Evaluation of the flow rate of 3 endodontic sealers: Sealer 26, AH Plus, and MTA Obtura

Objective. The aim of this study was to evaluate the flow rate of 3 endodontic sealers: Sealer 26, AH Plus, and MTA Obtura. Study design. According to the method proposed by the American Dental Association (ADA specification no. 57), the sealers were placed between 2 glass slabs under a weight of 120 g. The diameters of the formed discs were measured with a digital paquimeter. The test was repeated 5 times for each sealer. Results. The results were expressed as arithmetic means, and the statistical analysis was performed through Tukey test. AH Plus showed significantly superior flow rate compared with Sealer 26 and MTA Obtura. There was no statistically significant difference between flow rates presented by Sealer 26 and MTA Obtura. Conclusion. Within the limitations of this in vitro study, it was concluded that all of the the endodontic sealers tested presented greater flow than the minimum recommended in the ADA 57 specification. (Oral Surg Oral Med Oral Pathol Oral Radiol Endod 2010;109:e47-e49)

Effect of oxalate desensitizers and dentin moisture during total-etch bonding

Purpose: To evaluate the effect of oxalate during total-etch bonding, under different dentin moisture conditions, over time. The null hypothesis tested was that microtensile bond strength (mu TBS) was not affected by oxalate treatment and dentin moisture during two evaluation periods. Methods: Extracted human third molars had their mid-coronal dentin exposed flat and polished with 600-grit SiC paper. The surfaces were etched with 35% phosphoric acid for 15 seconds, washed and blot dried. After etching, a 3% potassium oxalate gel was applied for 120 seconds, except for the control group (no desensitizer). The surface was then washed and left moist (Wet bonding) or air-dried for 30 seconds (Dry bonding). The surfaces were bonded with: (I) two 2-step etch-and-rinse adhesives: Single Bond (SB); Prime & Bond NT (PBNT) and (2) one 3-step etch-and-rinse adhesive: Scotchbond Multi Purpose (SBMP). Composite buildups were constructed incrementally with Tetric Ceram resin composite. Each increment was cured for 40 seconds. After storage in water for 24 hours or 1 year at 37 C, the specimens were prepared for mu TBS testing with a cross-sectional area of approximately 1 mm(2). They were then tested in tension in an Instron machine at 0.5 mm/minute. Data were analyzed by ANOVA and Student-Newman-Keuls at alpha = 0.05. Results: Application of potassium oxalate had no significant effect on the bond strengths of SBMP and PBNT, regardless of the surface moisture condition (P > 0.05). Conversely, reduced bond strengths were observed after oxalate treatment for SB in both moisture conditions, that being significantly lower when using a dry-bonding procedure (P < 0.05). Lower bond strength was obtained for PBNT when a dry-bonding technique was used, regardless of the oxalate treatment (P < 0.05). After aging the specimens for 1 year, bond strengths decreased. Smaller reductions were observed for SBMP, regardless of moisture conditions. For the WB technique, smaller reductions after 1 year were observed without oxalate treatment for SB and after oxalate treatment for PBNT. (Am J Dent 2010;23:137-141).