Effect of curing protocol on the polymerization of dual-cured resin cements

Objectives. The purpose of this study was to evaluate how curing protocol affects the extent of polymerization of dual-cured resin cements. Methods. Four commercial resin cements were used (DuoLink, Panavia F 2.0, Variolink II and Enforce). The extent of polymerization of the resin cements cured under different conditions was measured using a (1)H Stray-Field MRI method, which also enabled to probe molecular mobility in the kHz frequency range. Results. Resin cements show well distinct behaviours concerning chemical cure. Immediate photo-activation appears to be the best choice for higher filler loaded resin cements (Panavia F 2.0 and Variolink). A photo-activation delay (5 min) did not induce any significant difference in the extent of polymerization of all cements. Significance. The extent of polymerization of dual-cured resin cements considerably changed among products under various curing protocols. Clinicians should optimize the materials choice taking into account the curing characteristics of the cements. (C) 2010 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Influence of curing protocol on selected properties of light-curing polymers: Degree of conversion, volume contraction, elastic modulus, and glass transition temperature

Objectives. The purpose of this study was to investigate the effect of light-curing protocol on degree of conversion (DC), volume contraction (C), elastic modulus (E), and glass transition temperature (T(g)) as measured on a model polymer. It was a further aim to correlate the measured values with each other. Methods. Different light-curing protocols were used in order to investigate the influence of energy density (ED), power density (PD), and mode of cure on the properties. The modes of cure were continuous, pulse-delay, and stepped irradiation. DC was measured by Raman micro-spectroscopy. C was determined by pycnometry and a density column. E was measured by a dynamic mechanical analyzer (DMA), and T(g) was measured by differential scanning calorimetry (DSC). Data were submitted to two-and three-way ANOVA, and linear regression analyses. Results. ED, PD, and mode of cure influenced DC, C, E, and T(g) of the polymer. A significant positive correlation was found between ED and DC (r = 0.58), ED and E (r = 0.51), and ED and T(g) (r = 0.44). Taken together, ED and PD were significantly related to DC and E. The regression coefficient was positive for ED and negative for PD. Significant positive correlations were detected between DC and C (r = 0.54), DC and E (r = 0.61), and DC and T(g) (r = 0.53). Comparisons between continuous and pulse-delay modes of cure showed significant influence of mode of cure: pulse-delay curing resulted in decreased DC, decreased C, and decreased T(g). Influence of mode of cure, when comparing continuous and step modes of cure, was more ambiguous. A complex relationship exists between curing protocol, microstructure of the resin and the investigated properties. The overall performance of a composite is thus indirectly affected by the curing protocol adopted, and the desired reduction of C may be in fact a consequence of the decrease in DC. (C) 2009 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Evaluation of physicochemical properties of four root canal sealers

P>Aim To assess the physicochemical properties and the surface morphology of AH Plus, GuttaFlow, RoekoSeal and Activ GP root canal sealers. Methodology Five samples of each material were evaluated for setting time, dimensional alteration, solubility and radiopacity tests, according to ANSI/ADA Specification 57. A total of 50 mL of deionized distilled water from the solubility tests were used to measure the metal solubility by atomic absorption spectrometry. The morphologies of the external surface and the cross-section of the samples were analysed by means of a scanning electron microscope (SEM). Statistical analysis was performed by using one-way anova and post hoc Tukey-Kramer tests with the null hypothesis set as 5%. Results AH Plus had the longest setting time (580.6 +/- 3.05 min) (P < 0.05). Activ GP did not have a mean value on the radiopacity and solubility tests (1.31 +/- 0.35 mm and 11.8 +/- 0.43%, respectively) in accordance with ANSI/ADA, being significantly different from the other materials (P < 0.05), which had mean values for these tests in accordance with the ADA`s requirements. GuttaFlow was the only sealer that conformed to the Specification 57 concerning the dimensional alteration test (0.44 +/- 0.16%) (P < 0.05). The spectrometry test revealed significant Ca2+, K+, Zn2+ ion release from Activ GP sealer (32.57 +/- 5.0, 1.57 +/- 0.22 and 8.20 +/- 1.74 mu g mL-1, respectively). In SEM analysis, the loss of matrix was evident and the filler particles were more distinguishable in all groups. Conclusions The setting time of all sealers was in accordance with ANSI/ADA`s requirements. Activ GP did not fulfill ANSI/ADA`s protocols regarding radiopacity, dimensional alteration and solubility. GuttaFlow was the only sealer that conformed to the Specification 57 in all tests. SEM analysis revealed that the surfaces of all sealers had micromorphological changes after the solubility test.

A comparative study of physicochemical properties of AH Plus, Epiphany, and Epiphany SE root canal sealers

P>Aim To assess the physicochemical properties and the surface morphology of AH Plus, Epiphany, and Epiphany SE root canal sealers. Methodology Five samples of each material were employed for each test according to ANSI/ADA specification 57. The samples were assigned to four groups: (i) AH Plus; (ii) Epiphany; (iii) Epiphany + Thinning Resin; (iv) Epiphany SE. The distilled water used during the solubility test was submitted to spectrometry to verify the release of calcium ions. The morphologies of the external surface and the cross-section of the samples were analysed by means of a scanning electron microscope (SEM). Statistical analysis was performed by using One-Way anova and post hoc Tukey-Kramer tests with the null hypothesis set as 5%. Results Setting time, flow and radiopacity results were in accordance with ANSI/ADA requirements whereas the dimensional change of all sealers and solubility of Epiphany did not fulfil ANSI/ADA protocols. AH Plus and Epiphany SE were similar in terms of flow, radiopacity, solubility and dimensional change. The spectrometry test revealed significant calcium ion release from Epiphany with and without the thinning resin. SEM analysis revealed essentially a homogeneous surface with compact layer and some rough areas. Conclusions Setting time, flow, and radiopacity tests conformed to ANSI/ADA standardization. The dimensional change in all groups and the solubility of Epiphany were greater than values considered acceptable, with higher amounts of calcium ion release. Epiphany SE revealed more organized, compacted, and homogeneous polymers in a reduced resin matrix when compared with the other groups.