Reliability and Failure Modes of Implant-Supported Y-TZP and MCR Three-Unit Bridges

Purpose: Chipping within veneering porcelain has resulted in high clinical failure rates for implant-supported zirconia (yttria-tetragonal zirconia polycrystals [Y-TZP]) bridges. This study evaluated the reliability and failure modes of mouth-motion step-stress fatigued implant-supported Y-TZP versus palladium-silver alloy (PdAg) three-unit bridges. Materials and Methods: Implant-abutment replicas were embedded in polymethylmethacrylate resin. Y-TZP and PdAg frameworks, of similar design (n = 21 each), were fabricated, veneered, cemented (n = 3 each), and Hertzian contact-tested to obtain ultimate failure load. In each framework group, 18 specimens were distributed across three step-stress profiles and mouth-motion cyclically loaded according to the profile on the lingual slope of the buccal cusp of the pontic. Results: PdAg failures included competing flexural cracking at abutment and/or connector area and chipping, whereas Y-TZP presented predominantly cohesive failure within veneering porcelain. Including all failure modes, the reliability (two-sided at 90% confidence intervals) for a ""mission"" of 50,000 and 100,000 cycles at 300 N load was determined (Alta Pro, Reliasoft, Tucson, AZ, USA). No difference in reliability was observed between groups for a mission of 50,000. Reliability remained unchanged for a mission of 100,000 for PdAg, but significantly decreased for Y-TZP. Conclusions: Higher reliability was found for PdAg for a mission of 100,000 cycles at 300 N. Failure modes differed between materials.

Caries-preventive Efficacy and Retention of a Resin-modified Glass lonomer Cement and a Resin-based Fissure Sealant: A 3-year Split-mouth Randomised Clinical Trial

Purpose: This prospective clinical trial compared the retention rate and caries-preventive efficacy of two types of sealant modalities over a 3-year period. Materials and Methods: Using a split-mouth randomised design, 1280 sealants were randomly applied on sound permanent second molars of 320 young patients aged between 12 and 16 years. Half of the teeth (n = 640) were sealed with a resin-modified glass ionomer cement (RMGIC) (Vitremer (TM), 3M ESPE) and the other half (n = 640) with a conventional light-cure, resin-based fissure sealant (LCRB) (Fluoroshield (R), Dentsply Caulk). Teeth were evaluated at baseline, 6-, 12-, 18-, 24-, 30- and 36-month intervals with regard to retention and new caries development. Results: On the sealed occlusal surfaces after 3 years, 5.10% of RMGIC and 91.08% of LCRB sealants were totally intact and 6.37% of RMGIC and 7.65% of LCRB sealants were partially intact. New caries lesions were found in 20.06% of RMGIC sealed occlusal surfaces, compared to 8.91% for LCRB sealants. Conclusions: The findings of the present clinical study suggest that RMGIC should be used only as a transitional sealant that can be applied to newly erupting teeth throughout the eruptive process, whereas LCRB sealants are used to successfully prevent occlusal caries lesions once an effective rubber dam can be achieved. It can be concluded that there are differences between the RMGIC and LCRB sealants over a 3-year period in terms of the retention rate and caries-preventive efficacy. RMGIC can serve as a simple and economic sealing solution, however provisional. Due to its poor retention rate, periodic recalls are necessary, even after 6 months, to eventually replace the lost sealant.

Comparative histomorphometric and tomographic analysis of maxillary sinus floor augmentation in rabbits using autografts and xenografts

Our goal was to evaluate bone neoformation promoted by a bovine xenograft composite (XC) compared with autogenous graft for maxillary sinus augmentation in a rabbit model. The left maxillary sinus of 18 male rabbits was filled with 200 mg of cortical and cancellous autogenous bone and the right sinus was filled with 200 mg of a composite comprised organic and inorganic bovine matrices, pool of bBMPs and collagen. Postoperative implant intervals of 2, 4, and 8 weeks were analyzed. Differences in the bone optical density among the groups and experimental periods were evaluated by computed tomography analysis. The tissue response was evaluated by histomorphometric analysis of the newly formed bone, connective tissue and/or granulation tissue, residual material, and bone marrow. The tomographic analyses showed a maximum optical density in the 4-week period for both groups. Histologically, an inflammatory infiltrate was observed at 2 weeks in the XC group but exclusively around the organic particles of the biomaterial. Regarding to the amount of newly formed bone, no statistical differences (p > 0.05) were observed among the two treatments throughout the implant intervals. However, by the end of the 8 weeks, the quantity of bone marrow was two times greater (p < 0.05) in the control group than in the XC group. In conclusion, the xenograft composite promotes formation of new bone in a similar fashion to autogenous bone and could therefore be considered a biomaterial with potential applications as a bone substitute in maxillary sinus floor augmentation. (C) 2007 Wiley Periodicals, Inc.

Protective effect of different tetrafluorides on erosion of pellicle-free and pellicle-covered enamel and dentine

The aim was to analyze the protective effects of titanium, zirconium and hafnium tetrafluorides on erosion of pellicle-free and pellicle-covered enamel and dentine in vitro. Eight groups of 20 specimens each of bovine enamel and bovine dentine were prepared. Half the specimens in each group were immersed in human saliva for 2 h for pellicle formation. Specimens were then left untreated (controls) or were treated for 120 s with TiF(4), ZrF(4) or HfF(4) solutions (0.4 or 1%) or 1.25% AmF/NaF gel. All specimens were eroded by exposure to hydrochloric acid, pH 2.6, for 25 min. Cumulative calcium release into the acid was monitored in consecutive 30-second intervals for 5 min, then at 2-min intervals up to a total erosion time of 25 min using the Arsenazo III procedure. Data were analyzed by ANOVA. 1% TiF(4) solution offered the best protective effect, especially in dentine (reduction of calcium loss about 50% at 25 min). 1% ZrF 4, 1% HfF 4 and 0.4% TiF(4) also reduced calcium loss, but to a lesser extent. Long-term effects were limited to dentine, while reduction of enamel erosion (about 25%) was restricted to 1-min erosion. The fluoride gel had a protective effect only in dentine. The efficacy of the tetrafluorides was influenced by the presence of the pellicle layer, in that the protection against dentine erosion by TiF(4) and ZrF(4) was greater on pellicle-covered specimens. Tetrafluoride solutions, especially 1% TiF(4), could decrease dental erosion, but were more effective on dentine than on enamel. Copyright (C) 2008 S. Karger AG, Basel.

Determination of para-Chloroaniline and Reactive Oxygen Species in Chlorhexidine and Chlorhexidine Associated with Calcium Hydroxide

The aim of this study was to determine whether para-chloroaniline (PCA) and/or reactive oxygen species (ROS) are generated by chlorhexidine (CHX) alone or after CHX is mixed with calcium hydroxide at different time points. Mass spectrometry was performed to detect PCA in samples of 0.2% CHX and Ca(OH)2 mixed with 0.2% CHX. High-performance liquid chromatography was used to confirm the presence of CHX in the mixture with Ca(OH)2. The samples were analyzed immediately after mixing and after 7 and 14 days. During the intervals of the experiment, the samples were maintained at 36.5 degrees C and 95% relative humidity. PCA was detected in the 0.2% CHX solution after 14 days. The mixture of CHX with Ca(CH)2 liberated ROS at all time points, but no traces of CHX were present in the mixture as a result of immediate degradation of the CHX. (J Endod 2008;34:1508-1514)