Structural and photoelectrochemical properties of porous TiO2 nanofibers decorated with Fe2O3 by sol-flame

The hybrid structure of Fe2O3 nanoparticles/TiO2 nanofibers (NFs), combines the merits of large surface areas of TiO2 NFs and absorption in ultraviolet light–visible light range. This structure can be used for many applications such as photoelectrochemical water splitting and photo-catalysis. Here, a sol-flame method is used for depositing Fe2O3 on TiO2 NFs that were prepared by hydrothermal on Ti sheets. The obtained materials were characterized by XRD, SEM, UV/Vis diffuse reflectance, Raman, and XPS. The results revealed the formation of rutile and anatase crystalline phases together with Fe2O3. This process moves the absorption threshold of TiO2 NFs support into visible spectrum range and enhances the photocurrent in comparison to bare TiO2 NFs, although no hole scavenger was used. The impedance measurement at low and high frequencies revealed an increase in series resistance and a decrease in resistance of charge transfer with sol-flame treatment time. A mechanism for explaining the charge transfer in these TiO2 NFs decorated with Fe2O3 nanoparticles was proposed.

Improving the Photoelectrochemical Response of TiO2 Nanotubes upon Decoration with Quantum-Sized Anatase Nanowires

TiO2 nanotubes (NTs) have been widely used for a number of applications including solar cells, photo(electro)chromic devices, and photocatalysis. Their quasi-one-dimensional morphology has the advantage of a fast electron transport although they have a relatively reduced interfacial area compared with nanoparticulate films. In this study, vertically oriented, smooth TiO2 NT arrays fabricated by anodization are decorated with ultrathin anatase nanowires (NWs). This facile modification, performed by chemical bath deposition, allows to create an advantageous self-organized structure that exhibits remarkable properties. On one hand, the huge increase in the electroactive interfacial area induces an improvement by 1 order of magnitude in the charge accumulation capacity. On the other hand, the modified NT arrays display larger photocurrents for water and oxalic acid oxidation than bare NTs. Their particular morphology enables a fast transfer of photogenerated holes but also efficient mass and electron transport. The importance of a proper band energy alignment for electron transfer from the NWs to the NTs is evidenced by comparing the behavior of these electrodes with that of NTs modified with rutile NWs. The NT-NW self-organized architecture allows for a precise design and control of the interfacial surface area, providing a material with particularly attractive properties for the applications mentioned above.

Understanding the CO Preoxidation and the Intrinsic Catalytic Activity of Step Sites in Stepped Pt Surfaces in Acidic Medium

In order to deepen the knowledge about the origin of the CO preoxidation process and the intrinsic catalytic activity of Pt superficial steps toward CO oxidation, a series of CO stripping experiments were performed on stepped Pt electrodes in acidic medium. For the occurrence of CO preoxidation, it was found that it arises (reproducibly) whenever four interconnected conditions are simultaneously fulfilled: (1) CO adsorption at potentials lower than about 0.2 V; (2) on surfaces saturated with COads; (3) in the presence of traces of CO in solution; (4) in the presence of surface steps. If any of these four conditions is not satisfied, the CO preoxidation pathway does not appear, even though the steps on the electrode surface are completely covered by CO. By controlling the removal of the CO adlayer (voltammetrically), we show that once the CO adlayer has been partially oxidized, the (111) terrace sites of stepped surfaces are released earlier than the (110) step sites. Moreover, if (110) steps are selectively decorated with CO, its oxidation occurs only at potentials ∼150 mV higher than the CO preoxidation peak. Our results systematically demonstrate that step sites are less active to oxidize CO than those ones responsible for the CO preoxidation process. Once the sites responsible for the CO preoxidation are made free, there is no apparent motion of the remaining adsorbed CO layer, suggesting that the activation of the surface controls the whole process, rather than the diffusion of COads toward hypothetically “most active sites”. Voltammetric and chronoamperometric experiments performed on partially covered CO adlayers suggest that adsorbed CO behave as a motionless species during its oxidation, in which the CO adlayer is removed piece by piece. By means of in situ FTIR experiments, the stretching frequency of CO selectively adsorbed on (110) step sites was examined. Band frequency results confirm that those molecules adsorbed on steps are fully coupled with the adsorbed CO on (111) terraces when the surface reaches full coverage.