X-Ray Imaging of SAPO-34 Molecular Sieves at the Nanoscale: Influence of Steaming on the Methanol-to-Hydrocarbons Reaction

The effect of a severe steaming treatment on the physicochemical properties and catalytic performance of H-SAPO-34 molecular sieves during the methanol-to-hydrocarbons (MTH) reaction has been investigated with a combination of scanning transmission X-ray microscopy (STXM), catalytic testing, and bulk characterization techniques, including ammonia temperature programmed desorption and 27Al and 29Si magic angle spinning nuclear magnetic resonance. For this purpose, two samples, namely a calcined and a steamed H-SAPO-34 catalyst powder, have been compared. It has been found that calcined H-SAPO-34 displays a high selectivity towards light olefins, yet shows a poor stability as compared to a zeolite H-ZSM-5 catalyst. Moreover, in situ STXM at the carbon K-edge during the MTH reaction allows construction of nanoscale chemical maps of the hydrocarbon species formed within the H-SAPO-34 aggregates as a function of reaction time and steam post-treatment. It was found that there is an initial preferential formation of coke precursor species within the core of the H-SAPO-34 aggregates. For longer times on stream the formation of the coke precursor species is extended to the outer regions, progressively filling the entire H-SAPO-34 catalyst particle. In contrast, the hydrothermally treated H-SAPO-34 showed similar reaction selectivity, but decreased activity and catalyst stability with respect to its calcined counterpart. These variations in MTH performance are related to a faster and more homogeneous formation of coke precursor species filling up the entire steamed H-SAPO-34 catalyst particle. Finally, the chemical imaging capabilities of the STXM method at the Al and Si K-edge are illustrated by visualizing the silicon islands at the nanoscale before and after steaming H-SAPO-34.

Effect of the stabilisation time of pitch fibres on the molecular sieve properties of carbon fibres

The stabilisation of pitch fibres (PFs) is the most important step for their subsequent use in the preparation of carbon fibres (CFs) and their resulting characteristics. The present work studies the influence that the stabilisation time has on the porosity of the CFs, and on the subsequent properties as carbon molecular sieve (CMS). The increase of the stabilisation time carried out at 573 K, from 2 to 8 h favours their CMS properties producing a decrease in the microposity accessible to N2, which gets completely blocked after 6 and 8 h, while the narrow microporosity (V-DR CO2) remains accessible. Adsorption kinetic studies with CH4 and CO2 were performed to assess the possibility of using these CFs as CMS by comparing them with Takeda 3A CMS. The results suggest that there is an optimal stabilisation time which allows the preparation of CFs from an abundant raw precursor with properties similar to Takeda 3A CMS.

Colloidal gold immobilized on mesoporous silica as a highly active and selective catalyst for styrene epoxidation with H2O2

Colloidal gold nanoparticles were synthesized by different procedures affording suspensions with two different mean sizes (2 and 5 nm). Au catalysts were prepared by sol immobilization onto several silica frameworks with different 2D and 3D mesoporosities. The catalysts were tested in styrene oxidation reactions showing excellent efficiency and selectivity. The effect of nanoparticle size and mesoporous framework on the physical and catalytic properties of the final materials was studied. The most selective catalyst was prepared from the 5 nm Au nanoparticles and the more interconnected silica framework (3D mesoporosity).

Novel silica membrane material for molecular sieve applications

Development of new silica membranes properties, e.g., molecular sieving properties, has been increasingly gaining importance in the last few years. A novel unsupported silica membrane, referred to as hydrophobic metal-doped silica, was developed by cobalt-doping within the organic templated silica matrix. The novel material was prepared by the acid-catalyzed hydrolysis and condensation process of tetraethylorthosilicate (TEOS) and methyltriethoxysilane (MTES), which is the precursor for methyl ligand covalently bounded to the silica matrix. The synthesis and surface properties of the novel unsupported silica membrane as well as the unsupported blank silica and modified silica membranes were revealed by surface and microstructural techniques, such as water contact angle measurement, FTIR, X-ray, Solid-state 29Si MAS NMR, TGA and N2 and CO2 adsorption measurements. The results showed that the thermal stability of the organic templated silica matrix was enhanced by cobalt-doping process. A hydrophobic microporous silica membrane material with high thermal stability up to ∼560 °C in oxidizing atmosphere and a narrow pore size distribution centered at 1.1 nm was obtained. Therefore, a novel precursor material for molecular sieve silica membranes applications has been achieved and developed.

Mesoporous materials for clean energy technologies

Alternative energy technologies are greatly hindered by significant limitations in materials science. From low activity to poor stability, and from mineral scarcity to high cost, the current materials are not able to cope with the significant challenges of clean energy technologies. However, recent advances in the preparation of nanomaterials, porous solids, and nanostructured solids are providing hope in the race for a better, cleaner energy production. The present contribution critically reviews the development and role of mesoporosity in a wide range of technologies, as this provides for critical improvements in accessibility, the dispersion of the active phase and a higher surface area. Relevant examples of the development of mesoporosity by a wide range of techniques are provided, including the preparation of hierarchical structures with pore systems in different scale ranges. Mesoporosity plays a significant role in catalysis, especially in the most challenging processes where bulky molecules, like those obtained from biomass or highly unreactive species, such as CO2 should be transformed into most valuable products. Furthermore, mesoporous materials also play a significant role as electrodes in fuel and solar cells and in thermoelectric devices, technologies which are benefiting from improved accessibility and a better dispersion of materials with controlled porosity.

Mesoporous Metal Complex–Silica Aerogels for Environmentally Friendly Amination of Allylic Alcohols

Two series of mesoporous hybrid iron(III) complex–silica aerogels were prepared in one-pot synthesis by using the sol–gel coordination chemistry approach. The use of the ligands 3-(2-aminoethylamino)propyltrimethoxysilane and 2-(diphenylphosphino)ethyltriethoxysilane, both with terminal triethoxysilyl groups, were used to incorporate metal complexes in situ into the framework of silica, through their co-condensation with a silicon alkoxide during the aerogel formation. This methodology yielded optically translucent hybrid mesoporous gels with homogeneous metal incorporation and excellent textural properties. The catalytic performance of these materials was tested in the direct amination of allylic alcohols in water as a target reaction, with activities comparable or even higher than those corresponding to the homogeneous iron(III) complex. Furthermore, these catalysts were stable and maintained their catalytic activity after six reaction cycles.

Magnetically separable mesoporous Fe3O4/silica catalysts with very low Fe3O4 content

Two magnetically separable Fe3O4/SiO2 (aerogel and MSU-X) composites with very low Fe3O4 content (<1 wt%) have been successfully prepared at room temperature by co-condensation of MPTES-functionalized Fe3O4 nanoparticles (NPs) with a silicon alkoxide. This procedure yields a homogeneous incorporation of the Fe3O4 NPs on silica supports, leading to magnetic composites that can be easily recovered using an external magnetic field, despite their very low Fe3O4 NPs content (ca. 1 wt%). These novel hybrid Fe3O4/SiO2 materials have been tested for the oxidation reaction of 3,3′,5,5′-tetramethylbenzidine (TMB) with hydrogen peroxide showing an enhancement of the stability of the NPs in the Fe3O4/silica aerogel as compared to the Fe3O4 NPs alone, even after five catalytic cycles, no leaching or agglomeration of the Fe3O4/SiO2 systems.