The influence of surfactant loading level in a montmorillonite on the thermal, mechanical and rheological properties of EVA nanocomposites

In this work, montmorillonite (Mt) has been organically modified with ethyl hexadecyl dimethyl ammonium (EHDDMA) in 20, 50, 80 and 100% of the nominal exchange capacity (CEC) of the Mt. A full characterization of the organo-montmorillonite (OMt) obtained has been made, including thermal analysis, X-Ray Diffraction, elemental analysis CHN and nitrogen adsorption. According to the results, 12% in mass of the surfactant added is strongly retained by the Mt. When the mass percentage of EHDDMA exchanged in the OMt is increased up to this level, the interactions OMt–EHDDMA are steeply reduced depending on the EHDDMA content. Clay polymer nanocomposites (CPN) were prepared by melt mixing of EVA and different loads of OMt. The CPN were compress molded to obtain 1 mm thick sheets, which have been characterized according to their mechanical, thermal and rheological behaviors. The major changes in the structure of the OMt are obtained for low contents of EHDDMA. Nevertheless, the CPN containing OMt exchanged at 20 and 50% of the CEC show relatively low effect of the EHDDMA while the mechanical response and rheological behavior of CPN with OMt modified at 80 and 100% of the CEC are much more pronounced.

Methane dry reforming over Ni supported on pine sawdust activated carbon: Effects of support surface properties and metal loading

The influence of metal loading and support surface functional groups (SFG) on methane dry reforming (MDR) over Ni catalysts supported on pine-sawdust derived activated carbon were studied. Using pine sawdust as the catalyst support precursor, the smallest variety and lowest concentration of SFG led to best Ni dispersion and highest catalytic activity, which increased with Ni loading up to 3 Ni atoms nm-2. At higher Ni loading, the formation of large metal aggregates was observed, consistent with a lower "apparen" surface area and a decrease in catalytic activity. The H2/CO ratio rose with increasing reaction temperature, indicating that increasingly important side reactions were taking place in addition to MDR.

Electrocatalytic reduction of CO2 to formate using particulate Sn electrodes: Effect of metal loading and particle size

The development of electrochemical processes for the conversion of CO2 into value-added products allows innovative carbon capture & utilization (CCU) instead of carbon capture & storage (CCS). In addition, coupling this conversion with renewable energy sources would make it possible to chemically store electricity from these intermittent renewable sources. The electroreduction of CO2 to formate in aqueous solution has been performed using Sn particles deposited over a carbon support. The effect of the particle size and Sn metal loading has been evaluated using cyclic voltammetry and chronoamperometry. The selected electrode has been tested on an experimental filter-press type cell system for continuous and single pass CO2 electroreduction to obtain formate as main product at ambient pressure and temperature. Experimental results show that using electrodes with 0.75 mg Sn cm−2, 150 nm Sn particles, and working at a current density of 90 mA cm−2, it is possible to achieve rates of formate production over 3.2 mmol m−2 s−1 and faradaic efficiencies around 70% for 90 min of continuous operation. These experimental conditions allow formate concentrations of about 1.5 g L−1 to be obtained on a continuous mode and with a single pass of catholyte through the cell.