Mechanical, thermal and colorimetric properties of LLDPE coloured with a blue nanopigment and conventional blue pigments

Purpose – This research deals with a new kind of nanopigment, obtained from the combination of organic dyes and layered nanoclays, that the authors call nanoclay-colorant pigment (NCP). Whilst they have already been employed in inks and coatings, to date these nanopigments have not been used as pigments for polymers. The existing lack of knowledge surrounding them must be redressed in order to bridge the gap between current academic studies and commercial exploitation. Therefore, the main purpose of this paper is to examine the hitherto unknown aspects of the NCP, which relate specifically to their applicability as a new type of colorant for polymers. Design/methodology/approach – A blue NCP has been prepared at the laboratory according to the patented method of synthesis (patent WO0104216), using methylene blue and montmorillonite nanoclay. It has then been applied to a thermoplastic polymer (linear low-density polyethylene – LLDPE) to obtain a coloured sample. Furthermore, samples with the same polymer but using conventional blue colorants have been prepared under the same processing conditions. The mechanical, thermal and colorimetric properties of these materials have been compared. Findings – The thermal stability of the sample coloured with NCP is reduced to some extent, while the mechanical strength is slightly increased. Moreover, this sample has better colour performance than the conventionally pigmented samples. Originality/value – In this paper, a blue NCP has been synthesised and successfully employed with polyethylene and the obtained sample shows better colour performance than polyethylene with conventional pigments.

The influence of surfactant loading level in a montmorillonite on the thermal, mechanical and rheological properties of EVA nanocomposites

In this work, montmorillonite (Mt) has been organically modified with ethyl hexadecyl dimethyl ammonium (EHDDMA) in 20, 50, 80 and 100% of the nominal exchange capacity (CEC) of the Mt. A full characterization of the organo-montmorillonite (OMt) obtained has been made, including thermal analysis, X-Ray Diffraction, elemental analysis CHN and nitrogen adsorption. According to the results, 12% in mass of the surfactant added is strongly retained by the Mt. When the mass percentage of EHDDMA exchanged in the OMt is increased up to this level, the interactions OMt–EHDDMA are steeply reduced depending on the EHDDMA content. Clay polymer nanocomposites (CPN) were prepared by melt mixing of EVA and different loads of OMt. The CPN were compress molded to obtain 1 mm thick sheets, which have been characterized according to their mechanical, thermal and rheological behaviors. The major changes in the structure of the OMt are obtained for low contents of EHDDMA. Nevertheless, the CPN containing OMt exchanged at 20 and 50% of the CEC show relatively low effect of the EHDDMA while the mechanical response and rheological behavior of CPN with OMt modified at 80 and 100% of the CEC are much more pronounced.