Plastisol foaming process. Decomposition of the foaming agent, polymer behavior in the corresponding temperature range and resulting foam properties

The decomposition of azodicarbonamide, used as foaming agent in PVC—plasticizer (1/1) plastisols was studied by DSC. Nineteen different plasticizers, all belonging to the ester family, two being polymeric (polyadipates), were compared. The temperature of maximum decomposition rate (in anisothermal regime at 5 K min−1 scanning rate), ranges between 434 and 452 K. The heat of decomposition ranges between 8.7 and 12.5 J g−1. Some trends of variation of these parameters appear significant and are discussed in terms of solvent (matrix) and viscosity effects on the decomposition reactions. The shear modulus at 1 Hz frequency was determined at the temperature of maximum rate of foaming agent decomposition, and differs significantly from a sample to another. The foam density was determined at ambient temperature and the volume fraction of bubbles was used as criterion to judge the efficiency of the foaming process. The results reveal the existence of an optimal shear modulus of the order of 2 kPa that corresponds roughly to plasticizer molar masses of the order of 450 ± 50 g mol−1. Heavier plasticizers, especially polymeric ones are too difficult to deform. Lighter plasticizers such as diethyl phthalate (DEP) deform too easily and presumably facilitate bubble collapse.

Kinetic study of the decompositions involved in the thermal degradation of commercial azodicarbonamide

The transitions and reactions involved in the thermal treatment of several commercial azodicarbonamides (ADC) in an inert atmosphere have been studied by dynamic thermogravimetry analysis (TGA), mass spectrometry and Fourier transform infrared (FTIR) spectroscopy. A pseudo-mechanistic model, involving several competitive and non-competitive reactions, has been suggested and applied to the correlation of the weight loss data. The model applied is capable of accurately representing the different processes involved, and can be of great interest in the understanding and quantification of such phenomena, including the simulation of the instantaneous amount of gases evolved in a foaming process. In addition, a brief discussion on the methodology related to the mathematical modeling of TGA data is presented, taking into account the complex thermal behaviour of the ADC.

DSC study of transitions involved in thermal treatment of foamable mixtures of PE and EVA copolymer with azodicarbonamide

The transitions and reactions involved in the thermal processing of binary mixtures of polyethylene and poly(ethylene-co-vinyl acetate) copolymers with different concentrations of a foaming agent (azodicarbonamide) were studied using differential scanning calorimetry (DSC). The effect of ZnO as a kicker also was discussed. The temperature at the maximum rate and the heat evolved were measured for all the processes—melting, transitions, and reactions—all the mixtures prepared were measured and compared. Azodicarbonamide decomposed differently depending on the polymeric matrix. These data can be very useful for the plastic processing industry.

Modelo cinético para curvas de calorimetría diferencial de barrido (DSC): aplicación a diferentes polímeros y mezclas

En el presente trabajo se han estudiado mediante DSC, las reacciones involucradas en el tratamiento térmico de los principales componentes en las formulaciones de materiales espumados como son EVA, PE, azodicarbonamida y α- α’-bis(tertbutil-peroxi)-m/p-diisopropilbenceno. Los ensayos se han realizado a una velocidad de calefacción constante de 10 ºC/min en atmósfera inerte de N2. Por otro lado, también se proponen una serie de modelos cinéticos mecanísticos que contemplan la existencia de una o más fracciones reactivas y/o reacciones. Además se ha introducido la variación de las capacidades caloríficas con la temperatura, consiguiendo de esta forma una mejora considerable del ajuste de los datos experimentales. Los modelos presentados son capaces de representar los diferentes procesos observados (con varios picos) y pueden ser de gran interés para la compresión de este tipo de fenómenos, así como para el modelado de la transferencia de calor que se produce durante los procesos industriales de espumado. (Nota: se incluye al final un lisado actualizado con bibliografía específica sobre modelado cinético).