Laccase-assisted approach to graft multifunctional materials of interest: keratin-EC based novel composites and their characterisation

This study focuses on the evaluation of raw keratin as a potential material to develop composites with novel characteristics. Herein, we report a mild and eco-friendly fabrication of in-house extracted feather keratin-based novel enzyme assisted composites consisting of ethyl cellulose (EC) as a backbone material. A range of composites between keratin and EC using different keratin: EC ratios were prepared and characterised. Comparing keratin to the composites, the FT-IR peak at 1,630 cm-1 shifted to a lower wavenumber of 1,610 cm-1 in keratin-EC which typically indicates the involvement of β-sheet structures of the keratin during the graft formation process. SEM analysis revealed that the uniform dispersion of the keratin increases the area of keratin-EC contact which further contributes to the efficient functionality of the resulting composites. In comparison to the pristine keratin and EC, a clear shift in the XRD peaks was also observed at the specific region of 2-Theta values of keratin-g-EC. The thermo- mechanical properties of the composites reached their highest levels in comparison to the keratin which was too fragile to be measured for its mechanical properties. Considerable improvement in the water contact angle and surface tension properties was also recorded.

Laccase from Aspergillus niger: A novel tool to graft multifunctional materials of interests and their characterization

In the present study, we propose a green route to prepare poly(3-hydroxybutyrate) [(P(3HB)] grafted ethyl cellulose (EC) based green composites with novel characteristics through laccase-assisted grafting. P(3HB) was used as a side chain whereas, EC as a backbone material under an ambient processing conditions. A novel laccase obtained from Aspergillus niger through its heterologous expression in Saccharomyces cerevisiae was used as a green catalyst for grafting purposes without the use of additional initiator and/or cross-linking agents. Subsequently, the resulting P(3HB)-g-EC composites were characterized using a range of analytical and imagining techniques. Fourier transform infrared spectroscopy (FT-IR) spectra showed an increase in the hydrogen-bonding type interactions between the side chains of P(3HB) and backbone material of EC. Evidently, X-ray diffraction (XRD) analysis revealed a decrease in the crystallinity of the P(3HB)-g-EC composites as compared to the pristine individual polymers. A homogeneous P(3HB) distribution was also achieved in case of the graft composite prepared in the presence of 2,2'-azino-bis(3-ethylbenzothiazoline-6-sulphonic acid) (ABTS) as a mediator along with laccase as compared to the composite prepared using pure laccase alone. A substantial improvement in the thermal and mechanical characteristics was observed for grafted composites up to the different extent as compared to the pristine counterparts. The hydrophobic/hydrophilic properties of the grafted composites were better than those of the pristine counterparts.