Nanoarchitectures Based on Layered Titanosilicates Supported on Glass Fibers: Application to Hydrogen Storage

This work reports on the synthesis of nanosheets of layered titanosilicate JDF-L1 supported on commercial E-type glass fibers with the aim of developing novel nanoarchitectures useful as robust and easy to handle hydrogen adsorbents. The preparation of those materials is carried out by hydrothermal reaction from the corresponding gel precursor in the presence of the glass support. Because of the basic character of the synthesis media, silica from the silicate-based glass fibers can be involved in the reaction, cementing its associated titanosilicate and giving rise to strong linkages on the support with the result of very stable heterostructures. The nanoarchitectures built up by this approach promote the growth and disposition of the titanosilicate nanosheets as a house-of-cards radially distributed around the fiber axis. Such an open arrangement represents suitable geometry for potential uses in adsorption and catalytic applications where the active surface has to be available. The content of the titanosilicate crystalline phase in the system represents about 12 wt %, and this percentage of the adsorbent fraction can achieve, at 298 K and 20 MPa, 0.14 wt % hydrogen adsorption with respect to the total mass of the system. Following postsynthesis treatments, small amounts of Pd (<0.1 wt %) have been incorporated into the resulting nanoarchitectures in order to improve their hydrogen adsorption capacity. In this way, Pd-layered titanosilicate supported on glass fibers has been tested as a hydrogen adsorbent at diverse pressures and temperatures, giving rise to values around 0.46 wt % at 298 K and 20 MPa. A mechanism of hydrogen spillover involving the titanosilicate framework and the Pd nanoparticules has been proposed to explain the high increase in the hydrogen uptake capacity after the incorporation of Pd into the nanoarchitecture.

Photocatalytic oxidation of propene in gas phase at low concentration by optimized TiO2 nanoparticles

In the present study, nanocrystalline titanium dioxide (TiO2) was prepared by sol–gel method at low temperature from titanium tetraisopropoxide (TTIP) and characterized by different techniques (gas adsorption, XRD, TEM and FTIR). Variables of the synthesis, such as the hydrolyzing agent (acetic acid or isopropanol) and calcination temperatures (300–800 °C), were analyzed to get uniform size TiO2 nanoparticles. The effect that these two variables have on the structure of the resultant TiO2 nanoparticles and on their photocatalytic activity is investigated. The photocatalytic activities of TiO2 nanoparticles were evaluated for propene oxidation at low concentration (100 ppmv) under two different kinds of UV light (UV-A ∼ 365 nm and UV-C ∼ 257.7 nm) and compared with Degussa TiO2 P-25, used as reference sample. The results show that both hydrolyzing agents allow to prepare TiO2 nanoparticles and that the hydrolyzing agent influences the crystalline structure and its change with the thermal treatments. Interestingly, the prepared TiO2 nanoparticles possess anatase phase with small crystalline size, high surface area and higher photocatalytic activity for propene oxidation than commercial TiO2 (Degussa P-25) under UV-light. Curiously, these prepared TiO2 nanoparticles are more active with the 365 nm source than with the 257.7 nm UV-light, which is a remarkable advantage from an application point of view. Additionally, the obtained results are particularly good when acetic acid is the hydrolyzing agent at both wavelengths used, possibly due to the high crystallinity, low anatase phase size and high surface oxygen groups’ content in the nanoparticles prepared with it, in comparison to those prepared using isopropanol.

Cost-Effective Force Field Tailored for Solid-Phase Simulations of OLED Materials

A united atom force field is empirically derived by minimizing the difference between experimental and simulated crystal cells and melting temperatures for eight compounds representative of organic electronic materials used in OLEDs and other devices: biphenyl, carbazole, fluorene, 9,9′-(1,3-phenylene)bis(9H-carbazole)-1,3-bis(N-carbazolyl)benzene (mCP), 4,4′-bis(N-carbazolyl)-1,1′-biphenyl (pCBP), phenazine, phenylcarbazole, and triphenylamine. The force field is verified against dispersion-corrected DFT calculations and shown to also successfully reproduce the crystal structure for two larger compounds employed as hosts in phosphorescent and thermally activated delayed fluorescence OLEDs: N,N′-di(1-naphthyl)-N,N′-diphenyl-(1,1′-biphenyl)-4,4′-diamine (NPD), and 1,3,5-tri(1-phenyl-1H-benzo[d]imidazol-2-yl)phenyl (TPBI). The good performances of the force field coupled to the large computational savings granted by the united atom approximation make it an ideal choice for the simulation of the morphology of emissive layers for OLED materials in crystalline or glassy phases.