Assessment of CO2 adsorption capacity on activated carbons by a combination of batch and dynamic tests

In this work, batch and dynamic adsorption tests are coupled for an accurate evaluation of CO2 adsorption performance for three different activated carbons obtained from olives stones by chemical activation followed by physical activation with CO2 at varying times, i.e. 20, 40 and 60 h. Kinetic and thermodynamic CO2 adsorption tests from simulated flue-gas at different temperature and CO2 pressure are carried out both in batch (a manometric equipment operating with pure CO2) and dynamic (a lab-scale fixed-bed column operating with CO2/N2 mixture) conditions. The textural characterization of the activated carbon samples shows a direct dependence of both micropore and ultramicropore volume on the activation time, hence AC60 has the higher contribution. The adsorption tests conducted at 273 and 293 K showed that, when CO2 pressure is lower than 0.3 bar, the lower the activation time the higher CO2 adsorption capacity and a ranking ωeq(AC20)>ωeq(AC40)>ωeq(AC60) can be exactly defined when T= 293 K. This result can be likely ascribed to a narrower pore size distribution of the AC20 sample, whose smaller pores are more effective for CO2 capture at higher temperature and lower CO2 pressure, the latter representing operating conditions of major interest for decarbonation of a flue-gas effluent. Moreover, the experimental results obtained from dynamic tests confirm the results derived from the batch tests in terms of CO2 adsorption capacity. It is important to highlight that the adsorption of N2 on the synthesized AC samples can be considered negligible. Finally, the importance of a proper analysis of characterization data and adsorption experimental results is highlighted for a correct assessment of CO2 removal performances of activated carbons at different CO2 pressure and operating temperature.

Relationship between static and dynamic elastic modulus of calcarenite heated at different temperatures: the San Julián's stone

The San Julián’s stone is the main material used to build the most important historical buildings in Alicante city (Spain). This paper describes the analysis developed to obtain the relationship between the static and the dynamic modulus of this sedimentary rock heated at different temperatures. The rock specimens have been subjected to heating processes at different temperatures to produce different levels of weathering on 24 specimens. The static and dynamic modulus has been measured for every specimen by means of the ISRM standard and ultrasonic tests, respectively. Finally, two analytic formulas are proposed for the relationship between the static and the dynamic modulus for this stone. The results have been compared with some relationships proposed by different researchers for other types of rock. The expressions presented in this paper can be useful for the analysis, using non-destructive techniques, of the integrity level of historical constructions built with San Julián’s stone affected by fires.

Fire-resistance, physical, and mechanical characterization of particleboard containing Oceanic Posidonia waste

In this work, particleboards manufactured with Oceanic Posidonia waste and bonded with cement are investigated. The particleboards are made with 3/1.5/0.5 parts of cement per part of Posidonia waste. The physical properties of bulk density, swelling, surface absorption, and dimensional changes due to relative humidity as well as the mechanical properties of modulus of elasticity, bending strength, surface soundness, perpendicular tensile strength and impact resistance are studied. In terms of the above properties, the best results were obtained for particleboards with high cement content and when the waste “leaves” are treated (crushed) before board fabrication, due to internal changes to the board structure under these conditions. Based on the results of fire tests, the particleboard is non-flammable without any fire-resistant treatment.

Temperature influence on the physical and mechanical properties of a porous rock: San Julian's calcarenite

This work discusses the results from tests which were performed in order to study the effect of high temperatures in the physical and mechanical properties of a calcarenite (San Julian's stone). Samples, previously heated at different temperatures (from 105 °C to 600 °C), were tested. Non-destructive tests (porosity and ultrasonic wave propagation) and destructive tests (uniaxial compressive strength and slake durability test) were performed over available samples. Furthermore, the tests were carried out under different conditions (i.e. air-cooled and water-cooled) in order to study the effect of the fire off method. The results show that uniaxial compressive strength and elastic parameters (i.e. elastic modulus and Poisson's ratio), decrease as the temperature increases for the tested range of temperatures. A reduction of the uniaxial compressive strength up to 35% and 50% is observed in air-cooled and water-cooled samples respectively when the samples are heated to 600 °C. Regarding the Young's modulus, a fall over 75% and 78% in air-cooled and water-cooled samples respectively is observed. Poisson's ratio also declines up to 44% and 68% with the temperature in air-cooled and water-cooled samples respectively. Slake durability index also exhibits a reduction with temperature. Other physical properties, closely related with the mechanical properties of the stone, are porosity, attenuation and propagation velocity of ultrasonic waves in the material. All exhibit considerable changes with temperature.

Performance Factors in Women's Team Handball: Physical and Physiological Aspects—A Review

Team handball is an Olympic sport played professionally in many European countries. Nevertheless, a scientific knowledge regarding women's elite team handball demands is limited. Thus, the purpose of this article was to review a series of studies (n = 33) on physical characteristics, physiological attributes, physical attributes, throwing velocity, and on-court performances of women's team handball players. Such empirical and practical information is essential to design and implement successful short-term and long-term training programs for women's team handball players. Our review revealed that (a) players that have a higher skill level are taller and have a higher fat-free mass; (b) players who are more aerobically resistant are at an advantage in international level women team handball; (c) strength and power exercises should be emphasized in conditioning programs, because they are associated with both sprint performance and throwing velocity; (d) speed drills should also be implemented in conditioning programs but after a decrease in physical training volume; (e) a time-motion analysis is an effective method of quantifying the demands of team handball and provides a conceptual framework for the specific physical preparation of players. According to our results, there are only few studies on on-court performance and time-motion analysis for women's team handball players, especially concerning acceleration profiles. More studies are needed to examine the effectiveness of different training programs of women's team handball players' physiological and physical attributes.

Analysis of physical and physiological requirements in soccer trainings in young soccer players (under -10 years)

The aim of this study is to analyse the physical and physiological factors in soccer training at different categories of training. The participants were 30 soccer players of 8-aside soccer in the under 10’s age group (9.93±0.25 years) who participated in the under 10 Provincial Tournament in Alicante. During training, the variables of covered distance, heart rate, speed (average and maximum values) as well as the methodology used and position were registered. After the statistical analysis and its related discussion, it was concluded that the players do not show differences in the covered total distance in relation to the category. Notwithstanding, there are differences with regards to speed and heart rate, which are caused by the greater physical development of the players in comparison to the under10’s age group category. Regarding the methodology employed, it is worth stressing that the coaches used, to a greater extend, the global method, followed by the mixed method.

Physical and chemical evaluation of furniture waste briquettes

Furniture waste is mainly composed of wood and upholstery foam (mostly polyurethane foam). Both of these have a high calorific value, therefore, energy recovery would be an appropriate process to manage these wastes. Nevertheless, the drawback is that the energy content of these wastes is limited due to their low density mainly that of upholstery foam. Densification of separate foam presents difficulties due to its elastic character. The significance of this work lies in obtaining densified material by co-densification of furniture wood waste and polyurethane foam waste. Densification of furniture wood and the co-densification of furniture wood waste with polyurethane foam have been studied. On the one hand, the parameters that have an effect on the quality of the furniture waste briquettes have been analysed, i.e., moisture content, compaction pressure, presence of lignin, etc. The maximum weight percentage of polyurethane foam that can be added with furniture wood waste to obtain durable briquettes and the optimal moisture were determined. On the other hand, some parameters were analysed in order to evaluate the possible effect on the combustion. The chemical composition of waste wood was compared with untreated wood biomass; the higher nitrogen content and the concentration of some metals were the most important differences, with a significant difference of Ti content.