The incorporation of construction and demolition wastes as recycled mixed aggregates in non-structural concrete precast pieces

Concern for the environment has lately heightened awareness about the need for recycling in the construction industry. However, some standards, such as the Spanish standard, only accept the recycling of aggregates derived from concrete, which limits the extensive use of construction and demolition waste, which are produced in much bigger volumes. The aim of this work was to explore the possibility of using recycled mixed aggregates (RMA) in the preparation of precast non-structural concretes. To that end different percentages of natural aggregate were replaced by RMA in non-structural elements (25, 50, 75 and 100%). Contents of cement, water, and the dosages commonly used by companies were unchanged by the introduction of RMA. The characterization of the prepared elements has been done using the specific tests for each type of non-structural element (terrazzo for indoor use, hollow tiles, kerbstones and paving blocks): compression and flexural strength, water absorption, dimensional tolerances, abrasion and slipping resistance. The paving blocks, kerbstones, and hollow tiles prepared were tested for 360 days. The stability of the tested properties confirmed the possibility of using these wastes on an industrial scale satisfying the standard requirements. However, the surface of terrazzo with RMA is not as good as that prepared with natural aggregate.

Radiological impact of cement, concrete and admixtures in Spain

It has been analyzed samples of portland cement (PC) with and without admixtures, samples of calcium aluminate cement (CAC) with different content of Al2O3 and specimens of concrete made with PC and CAC using High Resolution Gamma Spectrometry. The activity concentration index (I) is much less than 0.5 mSv y-1 for all the concrete specimens according to the Radiation protection document 112 of the European Commission. The PC without admixtures (CEM I 52,5 R) and the PC with addition of limestone (CEM II/BL 32,5 N) also have an I value much lower than 0.5 and the PC with the addition of fly ash and blast furnace slag (CEM IV/B (V) 32,5 N and III/A 42.5 N/SR) have an I value close to 0.6. The I value of the CAC used in the manufacture of structural precast concrete is of the order of 1 mSv y-1. Some of the CAC used in refractory concrete reaches a value close to 2 mSv y-1.

Uso potencial de ceniza de lodo de depuradora como sustitución de árido fino en bloques de hormigón prefabricados

El presente artículo se centra en la valorización de las cenizas de lodo de depuradora adicionadas en bloques de hormigón prefabricados, por tanto, en una matriz a base de cemento Portland con características particulares (consistencia seca). Se realiza una experiencia piloto mediante la fabricación de bloques en una planta industrial local, utilizando mezclas con porcentajes de sustitución de árido fino del 5, 10 y 15% por cenizas de lodo de depuradora, cuyos resultados se compararán con bloques de referencia (sin adición). Los ensayos aplicados son los preceptivos para su comercialización según normativa europea (marcado CE), lo que permitirá igualmente comprobar las características físicas y mecánicas de los hormigones. Los resultados obtenidos son prometedores: la utilización de este residuo permitiría su comercialización, mejora características de los bloques como la resistencia a compresión, y permitiría reducir un gran volumen de material utilizado habitualmente como materia prima y consumir un residuo destinado a vertedero.

Valorización de cenizas de lodo de depuradora como componente de hormigones para prefabricados

Se plantea la combinación binaria y ternaria de cenizas de lodo de depuradora (CLD) con ceniza volante, polvo de mármol y ceniza de cáscara de arroz, como sustitución parcial o como adición respecto al cemento Portland en hormigones, con una dosificación similar a la utilizada en la prefabricación de bloques (consistencia muy seca). Se llevaron a cabo ensayos físico-mecánicos sobre probetas de mortero y hormigón con edades de curado de 28 y 90 días: densidad, absorción y resistencia a compresión. Se comprueba que la sustitución de cemento por CLD supone una disminución de la densidad y de la resistencia respecto a la muestra patrón, sin embargo, las combinaciones con otros residuos mejoran notablemente las características de los materiales cementantes. La adición de CLD proporcionó densidades y resistencias similares a la muestra de control y reduce significativamente la absorción de agua.