Domestic use of a disclosing solution for denture hygiene: a randomised trial

Objectives: The purpose of this study was to investigate the effect of the domestic use of a disclosing agent for denture hygiene. Materials and methods: Completely edentulous participants wearing maxillary dentures were randomly assigned to one of the three intervention groups: (1) Follow-up only (control; n = 12); (2) Oral and denture hygiene instructions (n = 10); (3) Instructions associated with the home use of a disclosing agent (1% neutral red; n = 10). Biofilm coverage area (%) over internal and external surfaces of the maxillary denture was assessed at baseline and after 14 and 90 days. Data were evaluated by generalised estimating equations based on score tests (alpha = 0.05). Results: The participants presented low changes for areas of biofilm coverage (14 days (%): internal: GI = 1.4 +/- 0.9; GII = 1.5 +/- 1.3; GIII = -0.4 +/- 0.9; external: GI = 1.4 +/- 1.5; GII = 1.5 +/- 1.4; GIII = -0.4 +/- 0.9; 90 days (%): internal: GI = 2.0 +/- 0.9; GII = 2.2 +/- 1.4; GIII = 0.3 +/- 1.0; external: GI = 2.1 +/- 1.4; GII = 2.2 +/- 1.5; GIII = 0.3 +/- 0.9). Changes were similar for the three groups (p = 0.293) and were not influenced by the test time (p = 0.218). Conclusion: It can be concluded that the home use of a disclosing agent for denture hygiene does not improve the removal of the biofilm, particularly for patients with adequate oral hygiene habits.

Effects of Ethanol on the Surface and Bulk Properties of a Microwave-Processed PMMA Denture Base Resin

Purpose: This study evaluated the effect of different concentrations of ethanol on hardness, roughness, flexural strength, and color stability of a denture base material using a microwave-processed acrylic resin as a model system. Materials and Methods: Sixty circular (14 x 4 mm) and 60 rectangular microwave-polymerized acrylic resin specimens (65 x 10 x 3 mm(3)) were employed in this study. The sample was divided into six groups according to the ethanol concentrations used in the immersion solution, as follows: 0% (water), 4.5%, 10%, 19%, 42%, and 100%. The specimens remained immersed for 30 days at 37 degrees C. The hardness test was performed by a hardness tester equipped with a Vickers diamond penetrator, and a surface roughness tester was used to measure the surface roughness of the specimens. Flexural strength testing was carried out on a universal testing machine. Color alterations (Delta E) were measured by a portable spectrophotometer after 12 and 30 days. Variables were analyzed by ANOVA/Tukey`s test (alpha = 0.05). Results: For the range of ethanol-water solutions for immersion (water only, 4.5%, 10%, 19.5%, 42%, and 100%), the following results were obtained for hardness (13.9 +/- 2.0, 12.1 +/- 0.7, 12.9 +/- 0.9, 11.2 +/- 1.5, 5.7 +/- 0.3, 2.7 +/- 0.5 VHN), roughness (0.13 +/- 0.01, 0.15 +/- 0.07, 0.13 +/- 0.05, 0.13 +/- 0.02, 0.23 +/- 0.05, 0.41 +/- 0.19 mu m), flexural strength (90 +/- 12, 103 +/- 18, 107 +/- 16, 90 +/- 25, 86 +/- 22, 8 +/- 2 MPa), and color (0.8 +/- 0.6, 0.8 +/- 0.3, 0.7 +/- 0.4, 0.9 +/- 0.3, 1.3 +/- 0.3, 3.9 +/- 1.5 Delta E) after 30 days. Conclusions: The findings of this study showed that the ethanol concentrations of tested drinks affect the physical properties of the investigated acrylic resin. An obvious plasticizing effect was found, which could lead to a lower in vivo durability associated with alcohol consumption.