4 resultados para Split tensile strength
em Universidad de Alicante
Resumo:
Edible active films based on sodium caseinate (SC) and calcium caseinate (CC) plasticized with glycerol (G) at three different concentrations and carvacrol (CRV) as active agent were prepared by solvent casting. Transparent films were obtained and their surfaces were analysed by optical microscopy and scanning electron microscopy (SEM). The influence of the addition of three different plasticizer concentrations was studied by determining tensile properties, while Fourier transformed infrared spectroscopy (FTIR) and thermogravimetric analysis (TGA) were used to evaluate the structural and thermal behavior of such films. The addition of glycerol resulted in a reduction in the elastic modulus and tensile strength, while some increase in the elongation at break was observed. In general terms, SC films showed flexibility higher than the corresponding CC counterparts. In addition, the presence of carvacrol caused further improvements in ductile properties suggesting the presence of stronger interactions between the protein matrix and glycerol, as it was also observed in thermal degradation studies. FTIR spectra of all films showed the characteristic bands and peaks corresponding to proteins as well as to primary and secondary alcohols. In summary, the best results regarding mechanical and structural properties for caseinates-based films containing carvacrol were found for the formulations with high glycerol concentrations.
Resumo:
In this work, particleboards manufactured with Oceanic Posidonia waste and bonded with cement are investigated. The particleboards are made with 3/1.5/0.5 parts of cement per part of Posidonia waste. The physical properties of bulk density, swelling, surface absorption, and dimensional changes due to relative humidity as well as the mechanical properties of modulus of elasticity, bending strength, surface soundness, perpendicular tensile strength and impact resistance are studied. In terms of the above properties, the best results were obtained for particleboards with high cement content and when the waste “leaves” are treated (crushed) before board fabrication, due to internal changes to the board structure under these conditions. Based on the results of fire tests, the particleboard is non-flammable without any fire-resistant treatment.
Resumo:
In this study, the behavior of bituminous mixes made with sewage sludge ash (SSA) as mineral filler was investigated. The behavior of these mixes was evaluated with the Cantabro, indirect tensile strength, water sensitivity, permanent deformation, and resilient modulus tests. The results show that SSA waste may be used in bituminous mixes at approximately 2–3% weight percent, maintaining adequate levels of cohesion and adhesion in the mixtures, which is comparable to mixtures made with active fillers such as hydrated lime and cement. Moreover, its use does not increase permanent deformations. However, the resilient modulus test gave slightly lower results for mixes made with SSA than for mixtures made with other fillers. It may be concluded that SSA waste may be used as a filler for bituminous mixes with better results than for mixes made with limestone fillers and with similar results for mixes made with other fillers such as hydrated lime and cement.
Resumo:
En el conjunto de materiales de construcción habituales en la edificación y las obras de ingeniería, el hormigón destaca entre otras razones por su excelente comportamiento frente a las altas temperaturas y la exposición al fuego. El presente estudio se centra en la adherencia residual entre el hormigón y las barras de acero corrugado soldable tras exponer probetas a altas temperaturas y enfriarlas hasta temperatura ambiente por convección natural. El estudio incluye hormigones de resistencia convencional, hormigones de alta resistencia y hormigones reforzados con fibras de polipropileno y fibras de acero. La adherencia hormigón-acero se ha medido mediante el conocido ensayo de pull-out. La campaña experimental también ha incluido la resistencia a compresión y la resistencia a tracción indirecta. Parte de las probetas se han ensayado a 28 días de edad a temperatura ambiente. A 60 días de edad se han repetido los ensayos a temperatura ambiente y se han realizado esos mismos ensayos en probetas calentadas en un horno industrial hasta tres rangos de temperatura: 450°C, 650°C y 825°C. Previo al proceso de calentamiento han sido sometidas durante 3 horas a un escalón de secado a 120°C. Mediante la metodología propuesta ha sido posible caracterizar la evolución de la pérdida de adherencia residual entre el acero y el hormigón conforme se exponen los especímenes a temperaturas más elevadas. La adición de fibras no tiene una influencia clara en la adherencia a temperatura ambiente. Sin embargo, sí se ha conseguido determinar una mejora sustancial de la adherencia residual en los hormigones, reforzados con fibras de acero sometidos a altas temperaturas.