Effect of different cleansers on the weight and ion release of removable partial denture: an in vitro study

OBJECTIVE: Removable partial dentures (RPD) require different hygiene care, and association of brushing and chemical cleansing is the most recommended to control biofilm formation. However, the effect of cleansers has not been evaluated in RPD metallic components. The aim of this study was to evaluate in vitro the effect of different denture cleansers on the weight and ion release of RPD. MATERIAL AND METHODS: Five specimens (12x3 mm metallic disc positioned in a 38x18x4 mm mould filled with resin), 7 cleanser agents [Periogard (PE), Cepacol (CE), Corega Tabs (CT), Medical Interporous (MI), Polident (PO), 0.05% sodium hypochlorite (NaOCl), and distilled water (DW) (control)] and 2 cobalt-chromium alloys [DeguDent (DD), and VeraPDI (VPDI)] were used for each experimental situation. One hundred and eighty immersions were performed and the weight was analyzed with a high precision analytic balance. Data were recorded before and after the immersions. The ion release was analyzed using mass spectrometry with inductively coupled plasma. Data were analyzed by two-way ANOVA and Tukey HSD post hoc test at 5% significance level. RESULTS: Statistical analysis showed that CT and MI had higher values of weight loss with higher change in VPDI alloy compared to DD. The solutions that caused more ion release were NaOCl and MI. CONCLUSIONS: It may be concluded that 0.05% NaOCl and Medical Interporous tablets are not suitable as auxiliary chemical solutions for RPD care.

pH, Calcium Ion Release, and Setting Time of an Experimental Mineral Trioxide Aggregate-based Root Canal Sealer

Introduction: An experimental mineral trioxide aggregate sealer (MTAS) has been developed for use as a root canal sealer. The aim of this study was to evaluate the setting time, pH, and calcium ion release of MTAS compared with white Portland cement (CPB-40; Votorantin Cimentos, Camargo Correa SA, Pedro Leopoldo, MG, Brazil), white MTA Angelus (MTA; Angelus, Londrina, PR, Brazil), and AH Plus (Dentsply DeTrey, Konstanz, Germany). Methods: For the evaluation of setting time, each material was analyzed using Gilmore-type needles. Polyethylene tubes with the materials were immersed in distilled water for the measurement of pH (digital pH meter) and calcium release (atomic absorption spectrophotometry). The evaluations were performed at 3, 6, 12, 24, and 48 hours and 7, 14, and 28 days. Data were analyzed by analysis of variance and the Tukey test at 5% significance level. Results: MTAS showed higher calcium release at all experimental periods, a greater increase in pH up to 48 hours and the longest setting time. Conclusions: MTAS presented favorable properties for its indication as a root canal sealer. (J Endod 2011;37:844-846)

Evaluation of pH and Calcium Ion Release of Root-end Filling Materials Containing Calcium Hydroxide or Mineral Trioxide Aggregate

Introduction: To evaluate calcium ion release and pH of Sealer 26 (S26) (Dentsply, Rio de Janeiro, RJ, Brazil), white mineral trioxide aggregate (MTA), Endo CPM Sealer (CPM1) (EGEO SRL Bajo licencia MTM Argentina SA, Buenos Aires, Argentina), Endo CPM Sealer in a thicker consistency (CPM 2), and zinc oxide and eugenol cement (ZOE). Methods: Material samples (n = 10) were placed in polyethylene tubes and immersed in 10 mL of distilled water. After 3, 6,12,24, and 48 hours and 7,14, and 28 days, the water pH was determined with a pH meter, and calcium release was assessed by atomic absorption spectrophotometry. An empty tube was used as the control group. Results: The control group presented a pH value of 6.9 at all studied periods and did not show the presence of calcium ion. S26 presented greater hydroxyl ion release up to 12 hours (p < 0.05). From 24 hours until 28 days, S26, MTA, CPM1, and CPM2 had similar results. in ail periods, ZOE presented the lowest hydroxyl ion release. CPM1, followed by CPM2, released the most calcium ions until 24 hours (p < 0.05). Between 48 hours and 7 days, CPM1 and CPM2 had the highest release. A greater calcium ion release was observed for CPM2, followed by CPM1 at 14 days and for S26, CPM1, and CPM2 at 28 days. ZOE released the least calcium ions in all periods. Conclusion: Sealer 26, MTA, and Endo CPM sealer at normal or thicker consistency release hydroxyl and calcium ions. Endo CPM sealer may be an alternative as root-end filling material. (J Endod 2009;35:1418-1421)

Evaluation of pH and calcium ion release of new root-end filling materials

Objective. The purpose of this study was to evaluate the pH and calcium ion release of 6 materials used for root-end filling and perforation repair. Study design. Gray ProRoot MTA, gray MTA-Angelus, white MTA-Angelus, and CPM were compared to 2 experimental ones: MTA-exp, also based in Portland cement with a modified mixing liquid, and MBPc, an epoxy-resin based cement containing calcium hydroxide. After 3, 24, 72, and 168 hours the water in which each sample had been immersed was tested to determine the ph and calcium ion release. Results. All the analyzed materials showed alkaline pH and capacity to release calcium ions; however, a tendency of reduction of these characteristics was noted for all the analyzed materials, except for the MBPc, which showed a slight increase of pH among the 3 initial periods. Conclusion. The results suggest that all materials investigated presented alkaline pH and ability of release of calcium ions. (Oral Surg Oral Med Oral Pathol Oral Radiol Endod 2009; 108: 135-139)

Evaluation of pH and Calcium Ion Release of Calcium Hydroxide Pastes Containing Different Substances

Introduction: The objective of this study was to evaluate the pH and calcium ion release of calcium hydroxide pastes associated with different substances. Methods: Forty acrylic teeth with simulated root canals were divided into 4 groups according to the substance associated to the calcium hydroxide paste: chlorhexidine (CHX) in 2 formulations (1% solution and 2% gel), Casearia sylvestris Sw extract, and propylene glycol (control). The teeth with pastes and sealed coronal accesses were immersed in 10 mL deionized water. After 10 minutes, 24 hours, 48 hours, and 7, 15, and 30 days, the teeth were removed to another container, and the liquid was analyzed. Calcium ion release was measured by atomic absorption spectrophotometry, and pH readings were made with a pH meter. Data were analyzed statistically by analysis of variance and Tukey test (alpha = 0.05). Results: Calcium analysis revealed significant differences (P < .05) for 1% CHX solution and 2% CHX gel at 10 minutes. After 24 hours, 2% CHX gel x Control and 2% CHX gel x 1% CHX solution differed significantly (P < .05). After 48 hours, there were significant differences (P < .05) for 2% CHX gel x Control and Extract x Control. No differences (P > .05) were observed among groups in the other periods. Regarding the pH, there were significant differences (P < .05) for 2% CHX gel x Control and 2% CHX gel x 1% CHX solution after 48 hours and for 2% CHX gel x Control after 15 days. In the other periods, no differences (P > .05) were observed among groups. Conclusions: All pastes behaved similarly in terms of pH and calcium ion release in the studied periods. (J Endod 2009;35:1274-1277)

Understanding the impact of divalent cation substitution on hydroxyapatite: An in vitro multiparametric study on biocompatibility

Hydroxyapatite (HA), a stable and biocompatible material for bone tissue therapy, may present a variable stoichiometry and accept a large number of cationic substitutions. Such substitutions may modify the chemical activity of HA surface, with possible impact on biocompatibility. In this work, we assessed the effects of calcium substitution with diverse divalent cations (Pb(2+), Sr(2+), Co(2+), Zn(2+), Fe(2+), Cu(2+), or Mg(2+)) on the biological behavior of HA. Physicochemical analyses revealed that apatite characteristics related to crystallinity and calcium dissolution/uptake rates are very sensitive to the nature of cationic substitution. Cytocompatibility was evaluated by mitochondrial activity, membrane integrity, cell density, proapoptotic potential, and adhesion tests. With the exception of Zn-HA, all the substituted HAs induced some level of apoptosis. The highest apoptosis levels were observed for Mg-HA and Co-HA. Cu-HA was the only material to impair simultaneously mitochondrial activity, membrane integrity, and cell density. The highest relative cell densities after exposure to the modified HAs were observed for Mg-HA and Zn-HA, while Co-HA significantly improved cell adhesion onto HA surface. These results show that changes on surface dissolution caused by cationic substitution, as well as the increase of metal species released to biological media, were the main responsible factors related to alterations on HA biocompatibility. (C) 2011 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 98A: 351-358, 2011.

Evaluation of the physical and chemical properties of two commercial and three experimental root-end filling materials

Objective. The aim of this study was to evaluate the pH, calcium release, setting time, and solubility of two commercially available mineral trioxide aggregate (MTA) cements (white MTA Angelus and MTA Bio), and of three experimental cements (light-cured MTA, Portland cement with 20% bismuth oxide and 5% calcium sulfate, and an epoxy resin-based cement). Study design. For evaluation of pH and calcium ion release, polyethylene tubes with 1.0 mm internal diameter and 10.0 mm length were filled with the cements and immediately immersed in flasks containing 10 mL deionized water. After 3, 24, 72, and 168 hours, the tubes were removed and the water from the previous container was measured for its pH and calcium content with a pH meter and an atomic absorption spectrophotometer. For analysis of the setting time, Gilmore needles weighing 100 g and 456.5 g were used, in accordance with the American Society for Testing and Materials specification no. C266-03. Solubility of each cement was also tested. Results. All the cements were alkaline and released calcium ions, with a declining trend over time. After 3 hours, Portland cement + bismuth oxide and MTA Bio had the highest pH and light-cured MTA the lowest. After 1 week, MTA Bio had the highest pH and light-cured MTA and epoxy resin-based cement the lowest. Regarding calcium ion release, after 3 hours, Portland cement + bismuth oxide showed the highest release. After 1 week, MTA Bio had the highest. Epoxy resin-based cement and light-cured MTA had the lowest calcium release in all evaluation periods. Regarding setting times, white MTA Angelus and MTA Bio had the shortest, Portland cement + bismuth oxide had an intermediate setting time, and the epoxy resin-based cement had the longest. The materials that showed the lowest solubility values were the epoxy resin-based cement, Portland cement + bismuth oxide, and light-cured MTA. The highest solubility values were presented in white MTA Angelus and MTA Bio. Conclusions. The white MTA Angelus and MTA Bio had the shortest setting times, higher pH and calcium ion release, and the highest solubility. In contrast, the epoxy resin-based cement and light-cured MTA showed lower values of solubility, pH, and calcium ion release. (Oral Surg Oral Med Oral Pathol Oral Radiol Endod 2010; 110: 250-256)

Influence of Calcium Hydroxide Association on the Physical Properties of AH Plus

Introduction: This study evaluated in vitro the radiopacity, setting time, flow, film thickness, solubility, and dimensional changes of AH Plus sealer pure (Dentsply De Trey Gmbh, Konstanz, Germany) and containing 5% and 10% of calcium hydroxide. Methods: The study was performed according to the requirements of the ISO 6876:2001 standard and the American National Standards Institute/American Dental Association (ANSI/ADA)`s Specification No. 57. The following tests were performed: setting time, flow, film thickness, dimensional stability, radiopacity, and solubility. Data were analyzed statistically by analysis of variance and the Tukey tests with a significance level of 5%. Results: The addition of 5% or 10% calcium hydroxide to AH Plus sealer did not alter significantly the radiopacity or setting time values (p > 0.05). Adding 10% calcium hydroxide reduced the flow compared with pure AH Plus and AH Plus/5% calcium hydroxide. The addition of 5% and 10% calcium hydroxide increased the solubility and expansion of AH Plus. All materials presented expansion valued above those recommended by the ADA. The addition of calcium hydroxide to the sealer resulted in greater film thickness. Conclusions: The addition of 5% calcium hydroxide did not affect most physical properties of AH Plus sealer. (J Endod 2010;36:1048-1051)

The Influence of Calcium Chloride on the Setting Time, Solubility, Disintegration, and pH of Mineral Trioxide Aggregate and White Portland Cement with a Radiopacifier

This study evaluated the influence of addition of 10% calcium chloride (CaCl(2)) on the setting time, solubility, disintegration, and pH of white MTA (WMTA) and white Portland cement (WPC). A test of the setting time was performed following the #57 ADA specifications and a test of the final setting time according to the ASTM. For the solubility tests disintegration and pH, Teflon rings were filled with the cements and weighed after setting. After 24 h in a desiccator, they were once again weighed. Thereafter, they were immersed in MiliQ water for 24 and 72 h and 7, 14, and 28 days, with maintenance in the desiccator and weighing between periods. The pH of water in which the rings were immersed was measured immediately after contact with them and in the other periods. The addition of CaCl(2) provided a significant reduction (50%) in the initial setting time of cements. The final setting time of WMTA was reduced in 35.5% and the final setting time of WPC in 68.5%. The WMTA with CaCl(2) absorbed water and gained weight with time, except for in the 24-h period. The addition of CaCl(2) to the WPC reduced its solubility. The addition of CaCl(2) increased the pH of WMTA in the immediate period and at 24 and 72 h and for WPC in the immediate period and at 24 h. The addition of CaCl(2) to WMTA and WPC reduced the setting times and solubility of both and increased the pH of cements in the initial periods. (J Endod 2009;35:550-554)

Evaluation of physicochemical properties of four root canal sealers

P>Aim To assess the physicochemical properties and the surface morphology of AH Plus, GuttaFlow, RoekoSeal and Activ GP root canal sealers. Methodology Five samples of each material were evaluated for setting time, dimensional alteration, solubility and radiopacity tests, according to ANSI/ADA Specification 57. A total of 50 mL of deionized distilled water from the solubility tests were used to measure the metal solubility by atomic absorption spectrometry. The morphologies of the external surface and the cross-section of the samples were analysed by means of a scanning electron microscope (SEM). Statistical analysis was performed by using one-way anova and post hoc Tukey-Kramer tests with the null hypothesis set as 5%. Results AH Plus had the longest setting time (580.6 +/- 3.05 min) (P < 0.05). Activ GP did not have a mean value on the radiopacity and solubility tests (1.31 +/- 0.35 mm and 11.8 +/- 0.43%, respectively) in accordance with ANSI/ADA, being significantly different from the other materials (P < 0.05), which had mean values for these tests in accordance with the ADA`s requirements. GuttaFlow was the only sealer that conformed to the Specification 57 concerning the dimensional alteration test (0.44 +/- 0.16%) (P < 0.05). The spectrometry test revealed significant Ca2+, K+, Zn2+ ion release from Activ GP sealer (32.57 +/- 5.0, 1.57 +/- 0.22 and 8.20 +/- 1.74 mu g mL-1, respectively). In SEM analysis, the loss of matrix was evident and the filler particles were more distinguishable in all groups. Conclusions The setting time of all sealers was in accordance with ANSI/ADA`s requirements. Activ GP did not fulfill ANSI/ADA`s protocols regarding radiopacity, dimensional alteration and solubility. GuttaFlow was the only sealer that conformed to the Specification 57 in all tests. SEM analysis revealed that the surfaces of all sealers had micromorphological changes after the solubility test.

A comparative study of physicochemical properties of AH Plus, Epiphany, and Epiphany SE root canal sealers

P>Aim To assess the physicochemical properties and the surface morphology of AH Plus, Epiphany, and Epiphany SE root canal sealers. Methodology Five samples of each material were employed for each test according to ANSI/ADA specification 57. The samples were assigned to four groups: (i) AH Plus; (ii) Epiphany; (iii) Epiphany + Thinning Resin; (iv) Epiphany SE. The distilled water used during the solubility test was submitted to spectrometry to verify the release of calcium ions. The morphologies of the external surface and the cross-section of the samples were analysed by means of a scanning electron microscope (SEM). Statistical analysis was performed by using One-Way anova and post hoc Tukey-Kramer tests with the null hypothesis set as 5%. Results Setting time, flow and radiopacity results were in accordance with ANSI/ADA requirements whereas the dimensional change of all sealers and solubility of Epiphany did not fulfil ANSI/ADA protocols. AH Plus and Epiphany SE were similar in terms of flow, radiopacity, solubility and dimensional change. The spectrometry test revealed significant calcium ion release from Epiphany with and without the thinning resin. SEM analysis revealed essentially a homogeneous surface with compact layer and some rough areas. Conclusions Setting time, flow, and radiopacity tests conformed to ANSI/ADA standardization. The dimensional change in all groups and the solubility of Epiphany were greater than values considered acceptable, with higher amounts of calcium ion release. Epiphany SE revealed more organized, compacted, and homogeneous polymers in a reduced resin matrix when compared with the other groups.

Fluoride release profile of a nanofilled resin-modified glass ionomer cement

The present study aimed to compare the fluoride (F-) release pattern of a nanofilled resin-modified glass ionomer cement (GIC) (Ketac N100 - KN) with available GICs used in dental practice (resin-modified GIC - Vitremer - V; conventional GIC - Ketac Molar - KM) and a nanofilled resin composite (Filtek Supreme - RC). Discs of each material (n=6) were placed into 4 mL of deionized water in sealed polyethylene vials and shaken, for 15 days. F- release (μg F-/cm²) was measured each day using a fluoride-ion specific electrode. Cumulative F- release means were statistically analyzed by linear regression analysis. In order to analyze the differences among materials and the influence of time in the daily F- release, 2-way ANOVA test was performed (α=0.05). The linear fits between the cumulative F- release profiles of RC and KM and time were weak. KN and V presented a strong relationship between cumulative F- release and time. There were significant differences between the daily F- release overtime up to the third day only for GICs materials. The daily F- release means for RC were similar overtime. The results indicate that the F- release profile of the nanofilled resin-modified GIC is comparable to the resin-modified GIC.

The inducing NO-vasodilation by chemical reduction of coordinated nitrite ion in cis-[Ru(NO(2))L(bpy)(2)](+) complex

The synthesis of [Ru(NO(2)) L(bpy)(2)](+) (bpy = 2,2'-bipyridine and L = pyridine (py) and pyrazine (pz)) can be accomplished by addition of [Ru(NO) L(bpy) 2](PF(6))(3) to aqueous solutions of physiological pH. The electrochemical processes of [Ru(NO2) L(bpy) 2]+ in aqueous solution were studied by cyclic voltammetry and differential pulse voltammetry. The anodic scan shows a peak around 1.00 V vs. Ag/AgCl attributed to the oxidation process centered on the metal ion. However, in the cathodic scan a second peak around-0.60 V vs. Ag/AgCl was observed and attributed to the reduction process centered on the nitrite ligand. The controlled reduction potential electrolysis at-0.80 V vs. Ag/AgCl shows NO release characteristics as judged by NO measurement with a NO-sensor. This assumption was confirmed by ESI/MS(+) and spectroelectrochemical experiment where cis-[Ru(bpy)(2)L(H(2)O)](2+) was obtained as a product of the reduction of cis-[Ru(II)(NO(2)) L(bpy)(2)](+). The vasorelaxation observed in denuded aortic rings pre-contracted with 0.1 mu mol L(-1) phenylephrine responded with relaxation in the presence of cis-[RuII(NO2) L(bpy) 2]+. The potential of rat aorta cells to metabolize cis-[RuII(NO(2)) L(bpy)(2)](+) was also followed by confocal analysis. The obtained results suggest that NO release happens by reduction of cis-[RuII(NO(2)) L(bpy)(2)](+) inside the cell. The maximum vasorelaxation was achieved with 1 x 10(-5) mol L(-1) of cis-[RuII(NO(2)) L(bpy)(2)](+) complex.

An in vitro comparison of nickel and chromium release from brackets

This study aimed at comparing amounts of nickel (Ni) and chromium (Cr) released from brackets from different manufacturers in simulated oral environments. 280 brackets were equally divided into 7 groups according to manufacturer. 6 groups of brackets were stainless steel, and 1 group of brackets was made of a cobalt-chromium alloy with low Ni content (0.5%). International standard ISO 10271/2001 was applied to provide test methods. Each bracket was immersed in 0.5 ml of synthetic saliva (SS) or artificial plaque fluid (PF) over a period of 28 days at 37ºC. Solutions were replaced every 7 days, and were analyzed by spectrometry. The Kruskal-Wallis test was applied. Amounts of Ni release in SS (µg L-1 per week) varied between groups from "bellow detection limits" to 694, and from 49 to 5,948.5 in PF. The group of brackets made of cobalt-chromium alloy, with the least nickel content, did not release the least amounts of Ni. Amounts of Cr detected in SS and in PF (µg L-1 per week) were from 1 to 10.4 and from 50.5 to 8,225, respectively. It was therefore concluded that brackets from different manufacturers present different corrosion behavior. Further studies are necessary to determine clinical implications of the findings.

Adsorption of amyloglucosidase from Aspergillus niger NRRL 3122 using ion exchange resin

Amyloglucosidase enzyme was produced by Aspergillus niger NRRL 3122 from solid-state fermentation, using deffated rice bran as substrate. The effects of process parameters (pH, temperature) in the equilibrium partition coefficient for the system amyloglucosidase - resin DEAE-cellulose were investigated, aiming at obtaining the optimum conditions for a subsequent purification process. The highest partition coefficients were obtained using 0.025M Tris-HCl buffer, pH 8.0 and 25ºC. The conditions that supplied the highest partition coefficient were specified, the isotherm that better described the amyloglucosidase process of adsorption obtained. It was observed that the adsorption could be well described by Langmuir equation and the values of Qm and Kd estimated at 133.0 U mL-1 and 15.4 U mL-1, respectively. From the adjustment of the kinetic curves using the fourth-order Runge-Kutta algorithm, the adsorption (k1) and desorption (k2) constants were obtained through optimization by the least square procedure, and the values calculated were 2.4x10-3 mL U-1 min-1 for k1 and 0.037 min-1 for k2 .