Microhardness of resin cements in the intraradicular environment: Effects of water storage and softening treament

Objectives. To analyze the microhardness of four dual-cure resin cements used for cementing fiber-reinforced posts under the following conditions: after 7 days of storage in water, after additional 24 h of immersion in 75% ethanol, and after 3 months of storage in water. Hardness measurements were taken at the cervical, middle and apical thirds along the cement line. Methods. Root canals of 40 bovine incisors were prepared for post space. Fibrekor (R) glass fiber-reinforced posts (Jeneric/Pentron) of 1 mm in diameter were cemented using Panavia F 2.0 (Kuraray), Variolink (Ivoclar-Vivadent), Rely X Unicem (3M ESPE) or Duolink (Bisco) (N = 10). After 7 days of water storage at 37 degrees C, half the sample (N = 5) was longitudinally sectioned and the initial microhardness measured along the cement line from cervical to apex. These same samples were further immersed in 75% ethanol for 24 h and reassessed. The remaining half (N = 5) was kept unsectioned in deionized water at 37 degrees C for 3 months, followed by sectioning and measuring. Data were analyzed by a series of two-way ANOVA and Tukey tests at alpha = 5%. Results. Statistically significant differences were identified among the cements, thirds and conditions. Significant interactions were also observed between cements and thirds and between cements and conditions. Panavia F exhibited significantly higher initial microhardness than the other three cements, which showed no statistical difference among themselves. Variolink and Duolink showed significantly higher microhardness values in the cervical third, without significant difference among the thirds for the other cements. Immersion in ethanol significantly reduced the hardness values for all cements, regardless of the thirds. Storage in water for 3 months had no influence on the hardness of most of the cements, with the exception of Unicem that showed a significant increase in the hardness values after this period. Results showed heterogeneity in the microhardness of the cements inside the canal. All cements presented some degree of softening after ethanol treatment, which suggests instability of the polymer. The quality of curing of resin cements in the root canal environment seems unpredictable and highly material dependent. (C) 2009 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Mechanical stability of adhesives under water storage

Objectives. To evaluate the effects of storage condition (wet or dry) and storage time (24 h and 3 months) on the ultimate tensile strength (UTS) of Single Bond (SB), 3M-ESPE; Opti Bond Solo Plus (OB), Kerr; One Step (OS), Bisco, and Prime & Bond NT (PB), Dentsply adhesive resins. Methods. Hourglass-shaped specimens were obtained from a metallic matrix. Each adhesive was dispensed to fill the molds completely and left undisturbed in a dark chamber for 4 min at 37 degrees C for solvent evaporation. They were individually light-cured for 80 s at 500 mW/cm(2) and randomly divided into three groups: 24 h of water storage; 3 months of water storage; 3 months of dry storage. The specimens were tested in tension at 0.5 mm/min using the microtensile method and data were analyzed by two-way ANOVA and SNK tests for each material. Results. Water storage for 3 months did not cause significant changes in the UTS of any of the adhesives (p-value). Values for water storage ranged from 25.9 MPa for Single Bond at 24 h to 32.7 MPa for Prime & Bond NT after 3 months. Dry storage for 3 months yielded significantly higher UTS for most adhesives, which ranged from approximately 20% for Opti Bond to 160% higher values for Single Bond compared to their 3 months wet storage values. Conclusion. The effects of storage condition and time on the UTS of adhesives were material-dependent. (C) 2009 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.