Magnetic retention and bar-clip attachment for implant-retained auricular prostheses: A comparative analysis

Retention systems for implant-retained auricular prostheses using either bar-clip attachments with 2 or 3 clips or retention with 2 or 3 magnets were wear tested (insertion and removal cycles) to simulate clinical periods of use. Measurements were taken at intervals of 540 cycles, which represents a period of use of approximately 6 months, for up to 3,240 cycles. Assessments of retentive force were carried out before, during, and after the wear test. Statistical analysis indicated that the bar-clip systems provided higher retention than the magnetic systems. The bar-clip attachment with 2 clips showed a significant loss of retentive force after wear testing (P < .05), suggesting lower durability and shorter clinical life. The retention provided by the bar-clip attachment with 3 clips remained stronger than that provided by all other systems tested. At the end of the wear test, the magnetic systems showed very little loss of retention but were still less retentive than the bar-clip systems, suggesting higher durability under clinical simulation despite the lower retention initially provided.

Comparative analysis of root surface smear layer removal by different etching modalities or erbium:yttrium-aluminum-garnet laser irradiation. A scanning electron microscopy study

The purpose of this study was to evaluate the effect of erbium:yttrium-aluminum-garnet (Er:YAG) laser (2.94 mu m) irradiation on the removal of root surface smear layer of extracted human teeth and to compare its efficacy with that of citric acid, ethylenediamine tetra-acetic acid (EDTA), or a gel containing a mixture of tetracycline hydrochloride (HCl) and citric acid, using scanning electron microscopy (SEM). Thirty human dentin specimens were randomly divided into six groups: G1 (control group), irrigated with 10 ml of physiologic saline solution; G2, conditioned with 24% citric acid gel; G3, conditioned with 24% EDTA gel; G4, conditioned with a 50% citric acid and tetracycline gel; G5, irradiated with Er:YAG laser (47 mJ/10 Hz/5.8 J/cm(2)/pulse); G6, irradiated with Er:YAG laser (83 mJ/10 Hz/10.3 J/cm(2)/pulse). Electron micrographs were obtained and analyzed according to a rating system. Statistical analysis was conducted with Kruskal-Wallis and Mann-Whitney tests (P < 0.05). G1 was statistically different from all the other groups; no statistically significant differences were observed between the Er:YAG laser groups and those undergoing the other treatment modalities. When the two Er:YAG laser groups were compared, the fluency of G6 was statistically more effective in smear layer removal than the one used in G5 (Mann-Whitney test, P < 0.01). Root surfaces irradiated by Er:YAG laser had more irregular contours than those treated by chemical agents. It can be concluded that all treatment modalities were effective in smear layer removal. The results of our study suggest that the Er:YAG laser can be safely used to condition diseased root surfaces effectively. Furthermore, the effect of Er:YAG laser irradiation on root surfaces should be evaluated in vivo so that its potential to enhance the healing of periodontal tissues can be assessed.

Caries Resistance of Lased Human Root Surface with 10.6 mu m CO(2) Laser-Thermal, Morphological, and Microhardness Analysis

Although the cariostatic effects of CO(2) laser on enamel have been shown, its effects on root surface demineralization remains uncertain. The objectives of this in vitro research was to establish safe parameters for a pulsed 10.6 mu m CO(2) laser and to evaluate its effect on morphological features of the root surface, as well as on the reduction of root demineralization. Ninety-five human root surfaces were randomly divided into five groups: G1-No treatment (control); G2-2.5 J/cm(2); G3-4.0 J/cm(2); G4-5.0 J/cm(2); and G5-6.0 J/cm(2). Intrapulpal temperature was evaluated during root surface irradiation by a thermocouple and morphological changes were evaluated by SEM. After the surface treatment, the specimens were submitted to a 7-day pH-cycling model. Subsequently, the cross-sectional Knoop microhardness values were measured. For all irradiated groups, intrapulpal temperature changes were less than 1.5 degrees C. Scanning electron microscopy images indicated that fluences as low as 4.0 J/cm(2) were sufficient to induce morphological changes in the root surface. Additionally, for fluences reaching or exceeding 4.0 J/cm(2), laser-induced inhibitory effects on root surface demineralization were observed. It was concluded that laser energy density in the range of 4.0 to 6.0 J/cm(2) could be applied to a dental root to reduce demineralization of this surface without compromising pulp vitality.

Laser phototherapy effect on protein metabolism parameters of rat salivary glands

The aim of this study was to evaluate the effects of infrared diode laser phototherapy (LP) on tissues of the submandibular gland (SMG) and parotid gland (PG). Wistar rats were randomly divided into experimental (A and B) and control (C) groups. A diode laser, 808 nm wavelength, in continuous wave mode, was applied to the PG, SMG and sublingual gland in the experimental groups on two consecutive days. The doses were 4 J/cm(2) and 8 J/cm(2), and total energy was 7 J and 14 J, respectively. The power output (500 mW) and power density (277 mW/cm(2)) were the same for both experimental groups. In order to visualize the area irradiated by the infrared laser, we used a red pilot beam (650 nm) with 3 mW maximum power for the experimental groups. For the control group, the red pilot beam was the only device used. The SMG and PG were removed after 1 week of the first irradiation. Total protein concentration, amylase, peroxidase, catalase and lactate dehydrogenase assays were performed, as well as histological analysis. Statistical tests revealed significant increase in the total protein concentration for groups A and B in the parotid glands (P < 0.05). Based on the results of this study, LP altered the total protein concentration in rats` parotid glands.

GAPD and tubulin are suitable internal controls for qPCR analysis of oral squamous cell carcinoma cell lines

The selection of housekeeping genes is critical for gene expression studies. To address this issue, four candidate housekeeping genes, including several commonly used ones, were investigated in oral squamous cell carcinoma cell lines. A simple quantitative RT-PCR approach was employed by comparing relative expression of the four candidate genes within two cancerous cell tines (HN6 and HN31) and one noncancerous cell tine (HaCaT) treated or not with EGF and TGF-beta 1. Data were analyzed using ANOVA followed by the NormFinder software program. On this basis, stability of the candidate housekeeping genes was ranked and non statistical differences were found using ANOVA test. On the other hand, the NormFinder was able to show that GAPD and TUBB presented the less variable results, representing appropriated housekeeping genes for the samples and conditions anatyzed. In conclusion, this study suggests that the GAPD and the TUBB represent adequate normalizers for gene profiting studies in OSCC cell. tines, covering, respectively, high and low expression levels genes. (C) 2008 Elsevier Ltd. All rights reserved.

Influence of irradiant energy on degree of conversion, polymerization rate and shrinkage stress in an experimental resin composite system

Objective. This study evaluated the degree of conversion (DC), maximum rate of cure (R(p)(max)), and polymerization stress (PS) developed by an experimental dental composite subjected to different irradiant energies (3,6,12, 24, or 48J/cm(2)) under constant irradiance (500 mw/cm(2)). Methods. DC and R(p)(max) were monitored for 10 min on the bottom surface of 2-mm thick disks and on 150-mu m thick films (representing the top of the specimen) using ATR-FTIR. PS was monitored for 10 min in 2-mm thick disks bonded to two glass rods (O = 5 mm) attached to a universal testing machine. One-way ANOVA/Tukey tests were used and differences in DC and R(p)(max) between top and bottom surfaces were examined using Student`s t-test. Statistical testing was performed at a pre-set alpha of 0.05. Results. For a given surface, DC showed differences among all groups, except at the top between 24 and 48 J/cm(2). R(p)(max) was similar among all groups at the same surface and statistically higher at the top surface. PS also showed significant differences among all groups. Data for 48 J/cm(2) were not obtained due to specimen failure at the glass/composite interface. Significance. Increases in irradiant exposure led to significant increases in DC and PS, but had no effect on R(p)(max) (c) 2008 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Analysis of four gutta-percha techniques used to fill mesial root canals of mandibular molars

P>Aim To compare the percentage of gutta-percha, sealer and voids and the influence of isthmuses in mesial root canals of mandibular molars filled with different techniques. Methodology Canals in 60 mesial roots of mandibular first molars were prepared with ProTaper instruments to size F2 (size 25, 0.08 taper) and filled using a single-cone, lateral compaction, System B or Thermafil techniques. An epoxy resin sealer was labelled with Rhodamine-B dye to allow analysis under a confocal microscope. The percentage of gutta-percha, sealer and area of voids was calculated at 2, 4 and 6 mm from the apex, using Image Tool 3.0 software. Statistical analysis was performed using nonparametric Kruskal-Wallis and Dunn tests (P < 0.05). The influence of isthmuses on the presence or absence of voids was evaluated using the Fisher test. Results At the 2 mm level, the percentage of gutta-percha, sealer and voids was similar amongst the System B, lateral compaction and single-cone techniques. The single-cone technique revealed significantly less gutta-percha, more sealer and voids in comparison with the Thermafil technique at the 2 and 4 mm level (P < 0.05). The analysis of all sections (2, 4 and 6 mm) revealed that more gutta-percha and less sealer and voids were found in root canals filled with Thermafil and System B techniques (P < 0.05). The Fisher test revealed that the presence of isthmuses increased the occurence of voids in the lateral compaction group only (P < 0.05). Conclusion Gutta-percha, sealer filled area and voids were dependent on the canal-filling technique. The presence of isthmuses may influence the quality of root filling.

Comparative histomorphometric and tomographic analysis of maxillary sinus floor augmentation in rabbits using autografts and xenografts

Our goal was to evaluate bone neoformation promoted by a bovine xenograft composite (XC) compared with autogenous graft for maxillary sinus augmentation in a rabbit model. The left maxillary sinus of 18 male rabbits was filled with 200 mg of cortical and cancellous autogenous bone and the right sinus was filled with 200 mg of a composite comprised organic and inorganic bovine matrices, pool of bBMPs and collagen. Postoperative implant intervals of 2, 4, and 8 weeks were analyzed. Differences in the bone optical density among the groups and experimental periods were evaluated by computed tomography analysis. The tissue response was evaluated by histomorphometric analysis of the newly formed bone, connective tissue and/or granulation tissue, residual material, and bone marrow. The tomographic analyses showed a maximum optical density in the 4-week period for both groups. Histologically, an inflammatory infiltrate was observed at 2 weeks in the XC group but exclusively around the organic particles of the biomaterial. Regarding to the amount of newly formed bone, no statistical differences (p > 0.05) were observed among the two treatments throughout the implant intervals. However, by the end of the 8 weeks, the quantity of bone marrow was two times greater (p < 0.05) in the control group than in the XC group. In conclusion, the xenograft composite promotes formation of new bone in a similar fashion to autogenous bone and could therefore be considered a biomaterial with potential applications as a bone substitute in maxillary sinus floor augmentation. (C) 2007 Wiley Periodicals, Inc.

Coupling of composite resin cements to quartz fiber posts: A comparison of industrial and ""chairside"" treatments of the post surface

Purpose: To evaluate the influence of surface treatments on microtensile bond strength of luting resin cements to fiber posts. Materials and Methods: Forty-two quartz fiber posts (Light Post, RTD) were divided into 7 groups (n = 6) according to the surface treatment. I and 11: experimental patented industrial treatment consisting of zirconium oxide coating and silanization (RTD); III: industrial treatment followed by adhesive application (XPBond, Dentsply Caulk); IV: adhesive (XPBond); V: adhesive (Prime&Bond NT, Dentsply Caulk); VI: silane (Calibra Silane, Dentsply Caulk); VII: no treatment. Adhesives were used in the self-curing mode. Two cements (Sealbond, RTD - group 1, and Calibra, Dentsply Caulk - groups 11 to VII) were applied on the posts to produce cylindrical specimens. Post/cement interfaces were evaluated under SEM. The surface of the industrially coated posts was examined using energy dispersive analysis by x-ray. Cylinders were cut to obtain microtensile sticks that were loaded in tension at a crosshead speed of 0.5 mm/min until failure. Statistical analysis was performed using Kruskal-Wallis analysis of variance followed by Dunn`s multiple range test for post-hoc comparisons (p < 0.05). Weibull analysis was also performed. Results: The post/cement bond strength was significantly higher on fiber posts treated industrially (I: 23.14 +/- 8.05 MPa; II: 21.56 +/- 7.07 MPa; III: 22.37 +/- 7.00 MPa) or treated with XPBond adhesive (IV: 21.03 +/- 5.34 MPa) when compared to Prime&Bond NT application (V: 14.05 +/- 5.06 MPa), silanization (VI: 6.31 +/- 4.60 MPa) or no treatment (VII: 4.62 +/- 4.31) of conventional fiber posts (p < 0.001). Conclusion: The experimental industrial surface treatment and the adhesive application enhanced fiber post to resin cement interfacial strength. Industrial pretreatment may simplify the clinical luting procedure.

Masticatory process in individuals with maxillary and mandibular osteoporosis: electromyographic analysis

The masseter and temporal muscles of patients with maxillary and mandibular osteoporosis were submitted to electromyographic analysis and compared with a control group. In conclusion, individuals with osteoporosis did not show significantly lower masticatory cycle performance and efficiency compared to the control group during the proposal mastications. This study aimed to examine electromyographically the masseter and temporal muscles of patients with maxillary and mandibular osteoporosis and compare these patients with control patients. Sixty individuals of both genders with an average age of 53.0 +/- 5 years took part in the study, distributed in two groups with 30 individuals each: (1) individuals with osteoporosis; (2) control patients during the habitual and non-habitual mastication. The electromyographic apparel used was a Myosystem-BR1-DataHomins Technology Ltda., with five channels of acquisition and electrodes active differentials. Statistical analysis of the results was performed using SPSS version 15.0 (Chicago, IL, USA). The result of the Student`s t test indicated no significant differences (p > 0.05) between the normalized values of the ensemble average obtained in masticatory cycles in both groups. Based on the results of this study, it was concluded that individuals with osteoporosis did not show significantly lower masticatory cycle performance and efficiency compared to control subjects during the habitual and non-habitual mastications. This result is very important because it demonstrates the functionality of the complex physiological process of mastication in individuals with osteoporosis at the bones that compose the face.

Influence of the irradiation distance and the use of cooling to increase enamel-acid resistance with Er:YAG laser

Objectives: The aim of this study was to assess the influence of irradiation distance and the use of cooling in the Er:YAG laser efficacy in preventing enamel demineralization. Methods: 84 enamel blocks were randomly assigned to seven groups (n = 12): G1: control group - no treatment, G2-G7: experimental groups treated with Er:YAG laser (80 mJ/2 Hz) at different irradiation distances with or without cooling: G2: 4 mm/2 mL; G3: 4 mm/no cooling; G4: 8 mm/2 mL; G5: 8 mm/no cooling; G6: 16 mm/2 mL; G7: 16 mm/no cooling. The samples were submitted to an in vitro pH cycles for 14 days. Next, the specimens were sectioned in sections of 80-100 mu m in thickness and the demineralization patterns of prepared slices were assessed using a polarized light microscope. Three samples from each group were analyzed with scanning electronic microscopy. Analysis of variance and the Fisher test were performed for the statistical analysis of the data obtained from the caries-lesion-depth measurements (CLDM) (alpha = 5%). Results: The control group (CLDM = 0.67 mm) was statistically different from group 2 (CLDM = 0.42 mm), which presented a smaller lesion depth, and group 6 (0.91 mm), which presented a greater lesion depth. The results of groups 3 (CLDM = 0.74 mm), 4 (CLDM = 0.70 mm), 5 (CLDM = 0.67 mm) and 7 (CLDM = 0.89 mm) presented statistical similarity. The scanning electronic microscopy analysis showed ablation areas in the samples from groups 4, 5, 6 and 7, and a slightly demineralized area in group 2. Conclusions: It was possible to conclude that Er:YAG laser was efficient in preventing enamel demineralization at a 4-mm irradiation distance using cooling. (C) 2010 Elsevier Ltd. All rights reserved.