Novel Ti/Ta2O5-SnO2 electrodes for water electrolysis and electrocatalytic oxidation of organics

Mixed metal oxide (MMO) electrodes have been applied to different technologies including chlorine production, organic compounds oxidation, water electrolysis, electroplating, etc. due to their catalytic, optical and electronic properties. Most of the existing MMO electrodes contain either toxic metals or precious metals of the platinum group. The aim of this study was to develop environmentally friendly and cost-effective MMO electrodes for water and organic compounds oxidation. Ti/Ta2O5-SnO2 electrodes of different nominal composition were prepared, and electrochemically and physically characterized. For water oxidation, Ti/SnO2 electrode with 5 at.% of Ta produced the highest electroactivity. Ti/SnO2 electrode with 7.5 at.% of Ta showed the best performance for the oxidation of methylene blue (MB). The electrocatalytic activity of the Ti/Ta2O5-SnO2 electrodes increased with the number of active layers. The maximum current of water oxidation reached 3.5 mA at 2.5 V when the electrode was covered with ten layers of Ta2O5. In case of the oxidation of 0.1 mM MB, eight and ten active layers of Ta2O5 significantly increased the electrode activity. The prepared electrodes have been found applicable for both water electrolysis and organic compounds oxidation.

Oxygen evolution at ultrathin nanostructured Ni(OH)2 layers deposited on conducting glass

Ultrathin and transparent nanostructured Ni(OH)2 films were deposited on conducting glass (F:SnO2) by a urea-based chemical bath deposition method. By controlling the deposition time, the amount of deposited Ni(OH)2 was varied over 7 orders of magnitude. The turnover number for O2 generation, defined as the number of O2 molecules generated per catalytic site (Ni atom) and per second, increases drastically as the electrocatalyst amount decreases. The electrocatalytic activity of the studied samples (measured as the current density at a certain potential) increases with the amount of deposited Ni(OH)2 until a saturation value is already obtained for a thin film of around 1 nm in thickness, composed of Ni(OH)2 nanoplatelets lying flat on the conductive support. The deposition of additional amounts of catalyst generates a porous honeycomb structure that does not improve (only maintains) the electrocatalytic activity. The optimized ultrathin electrodes show a remarkable stability, which indicates that the preparation of highly transparent electrodes, efficient for oxygen evolution, with a minimum amount of nickel is possible.

Interplay Between Structure, Stoichiometry, and Electron Transfer Dynamics in SILAR-based Quantum Dot-Sensitized Oxides

We quantify the rate and efficiency of picosecond electron transfer (ET) from PbS nanocrystals, grown by successive ionic layer adsorption and reaction (SILAR), into a mesoporous SnO2 support. Successive SILAR deposition steps allow for stoichiometry- and size-variation of the QDs, characterized using transmission electron microscopy. Whereas for sulfur-rich (p-type) QD surfaces substantial electron trapping at the QD surface occurs, for lead-rich (n-type) QD surfaces, the QD trapping channel is suppressed and the ET efficiency is boosted. The ET efficiency increase achieved by lead-rich QD surfaces is found to be QD-size dependent, increasing linearly with QD surface area. On the other hand, ET rates are found to be independent of both QD size and surface stoichiometry, suggesting that the donor–acceptor energetics (constituting the driving force for ET) are fixed due to Fermi level pinning at the QD/oxide interface. Implications of our results for QD-sensitized solar cell design are discussed.

Pt- and Ru-Doped SnO2–Sb Anodes with High Stability in Alkaline Medium

Different Pt- and Ru-doped Ti/SnO2–Sb electrodes were synthesized by thermal decomposition. The effect of the gradual substitution of Sb by Ru in the nominal composition on the physicochemical and electrochemical properties were evaluated. The electrochemical stability of the electrodes was estimated from accelerated tests at 0.5 A cm–2 in 1 M NaOH. Both as-synthesized and deactivated electrodes were thoroughly characterized by scanning electron microscopy (SEM), energy-dispersive X-ray microanalysis (EDX), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS) and X-ray diffraction analysis (XRD). The incorporation of a small amount (about 3 at. %) of both Pt and Ru into the SnO2–Sb electrodes produced a 400-times increase in their service life in alkaline medium, with no remarkable change in the electrocatalysis of the oxygen evolution reaction (OER). It is concluded that the deactivation of the electrodes is promoted by alkaline dissolution of metal species and coating detachment at high potentials. The introduction of Pt has a coating compacting effect, and Ru(IV), at low amounts until 9.75 at. %, replaces the Sn(IV) cations in the rutile-like SnO2 structure to form a solid solution that strongly increases the stability of the electrodes. The observed Ru segregation and decreased stability for larger Ru contents (x > 9.75 at. %), together with the selective dissolution of Ru after deactivation, suggest that the formation of a homogeneous (RuδSn1−δ)O2 single-phase is crucial for the stabilization of these electrodes.