Synthesis of Ordered Mesoporous Carbon Materials by Dry Etching

A novel synthesis method for ordered mesoporous carbons is presented. The inverse replication of a silica template was achieved using the carbonization of sucrose within mesoporous KIT-6. Instead of liquid acid etching, as in classical nanocasting, a novel dry chlorine etching procedure for template removal is presented for the first time. The resultant ordered mesostructured carbon material outperforms carbons obtained by conventional hard templating with respect to high specific micro- and mesopore volumes (0.6 and 1.6 cm3 g−1, respectively), due to the presence of a hierarchical pore system. A high specific surface area of 1671 m2 g−1 was achieved, rendering this synthesis route a highly convenient method to produce ordered mesoporous carbons.

Synthesis of high surface area TiO2 nanoparticles by mild acid treatment with HCl or HI for photocatalytic propene oxidation

Nanostructured TiO2 photocatalysts with small crystalline sizes have been synthesized by sol-gel using the amphiphilic triblock copolymer Pluronic P123 as template. A new synthesis route, based on the treatment of TiO2 xerogels with acid-ethanol mixtures in two different steps, synthesis and extraction-crystallization, has been investigated, analyzing two acids, hydrochloric and hydriodic acid. As reference, samples have also been prepared by extraction-crystallization in ethanol, being these TiO2 materials amorphous and presenting higher porosities. The prepared materials present different degrees of crystallinity depending on the experimental conditions used. In general, these materials exhibit high surface areas, with an important contribution of microporosity and mesoporosity, and with very small size anatase crystals, ranging from 5 to 7 nm. The activity of the obtained photocatalysts has been assessed in the oxidation of propene in gas phase at low concentration (100 ppmv) under a UVA lamp with 365 nm wavelength. In the conditions studied, these photocatalysts show different activities in the oxidation of propene which do not depend on their surface areas, but on their crystallinity and band gap energies, being sample prepared with HCl both during synthesis and in extraction-crystallizations steps, the most active one, with superior performance than Evonik P25.

Evolution of surface properties of ornamental granitoids exposed to high temperatures

Granite submitted to high temperatures may lead to the loss of aesthetic values even before structural damage is caused. Thirteen granitoids were exposed to target temperatures, 200 °C, 400 °C, 600 °C, 800 °C and 1000 °C. Damage characterisation, including roughness, colour and oxidation of chromogen elements by means of X-ray photoelectron spectroscopy (XPS) was assessed. Altered granitoids are more resistant to structural failure but redden rapidly. Black mica-rich granitoids turn into yellow with a maximum at 800 °C. Alkali feldspar-rich granitoids redden progressively due to iron oxidation. Roughness varies progressively in mica-rich granitoids, while in mica-poor granitoids, an increase in roughness precedes catastrophic failure.