The role of mesoporosity and Si/Al ratio in the catalytic etherification of glycerol with benzyl alcohol using ZSM-5 zeolites

A comparative study of the influence of three different acid solids as catalysts (conventional zeolites Z15c with Si/Al = 19.5 and Z40c with Si/Al = 48.2, and a hierarchical zeolite Z40c-H with Si/Al = 50.0) for the etherification of glycerol with benzyl alcohol was performed. The catalytic activity and selectivity of these zeolites was elucidated at different catalyst contents. Three different ethers (3-benzyloxy-1,2-propanediol, which is a mono-benzyl-glycerol ether (MBG) and 1,3-dibenzyloxy-2-propanol, which is a di-benzyl-glycerol ether (DBG) and dibenzyl ether (DBz) were identified as the main products. MBG was the major product of the reaction catalyzed by the microporous Z15c zeolite with low Si/Al molar ratio, whereas DBG was formed in higher yield with the use of microporous Z40c and hierarchical Z40c-H zeolites, both of them having a similar high Si/Al molar ratio (≈50). MBG is a value-added product and it is obtained with good yield and selectivity when using the conventional zeolite Z15c as a catalyst. Under the best conditions tested, i.e., 25 mg of catalyst for 8 h at 120 °C, a 62% of conversion was obtained without the need of solvent, with an excellent 84% selectivity toward the MBG and no formation of DBz.

Steam reforming of ethanol over bimetallic RhPt/La2O3: Long-term stability under favorable reaction conditions

Recently, the steam reforming of biofuels has been presented as a potential hydrogen source for fuel cells. Because this scenario represents an interesting opportunity for Colombia (South America), which produces large amounts of bioethanol, the steam reforming of ethanol was studied over a bimetallic RhPt/La2O3 catalyst under bulk mass transfer conditions. The effect of temperature and the initial concentrations of ethanol and water were evaluated at space velocities above 55,000 h−1 to determine the conditions that maximize the H2/CO ratio and reduce CH4 production while maintaining 100% conversion of ethanol. These requirements were accomplished when 21 mol% H2O and 3 mol% C2H5OH (steam/ethanol molar ratio = 7) were reacted at 600 °C. The catalyst stability was assessed under these reaction conditions during 120 h on stream, obtaining ethanol conversions above 99% during the entire test. The effect of both H2 and air flows as catalyst regeneration treatments were evaluated after 44 and 67 h on stream, respectively. The results showed that H2 treatment accelerated catalyst deactivation, and air regeneration increased both the catalyst stability and the H2 selectivity while decreasing CH4 generation. Fresh and spent catalyst samples were characterized by TEM/EDX, XPS, TPR, and TGA. Although the Rh and Pt in the fresh catalyst were completely reduced, the spent samples showed a partial oxidation of Rh and small amounts of carbonaceous residue. A possible Rh–Pt–Rh2O3 structure was proposed as the active site on the catalyst, which was regenerated by air treatment.

Hydrogen Production by Steam Reforming of Ethanol on Rh-Pt Catalysts: Influence of CeO2, ZrO2, and La2O3 as Supports

CeO2-, ZrO2-, and La2O3-supported Rh-Pt catalysts were tested to assess their ability to catalyze the steam reforming of ethanol (SRE) for H2 production. SRE activity tests were performed using EtOH:H2O:N2 (molar ratio 1:3:51) at a gaseous space velocity of 70,600 h−1 between 400 and 700 °C at atmospheric pressure. The SRE stability of the catalysts was tested at 700 °C for 27 h time on stream under the same conditions. RhPt/CeO2, which showed the best performance in the stability test, also produced the highest H2 yield above 600 °C, followed by RhPt/La2O3 and RhPt/ZrO2. The fresh and aged catalysts were characterized by TEM, XPS, and TGA. The higher H2 selectivity of RhPt/CeO2 was ascribed to the formation of small (~5 nm) and stable particles probably consistent of Rh-Pt alloys with a Pt surface enrichment. Both metals were oxidized and acted as an almost constant active phase during the stability test owing to strong metal-support interactions, as well as the superior oxygen mobility of the support. The TGA results confirmed the absence of carbonaceous residues in all the aged catalysts.