Bis-GMA co-polymerizations: Influence on conversion, flexural properties, fracture toughness and susceptibility to ethanol degradation of experimental composites

Objectives. The aim of this study was to evaluate the influence of monomer content on fracture toughness (K(Ic)) before and after ethanol solution storage, flexural properties and degree of conversion (DC) of bisphenol A glycidyl methacrylate (Bis-GMA) co-polymers. Methods. Five formulations were tested, containing Bis-GMA (B) combined with TEGDMA (T), UDMA (U) or Bis-EMA (E), as follows (in mol%): 30B:70T; 30B:35T:35U; 30B:70U; 30B:35T:35E; 30B:70E. Bimodal filler was introduced at 80 wt%. Single-edge notched beams for fracture toughness (FT, 25 mm x 5 mm x 2.5 mm, a/w = 0.5, n = 20) and 10 mm x 2 mm x 1 mm beams for flexural strength (FS) and modulus (FM) determination (10 mm x 2 mm x 1 mm, n = 10) were built and then stored in distilled water for 24 h at 37 degrees C. All FS/FM beams and half of the FT specimens were immediately submitted to three-point bending test. The remaining FT specimens were stored in a 75%ethanol/25%water (v/v) solution for 3 months prior to testing. DC was determined with FT-Raman spectroscopy in fragments of both FT and FS/FM specimens at 24 h. Data were submitted to one-way ANOVA/Tukey test (alpha = 5%). Results. The 30B:70T composite presented the highest K(Ic) value (in MPa m(1/2)) at 24 h (1.3 +/- 0.4), statistically similar to 30B:35T:35U and 30B:70U, while 30B:70E presented the lowest value (0.5 +/- 0.1). After ethanol storage, reductions in K(Ic) ranged from 33 to 72%. The 30B:70E material presented the lowest reduction in FT and 30B:70U, the highest. DC was similar among groups (69-73%), except for 30B:70U (52 +/- 4%, p < 0.001). 30B:70U and 30B:35T:35U presented the highest FS (125 +/- 21 and 122 +/- 14 MPa, respectively), statistically different from 30B:70T or 30B:70E (92 +/- 20 and 94 +/- 16 MPa, respectively). Composites containing UDMA or Bis-EMA associated with Bis-GMA presented similar FM, statistically lower than 30B:35T:35U. Significance. Composites formulated with Bis-GMA:TEGDMA:UDMA presented the best compromise between conversion and mechanical properties. (C) 2009 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

GP5+/6+ SYBR Green methodology for simultaneous screening and quantification of human papillomavirus

Background: Detection and quantification of human papillomavirus (HPV) may help in predicting the evolution of HPV infection and progression of associated lesions. Objectives: We propose a novel protocol using consensus primers GP5+/6+ in a SYBR Green quantitative real-time (Q-RT) polymerase chain reaction (PCR). The strategy permits screening for HPV infection and viral load quantification simultaneously. Study design: DNA from 153 archived cervical samples, previously tested for HPV detection by GP5+/6+ PCR and typed by EIA-RLB (enzyme immunoassay-reverse line blot) or sequence analysis, was analysed using SYBR Green Q-RT PCR. Melting temperature assay (T(m)) and cycle threshold (C(t)) were used to evaluate HPV positivity and viral load. The T(m) in the range of 77-82 degrees C was considered to be positive for HPV-DNA. HPV results generated through GP5+/6+ conventional PCR were considered the gold standard against which sensitivity and specificity of our assay were measured. Results: Out of 104 HPV positive samples, 100 (96.2%) were also determined as positive by SYBR Green Q-RT PCR; of the 49 HPV-negative samples, all were determined as negative. There was an excellent positivity agreement (K = 0.94) between the SYBR Green Q-RT and the previous methods employed. The specificity and sensitivity were 100% and 96.2%, respectively. Comparison of SYBR Green Q-RT and TaqMan oligo-probe technologies gave an excellent concordance (pc = 0.95) which validated the proposed strategy. Conclusions: We propose a sensitive and easy-to-perform technique for HPV screening and viral load quantification simultaneously. (C) 2009 Elsevier B.V. All rights reserved.