Spherical carbons: Synthesis, characterization and activation processes

Spherical carbons have been prepared through hydrothermal treatment of three carbohydrates (glucose, saccharose and cellulose). Preparation variables such as treatment time, treatment temperature and concentration of carbohydrate have been analyzed to obtain spherical carbons. These spherical carbons can be prepared with particle sizes larger than 10 μm, especially from saccharose, and have subsequently been activated using different activation processes (H3PO4, NaOH, KOH or physical activation with CO2) to develop their textural properties. All these spherical carbons maintained their spherical morphology after the activation process, except when KOH/carbon ratios higher than 4/1 were used, which caused partial destruction of the spheres. The spherical activated carbons develop interesting textural properties with the four activating agents employed, reaching surface areas up to 3100 m2/g. Comparison of spherical activated carbons obtained with the different activating agents, taking into account the yields obtained after the activation process, shows that phosphoric acid activation produces spherical activated carbons with higher developed surface areas. Also, the spherical activated carbons present different oxygen groups’ content depending on the activating agent employed (higher surface oxygen groups content for chemical activation than for physical activation).

Influence of the Difference Between Corneal and Refractive Astigmatism on LASIK Outcomes Using Solid-State Technology

Purpose: To evaluate the influence of the difference between preoperative corneal and refractive astigmatism [ocular residual astigmatism (ORA)] on outcomes obtained after laser in situ keratomileusis (LASIK) surgery for correction of myopic astigmatism using the solid-state laser technology. Methods: One hundred one consecutive eyes with myopia or myopic astigmatism of 55 patients undergoing LASIK surgery using the Pulzar Z1 solid-state laser (CustomVis Laser Pty Ltd, currently CV Laser) were included. Visual and refractive changes at 6 months postoperatively and changes in ORA and anterior corneal astigmatism and posterior corneal astigmatism (PCA) were analyzed. Results: Postoperatively, uncorrected distance visual acuity improved significantly (P < 0.01). Likewise, refractive cylinder magnitude and spherical equivalent were reduced significantly (P < 0.01). In contrast, no significant changes were observed in ORA magnitude (P = 0.81) and anterior corneal astigmatism (P = 0.12). The mean overall efficacy and safety indices were 0.96 and 1.01, respectively. These indices were not correlated with preoperative ORA (r = −0.15, P = 0.15). Furthermore, a significant correlation was found between ORA (r = 0.81, P < 0.01) and PCA postoperatively, but not preoperatively (r = 0.12, P = 0.25). Likewise, a significant correlation of ORA with manifest refraction was only found postoperatively (r = −0.38, P < 0.01). Conclusions: The magnitude of ORA does not seem to be a predictive factor of efficacy and safety of myopic LASIK using a solid-state laser platform. The higher relevance of PCA after surgery in some cases may explain the presence of unexpected astigmatic residual refractive errors.

Thermodynamic, surface and structural properties of liquid Co-Si alloys

The knowledge of thermophysical properties of liquid Co-Si alloys is a key requirement for manufacturing of composite materials by infiltration method. Despite this need, the experimental and predicted property data of the Co-Si system are scarce and often inconsistent between the various sources. In the present work the mixing behaviour of Co-Si melts has been analysed through the study of the concentration dependence of various thermodynamic, surface (surface tension and surface composition) and structural properties (concentration fluctuations in the long-wavelength limit and chemical short-range order parameter) in the framework of the Compound Formation Model (CFM) and Quasi Chemical Approximation for regular solutions (QCA). In addition, the surface tension of the Co22·5Si77.5 (in at%) eutectic alloy, that is proposed to be used as the infiltrant, has been measured by the pendant drop method at temperatures ranging from 1593 to 1773 K. The results obtained were discussed with respect to both, temperature and concentration, and subsequently compared with the model predictions and literature data.