Electrooxidation methods to produce pseudocapacitance-containing porous carbons

Surface oxygen groups play a key role on the performance of porous carbon electrodes for electrochemical capacitors in aqueous media. The electrooxidation method in NaCl electrolyte using a filter press cell and dimensionally stable anodes is proposed as a viable process for the generation of oxygen groups on porous carbon materials. The experimental set-up is so flexible that allows the easy modification of carbon materials with different configurations, i.e. cloths and granular, obtaining different degrees of oxidation for both conformations without the requirement of binders and conductivity promoters. After the electrooxidation method, the attained porosity is maintained between 90 and 75% of the initial values. The surface oxygen groups generated can increase the capacitance up to a 30% when compared to the pristine material. However, a severe oxidation is detrimental since it may decrease the conductivity and increase the resistance for ion mobility.

CO2 adsorption on crystalline graphitic nanostructures

CO2 adsorption has been measured in different types of graphitic nanostructures (MWCNTs, acid treated MWCNTs, graphene nanoribbons and pure graphene) in order to evaluate the effect of the different defective regions/conformations in the adsorption process, i.e., sp3 hybridized carbon, curved regions, edge defects, etc. This analysis has been performed both in pure carbon and nitrogen-doped nanostructures in order to monitor the effect of surface functional groups on surface created after using different treatments (i.e., acid treatment and thermal expansion of the MWCNTs), and study their adsorption properties. Interestingly, the presence of exposed defective regions in the acid treated nanostructures (e.g., uncapped nanotubes) gives rise to an improvement in the amount of CO2 adsorbed; the adsorption process being completely reversible. For N-doped nanostructures, the adsorption capacity is further enhanced when compared to the pure carbon nanotubes after the tubes were unzipped. The larger proportion of defect sites and curved regions together with the presence of stronger adsorbent–adsorbate interactions, through the nitrogen surface groups, explains their larger adsorption capacity.

Electrospinning of silica sub-microtubes mats with platinum nanoparticles for NO catalytic reduction

Silica sub-microtubes loaded with platinum nanoparticles have been prepared in flexible non-woven mats using co-axial electrospinning technique. A partially gelated sol made from tetraethyl orthosilicate was used as the silica precursor, and oil was used as the sacrificial template for the hollow channel generation. Platinum has been supported on the wall of the tubes just adding the metallic precursor to the sol–gel, thus obtaining the supported catalyst by one-pot method. The silica tubes have a high aspect ratio with external/internal diameters of 400/200 nm and well-dispersed platinum nanoparticles of around 2 nm. This catalyst showed a high NO conversion with very high selectivity to N2 at mild conditions in the presence of excess oxygen when using C3H6 as reducing agent. This relevant result reveals the potential of this technique to produce nanostructured catalysts onto easy to handle conformations.