CeO2-promoted Ni/activated carbon catalysts for the water–gas shift (WGS) reaction

The low temperature water–gas shift (WGS) reaction has been studied over carbon-supported nickel catalysts promoted by ceria. To this end, cerium oxide has been dispersed (at different loadings: 10, 20, 30 and 40 wt.%) on the activated carbon surface with the aim of obtaining small ceria particles and a highly available surface area. Furthermore, carbon- and ceria-supported nickel catalysts have also been studied as references. A combination of N2 adsorption analysis, powder X-ray diffraction, temperature-programmed reduction with H2, X-ray photoelectron spectroscopy and TEM analysis were used to characterize the Ni–CeO2 interactions and the CeO2 dispersion over the activated carbon support. Catalysts were tested in the low temperature WGS reaction with two different feed gas mixtures: the idealized one (with only CO and H2O) and a slightly harder one (with CO, CO2, H2, and H2O). The obtained results show that there is a clear effect of the ceria loading on the catalytic activity. In both cases, catalysts with 20 and 10 wt.% CeO2 were the most active materials at low temperature. On the other hand, Ni/C shows a lower activity, this assessing the determinant role of ceria in this reaction. Methane, a product of side reactions, was observed in very low amounts, when CO2 and H2 were included in the WGS feed. Nevertheless, our data indicate that the methanation process is mainly due to CO2, and no CO consumption via methanation takes place at the relevant WGS temperatures. Finally, a stability test was carried out, obtaining CO conversions greater than 40% after 150 h of reaction.

The influence of promoters (Zr, La, Tb, Pr) on the catalytic performance of CuO-CeO2 systems for the preferential oxidation of CO in the presence of CO2 and H2O

CuO supported on CeO2 and Ce0.9X0.1O2, where X is Zr, La, Tb or Pr, were synthesized using nitrate precursors, giving rise ceria based materials with a small particle size which interact with CuO species generating a high amount of interfacial sites. The incorporation of cations to the ceria framework modifies the CeO2 lattice parameter, improving the redox behavior of the catalytic system. The catalysts were characterized by X-ray fluorescence spectrometry (XRFS), X-ray diffraction (XRD), high-resolution transmission electron microscopy (HRTEM), Raman spectroscopy, thermoprogrammed reduction with H2 (H2-TPR) and X-ray photoelectron spectroscopy (XPS). The catalysts were tested in the preferential oxidation of CO under a H2-rich stream (CO-PROX), reaching conversion values higher than 95% between 115 and 140 °C and being the catalyst with 6 wt.% of Cu supported on Ce0.9Zr0.1O2 (sample 6CUZRCE) the most active catalyst. The influence of the presence of CO2 and H2O was also studied simulating a PROX unit, taking place a decrease of the catalytic activity due to the inhibitor effect both CO2 and H2O.