite resin light-activated through a translucent fibre post for either 40 s (group 1), 80 s (group 2) or 120 s (group 3). In the case of control (group 4), the roots were not weakened. One day after post cementation, the specimens were sectioned transversally in three slices and processed for scanning electron microscopic analysis to observe bonding interface formation, quality of the hybrid layer and density of resin tags using a four-step scale method. Results: Formation of a hybrid layer and resin tags were evident in all groups. There was no statistically (p > 0.05) significant difference between the regions analysed in each group (Friedman test) and between groups in each section depth (Kruskal-Wallis test). Furthermore, comparison of the flared/reinforced groups showed that the different time;; used for composite resin cure did not affect the results significantly (Kruskal-Wallis test, p = 0.2139). Conclusions: Different light-exposure times used for composite resin polymerisation during root canal reinforcement did not affect significantly the formation and quality of the dentine/adhesive/composite resin bonding interface. (C) 2008 Elsevier Ltd. All rights reserved.

Influence of Artificial Accelerated Aging on Dimensional Stability of Acrylic Resins Submitted to Different Storage Protocols

Purpose: The aim of this study was to evaluate the influence of artificial accelerated aging on dimensional stability of two types of acrylic resins (thermally and chemically activated) submitted to different protocols of storage. Materials and Methods: One hundred specimens were made using a Teflon matrix (1.5cmx0.5mm) with four imprint marks, following the lost-wax casting method. The specimens were divided into ten groups, according to the type of acrylic resin, aging procedure, and storage protocol (30 days). GI: acrylic resins thermally activated, aging, storage in artificial saliva for 16 hours, distilled water for 8 hours; GII: thermal, aging, artificial saliva for 16 hours, dry for 8 hours; GIII: thermal, no aging, artificial saliva for 16 hours, distilled water for 8 hours, GIV: thermal, no aging, artificial saliva for 16 hours, dry for 8 hours; GV: acrylic resins chemically activated, aging, artificial saliva for 16 hours, distilled water for 8 hours; GVI: chemical, aging, artificial saliva for 16 hours, dry for 8 hours; GVII: chemical, no aging, artificial saliva for 16 hours, distilled water for 8 hours; GVIII: chemical, no aging, artificial saliva for 16 hours, dry for 8 hours GIX: thermal, dry for 24 hours; and GX: chemical, dry for 24 hours. All specimens were photographed before and after treatment, and the images were evaluated by software (UTHSCSA-Image Tool) that made distance measurements between the marks in the specimens (mm), calculating the dimensional stability. Data were submitted to statistical analysis (two-way ANOVA, Tukey test, p = 0.05). Results: Statistical analysis showed that the specimens submitted to storage in water presented the largest distance between both axes (major and minor), statistically different (p < 0.05) from control groups. Conclusions: All acrylic resins presented dimensional changes, and the artificial accelerated aging and storage period influenced these alterations.