Beyond the H2/CO2 upper bound: one-step crystallization and separation of nano-sized ZIF-11 by centrifugation and its application in mixed matrix membranes

The synthesis of nano-sized ZIF-11 with an average size of 36 ± 6 nm is reported. This material has been named nano-zeolitic imidazolate framework-11 (nZIF-11). It has the same chemical composition and thermal stability and analogous H2 and CO2 adsorption properties to the conventional microcrystalline ZIF-11 (i.e. 1.9 ± 0.9 μm). nZIF-11 has been obtained following the centrifugation route, typically used for solid separation, as a fast new technique (pioneering for MOFs) for obtaining nanomaterials where the temperature, time and rotation speed can easily be controlled. Compared to the traditional synthesis consisting of stirring + separation, the reaction time was lowered from several hours to a few minutes when using this centrifugation synthesis technique. Employing the same reaction time (2, 5 or 10 min), micro-sized ZIF-11 was obtained using the traditional synthesis while nano-scale ZIF-11 was achieved only by using centrifugation synthesis. The small particle size obtained for nZIF-11 allowed the use of the wet MOF sample as a colloidal suspension stable in chloroform. This helped to prepare mixed matrix membranes (MMMs) by direct addition of the membrane polymer (polyimide Matrimid®) to the colloidal suspension, avoiding particle agglomeration resulting from drying. The MMMs were tested for H2/CO2 separation, improving the pure polymer membrane performance, with permeation values of 95.9 Barrer of H2 and a H2/CO2 separation selectivity of 4.4 at 35 °C. When measured at 200 °C, these values increased to 535 Barrer and 9.1.

Children's Separation Anxiety Scale (CSAS): Psychometric Properties

This study describes the psychometric properties of the Children's Separation Anxiety Scale (CSAS), which assesses separation anxiety symptoms in childhood. Participants in Study 1 were 1,908 schoolchildren aged between 8 and 11. Exploratory factor analysis identified four factors: worry about separation, distress from separation, opposition to separation, and calm at separation, which explained 46.91% of the variance. In Study 2, 6,016 children aged 8–11 participated. The factor model in Study 1 was validated by confirmatory factor analysis. The internal consistency (α = 0.82) and temporal stability (r = 0.83) of the instrument were good. The convergent and discriminant validity were evaluated by means of correlations with other measures of separation anxiety, childhood anxiety, depression and anger. Sensitivity of the scale was 85% and its specificity, 95%. The results support the reliability and validity of the CSAS.