Effect of a 10% carbamide peroxide on wear resistance of enamel and dentine: In situ study

Objectives: This triple-blind, 2 x 2 crossover in situ study, was undertaken to verify whether the wear resistance of enamel and root dentine would be affected by bleaching with a 10% carbamide peroxide agent and a placebo agent. Methods: Thirty slabs of each. substrate (2 mm x 3 mm x 2 mm) were selected for each phase, after flattening and polishing procedures and microhardness test. After a 7-day lead-in period, one specimen of each substrate was randomly bonded on the facial surface of each one of 30 subject`s upper second premolars. The volunteers received instructions on how to perform toothbrushing and application of gel in the tray. Fifteen volunteers bleached their maxillary arch with a 10% carbamide peroxide bleaching agent for a 2-week period, while the remainders used a placebo agent. After a 1-week washout period, a new set of enamel and root dentine slabs were bonded to the premolars and volunteers were crossed over to the alternate agent for 14 days. The resistance of enamel and root dentine to wear following bleaching, toothbrushing and intraoral exposure was measured with a profilometer, using reference areas. Results: For enamel, ANOVA did not demonstrate significant difference between wear provided by placebo and bleaching agent (p = 0.3713), but higher wear depth was observed for bleached root dentine (p = 0.0346). Conclusions: While overnight bleaching caused no alteration in wear resistance of enamel, root dentine showed increased tissue loss. (C) 2008 Elsevier Ltd. All rights reserved.

Effects of light exposure time on composite resin hardness after root reinforcement using translucent fibre post

Objectives: The purpose of this in vitro study was to evaluate the Vickers hardness (VHN) of a Light Core (Bisco) composite resin after root reinforcement, according to the light exposure time, region of intracanal reinforcement and lateral distance from the light-transmitting fibre post. Methods: Forty-five 17-mm long roots were used. Twenty-four hours after obturation, the root canals were emptied to a depth of 12 mm and the root dentine was artificially flared to produce a 1 mm space between the fibre post and the canal walls. The roots were bulk restored with the composite resin, which was photoactivated through the post for 40 s (G1, control), 80 s (G2) or 120 s (G3). Twenty-four hours after post-cementation, the specimens were sectioned transversely into three slices at depths of 2, 6 and 10 mm, corresponding to the coronal, middle and apical regions of the reinforced root. Composite VHN was measured as the average of three indentations (100 g/15 s) in each region at lateral distances of 50, 200 and 350 mu m from the cement/post-interface. Results: Three-way analysis of variance (alpha = 0.05) indicated that the factors time, region and distance influenced the hardness and that the interaction time x region was statistically significant (p = 0.0193). Tukey`s test showed that the mean VHN values for G1 (76.37 +/- 8.58) and G2 (74.89 +/- 6.28) differed significantly from that for G3 (79.5 +/- 5.18). Conclusions: Composite resin hardness was significantly lower in deeper regions of root reinforcement and in lateral areas distant from the post. Overall, a light exposure time of 120 s provided higher composite hardness than the shorter times (40 and 80 s). (C) 2008 Elsevier Ltd. All rights reserved.