Influence of Filling Materials on the Bonding Interface of Thin-walled Roots Reinforced with Resin and Quartz Fiber Posts

Introduction: A common complication during the restoration of severely destroyed teeth is the loss of coronal root dentine. The aim of this study was to evaluate the influence of different sealers on the bonding interface of weakened roots reinforced with resin and fiber posts. Methods: Sixty extracted maxillary canines were used. The crowns were removed, and the thickness of root dentine was reduced in the experimental (n = 40) and positive control (n = 10) groups. The specimens of experimental group were assigned to four subgroups (n = 10) according to the filling material: gutta-percha + Grossmann`s sealer, gutta-percha + AH Plus (Dentsply De Trey Gmbh, Konstanz, Germany), gutta-percha + Epiphany (Pentron Clinical Technologies, Wallingford, CT), and Resilon (Resilon Research LLC, Madison, CT) + Epiphany. In the negative control group (n = 10), canals were not filled. After post space preparation, the roots were restored with composite resin light-activated through a translucent fiber post. After 24 hours, specimens were transversally sectioned into 1-mm-thick slices. Push-out test and scanning electron microscopic (SEM) analyses of different regions were performed. Data from push-out test were analyzed by using Tukey post hoc multiple comparison tests. The percentage of failure type was calculated. Data from SEM analysis were compared by Friedman and Kruskal-Wallis tests (alpha = 0.05). Results: The mean bond strength was significantly higher in the negative control group as compared with the other groups (P < .05). In all groups, the most frequent type of failure was adhesive. Overall, apical and middle regions presented a lower density of resin tags than the coronal region (P < .05). Conclusions: The push-out bond strength was not affected by sealer or region. The canal region affected significantly the resin tag morphology and density at the bonding interface. (J Endod 2011;37:531-537)

Influence of endodontic sealers on the bond strength of carbon fiber posts

Objective: The aim of this study was to verify the influence of endodontic sealers on the bond strength of an adhesive system and a resin cement used for carbon posts cementation. Methods: Thirty extracted human premolars were instrumented and randomly divided into three groups according to the tested sealer: EndoFill, Sealapex, or EndoREZ. Specimens were stored at 37 degrees C. After 48 h, half of specimens were prepared to receive the post and the others after 7 days. The posts were cemented with Adper Single Bond/Rely X ARC and stored in distilled water at 37 degrees C for 7 days. After this period, the specimens were sectioned in three slices (coronal, middle, and apical). The push-out test was performed in a universal machine and the debonded area was examined in a stereomicroscope. Results: Data were submitted ANOVA and Tukey test (alpha = 0.05). The EndoFill showed lower bond strength than other sealers (p < 0.01). The EndoREZ sealer was statistically greater than other groups for coronal and middle portions and similar for apical portion (P > 0.05). Coronal and middle portions showed the best results for all groups, mainly when the canal preparation was performed after 48 h (p < 0.01). Mixed failure occurs with more frequency (55.6%) followed by failure in adhesive-dentin interface (34.4%) and adhesive-post interface (10.0%). Conclusion: The use of EndoREZ sealer promoted higher bond strength in root coronal and middle portions when carbon post was fixed with a resin cement. (C) 2007 Wiley Periodicals, Inc.

Microtensile Bond Strength of Glass Fiber Posts Cemented with Self-adhesive and Self-etching Resin Cements

Purpose: To evaluate the bond strength of glass fiber posts to intraradicular dentin when cemented with self-etching and self-adhesive resin cements. Materials and Methods: Forty-eight single-rooted human teeth were decoronated, endodontically treated, post-space prepared and divided into 8 groups (n = 6). The glass fiber posts used were: Exacto (EA) (Angelus) and everStick (ES) (StichTeck), which were cemented with two self-adhesive resin cements: BisCem (BIS) (Bisco) and Rely-X Unicem (UNI) (3M/ESPE), and two self-etching resin cements: Esthetic Cementing System NAC100 (NAC) (Kuraray) and Panavia-F (PAN) (Kuraray). Specimens were thermocycled between 5 degrees C and 55 degrees C for 1000 cycles and stored in water at 37 degrees C for 1 month. Four 1-mm-thick (in cross section) rods were obtained from the cervical region of the roots. Specimens were then subjected to microtensile testing in a special machine (BISCO; Schaumburg, IL, USA) at a crosshead speed of 0.5 mm/min. Microtensile bond strength (mu TBS) data were analyzed with two-way ANOVA and Tukey`s tests. Results: Means (and SD) of mu TBS (MPa) were: EA/PAN: 10.3 (4.1), EA/NAC: 14 (5.1) EA/BIS: 16.4 (4.8), EA/UNI: 19.8 (5.1), ES/PAN: 25.9 (6.1), ES/NAC: 29.1 (7), ES/BIS: 28.9 (6), ES/UNI: 30.5 (6.6). ANOVA indicated significant differences among the groups (p < 0.001). Mean mu TBS values obtained with ES post were significantly higher than those obtained with EA (p < 0.001). For EA, Tukey`s test indicated that higher mu TBS means were obtained with the self-adhesive resin cements (BIS and UNI), which were statistically significantly different (p < 0.05) from values obtained with the self-etching resin cements (PAN and NAC). Different cements had no significant effects on the bond strength values of ES post (p > 0.05). mu TBS values obtained with ES post were significantly higher than those obtained with EA post irrespective of the resin cement used. Conclusion: everStick posts resulted in the highest mean mu TBS values with all cements. Self-adhesive cements performed well in terms of bond strength.